Preparation and structural characterization of epoxidized soybean oils-based pressure sensitive adhesive grafted with tea polyphenol palmitate

Vegetable oils-based pressure sensitive adhesives (PSAs) are green and sustainable but face unsatisfactory adhesion strengths and are prone to aging during storage and application due to the existence of residual double bonds and massive ester bonds. Nine common antioxidants (tea polyphenol palmitate (TPP), caffeic acid, ferulic acid, gallic acid, butylated hydroxytoluene, tertiary butylhydroquinone, butylated hydroxyanisole, propyl gallate, and tea polyphenols) were grafted into epoxidized soybean oils-PSA (ESO-PSA) system to enhance antiaging properties and adhesion strengths. Results showed ESO-PSAs grafted with caffeic acid, tertiary butylhydroquinone, butylated hydroxyanisole, propyl gallate, tea polyphenols, or TPP didn't occur failure with TPP having best performance. The optimal conditions were ESO reacted with 0.9 % TPP, 70 % rosin ester, and 7.0 % phosphoric acid at 50 °C for 5 min, under which peel strength and loop tack increased to 2.460 N/cm and 1.66 N, respectively, but peel strength residue reduced to 138.09 %, compared with control (0.407 N/cm, 0.43 N, and 1669.99 %). Differential scanning calorimetry and thermogravimetric results showed TPP grafting increased the glass transition temperature of ESO-PSA slightly but improved its thermal stability significantly. Fourier transform infrared spectroscopy and 1H nuclear magnetic resonance results showed TPP, phosphoric acid, and rosin ester all partially participated in the covalently crosslinking polymerization of ESO-PSAs and the rest existed in the network structures in the free form.

Epoxidized Soybean-Oils-Based Pressure-Sensitive Adhesives with Di-Hydroxylated Soybean-Oils Copolymerizing and Antioxidant Grafting

Vegetable-oils-based pressure-sensitive adhesives (PSAs) are being developed as a substitute for petrochemical-based PSAs for application in daily life. However, vegetable-oils-based PSAs face the problems of unsatisfactory binding strengths and easy aging. In this work, the grafting of antioxidants (tea polyphenol palmitates, caffeic acid, ferulic acid, gallic acid, butylated hydroxytoluene, tertiary butylhydroquinone, butylated hydroxyanisole, propyl gallate (PG), tea polyphenols) was introduced into an epoxidized soybean oils (ESO)/di-hydroxylated soybean oils (DSO)-based PSA system to improve the binding strengths and aging-resistant properties. PG was screened out as the most suitable antioxidant in the ESO/DSO-based PSA system. Under optimal conditions (ESO/DSO mass ratio of 9/3, 0.8% PG, 55% rosin ester (RE), 8% phosphoric acid (PA), 50 °C, and 5 min), the peel adhesion, tack, and shear adhesion of the PG-grafted ESO/DSO-based PSA increased to 1.718 N/cm, 4.62 N, and >99 h, respectively, in comparison with the control (0.879 N/cm, 3.59 N, and 13.88 h), while peel adhesion residue reduced to 12.16% in comparison with the control (484.07%). The thermal stability of the ESO/DSO-based PSA was enhanced after PG grafting. PG, RE, PA, and DSO were partially crosslinked in the PSA system, with the rest being free in the network structures. Thus, antioxidant grafting is a feasible method for improving the binding strengths and aging-resistant properties of vegetable-oils-based PSAs.

Approaches in Sustainable, Biobased Multilayer Packaging Solutions

The depletion of fossil resources and the growing demand for plastic waste reduction has put industries and academic researchers under pressure to develop increasingly sustainable packaging solutions that are both functional and circularly designed. In this review, we provide an overview of the fundamentals and recent advances in biobased packaging materials, including new materials and techniques for their modification as well as their end-of-life scenarios. We also discuss the composition and modification of biobased films and multilayer structures, with particular attention to readily available drop-in solutions, as well as coating techniques. Moreover, we discuss end-of-life factors, including sorting systems, detection methods, composting options, and recycling and upcycling possibilities. Finally, regulatory aspects are pointed out for each application scenario and end-of-life option. Moreover, we discuss the human factor in terms of consumer perception and acceptance of upcycling.

Adhesive Interfaces toward a Zero-Waste Industry

This Feature Article evaluates ongoing efforts to adapt adhesives toward the goal of zero-waste living and suggests the most promising future directions. Adhesives are not always considered in zero-waste manufacturing because they represent only a small fraction of a product and offer no additional functionality. However, their presence restricts the reintegration of constituent parts into a circular economy, so a new generation of adhesives is required. Furthermore, their production often leads to harmful pollutants. Here, two main approaches toward addressing these problems are considered: first, the use of natural materials that replace petroleum-based polymers from which conventional adhesives are made and second, the production of dismantlable adhesives capable of debonding on demand with the application of an external stimulus. These approaches, either individually or combined, offer a new paradigm in zero-waste industrial production and consumer applications.

End of Life of Biodegradable Plastics: Composting versus Re/Upcycling

Nowadays the issues related to the end of life of traditional plastics are very urgent due to the important pollution problems that plastics have caused. Biodegradable plastics can help to try to mitigate these problems, but even bioplastics need much attention to carefully evaluate the different options for plastic waste disposal. In this Minireview, three different end-of-life scenarios (composting, recycling, and upcycling) were evaluated in terms of literature review. As a result, the ability of bioplastics to be biodegraded by composting has been related to physical variables and materials characteristics. Hence, it is possible to deduce that the process is mature enough to be a good way to minimize bioplastic waste and valorize it for the production of a fertilizer. Recycling and upcycling options, which could open up many interesting new scenarios for the production of high-value materials, are less studied. Research in this area can be strongly encouraged.

Bio-based and Degradable Block Polyester Pressure-Sensitive Adhesives

A new class of bio-based fully degradable block polyesters are pressure-sensitive adhesives. Bio-derived monomers are efficiently polymerized to make block polyesters with controlled compositions. They show moderate to high peel adhesions (4-13 N cm-1 ) and controllable storage and loss moduli, and they are removed by adhesive failure. Their properties compare favorably with commercial adhesives or bio-based polyester formulations but without the need for tackifier or additives.

The optimization of heterogeneous catalytic conditions in the direct alkylation of waste vegetable oil

Alkylated waste vegetable oil is a versatile intermediate product in the synthesis of bio-based materials. Heterogeneous catalytic condition with high conversion rate in the direct alkylation of waste vegetable oil was reported and the deactivation mechanism of catalyst was revealed. The total exchange capacity, elemental composition and pyrolysis product of catalyst before and after the alkylation reaction were analysed by back titration, elemental analysis, electrospray ionization mass spectrometry, gas chromatography mass spectrometry and pyrolysis-gas chromatography/mass spectrometry, respectively. The results indicated that the metallic and non-metallic (C, H) elements contents of the catalyst have very much increased with great changes in pyrolysis product and a slight decrease in the total exchange capacity. The formation of insoluble polymers through Diels-Alder cycloaddition between triglycerides was proved to be the major factor causing the dysfunction of the catalytic centre. The metal ions from corrosion of the reactor were the minor factor causing about 2.56% loss of the catalytic centre. Moreover, the catalyst was able to maintain high catalytic efficiency when replacing the raw materials with other waste vegetable oil having low concentration of polyunsaturated fatty acids, which is significant for producing not only the aryl fatty acids derivatives but also the bio-based surfactants.

Tailoring Acrylated Soybean Oil-Containing Terpolymers through Emulsion Polymerization

This work focuses on the synthesis of terpolymers using methyl methacrylate (MMA) and vinyl pivalate (VPi), along with the incorporation of methacrylate acid (MA) and acrylated fatty acids (AFA) derived from commercial soybean oil. Emulsion polymerizations were carried out using different monomeric species, along with different initiator concentrations ranging from 0.5 g∙L−1 to 2.2 g∙L−1. The thermal properties of the terpolymers were improved when acrylated fatty acid was incorporated into the polymer chains, expressing glass transition temperatures (Tg) ranging from 70 °C to 90 °C and degradation temperatures in the interval between 350 °C and 450 °C for acrylated fatty acid concentrations ranging from 5 wt% to 10 wt%. Furthermore, a change was noted in the molar mass distributions as a result of acrylated fatty oil present in the polymers. The materials with 5 and 10 wt% of acrylated fatty oil presented mass-average molar masses of 225 kg∙mol−1 and 181 kg∙mol−1, respectively. As the results in this work suggest, the molar masses of the formed polymers are significantly altered by the presence of modified fatty acids.