Study on Osseointegration Capability of β-Type Ti-Nb-Zr-Ta-Si Alloy for Orthopedic Implants

Osseointegration is the basic condition for orthopedic implants to maintain long-term stability. In order to achieve osseointegration, a low elastic modulus is the most important performance indicator. It is difficult for traditional titanium alloys to meet this requirement. A novel β-titanium alloy (Ti-35Nb-7Zr-5Ta)98Si2 was designed, which had excellent strength (a yield strength of 1296 MPa and a breaking strength 3263 MPa), an extremely low elastic modulus (37 GPa), and did not contain toxic elements. In previous in vitro studies, we confirmed the good biocompatibility of this alloy and similar bioactivity to Ti-6Al-4V, but no in vivo study was performed. In this study, Ti-6Al-4V and (Ti-35Nb-7Zr-5Ta)98Si2 were implanted into rabbit femurs. Imaging evaluation and histological morphology were performed, and the bonding strength and bone contact ratio of the two alloys were measured and compared. The results showed that both alloys remained in their original positions 3 months after implantation, and neither imaging nor histological observations found inflammatory reactions in the surrounding bone. The bone-implant contact ratio and bonding strength of (Ti-35Nb-7Zr-5Ta)98Si2 were significantly higher than those of Ti-6Al-4V. The results confirmed that (Ti-35Nb-7Zr-5Ta)98Si2 has a better osseointegration ability than Ti-6Al-4V and is a promising material for orthopedic implants.

Laser Powder Bed Fusion Additive Manufacturing of a Low-Modulus Ti-35Nb-7Zr-5Ta Alloy for Orthopedic Applications

Laser powder bed fusion (L-PBF) was attempted here to additively manufacture a new generation orthopedic β titanium alloy Ti-35Nb-7Zr-5Ta toward engineering patient-specific implants. Parts were fabricated using four different values of energy density (ED) input ranging from 46.6 to 54.8 J/mm³ through predefined laser beam parameters from prealloyed powders. All the conditions yielded parts of >98.5% of theoretical density. X-ray microcomputed tomography analyses of the fabricated parts revealed minimal imperfections with enhanced densification at a higher ED input. X-ray diffraction analysis indicated a marginally larger d-spacing and tensile residual stress at the highest ED input that is ascribed to the steeper temperature gradients. Cellular to columnar dendritic transformation was observed at the highest ED along with an increase in the size of the solidified features indicating the synergetic effects of the temperature gradient and solidification growth rate. Density measurements indicated ≈99.5% theoretical density achieved for an ED of 50.0 J/mm³. The maximum tensile strength of ≈660 MPa was obtained at an ED of 54.8 J/mm³ through the formation of the columnar dendritic substructure. High ductility ranging from 25 to 30% was observed in all the fabricated parts irrespective of ED. The assessment of cytocompatibility in vitro indicated good attachment and proliferation of osteoblasts on the fabricated samples that were similar to the cell response on commercially pure titanium, confirming the potential of the additively manufactured Ti-35Nb-7Zr-5Ta as a suitable material for biomedical applications. Taken together, these results demonstrate the feasibility of L-PBF of Ti-35Nb-7Zr-5Ta for potentially engineering patient-specific orthopedic implants.

Comparative study on Ti-Nb binary alloys fabricated through spark plasma sintering and conventional P/M routes for biomedical application

The main purpose of this work is to obtain homogenous, single β phase in binary Ti-xNb (x = 18.75, 25, and 31.25 at.%) alloys by simple mixing of pure elemental powders using different sintering techniques such as spark plasma sintering (pressure-assisted sintering) and conventional powder metallurgy (pressure-less sintering). Synthesis parameters such as sintering temperature and holding time etc. are optimized in both techniques in order to get homogenous microstructure. In spark plasma sintering (SPS), complete homogeneous β phase is achieved in Ti25at.%Nb using 1300 °C sintering temperature with 60 min holding time under 50 MPa pressure. On the other hand, complete β phase is obtained in Ti25at.%Nb through conventional powder metallurgy (P/M) route using sintering temperature of 1400 °C for 120 min holding time which are adopted from the dilatometry studies. Nano-indentation is carried out for mechanical properties such as Young's modulus and nano-hardness. Elastic properties of binary Ti-xNb compositions are fallen within the range of 80-90 GPa. Cytotoxicity as well as cell adhesion studies carried out using MG63, osteoblast-like cells showed excellent biocompatibility of thus developed Ti25at.%Nb surface irrespective of fabrication route.