Polymeric composite membranes in carbon dioxide capture process: a review

Carbon dioxide (CO₂) emission to the atmosphere is the prime cause of certain environmental issues like global warming and climate change, in the present day scenario. Capturing CO₂ from various stationary industrial emission sources is one of the initial steps to control the aforementioned problems. For this concern, a variety of resources, such as liquid absorbents, solid adsorbents, and membranes, have been utilized for CO₂ capturing from various emission sources. Focused on membrane-based CO₂ capture, polymeric membranes with composite structure (polymeric composite membrane) offer a better performance in CO₂ capturing process than other membranes, due to the composite structure it offers higher gas flux and less material usage, thus facile to use high performed expensive material for membrane fabrication and achieved good efficacy in CO₂ capture. This compressive review delivers the utilization of different polymeric composite membranes in CO₂ capturing applications. Further, the types of polymeric materials used and the different physicochemical modifications of those membrane materials and their CO₂ capturing ability are briefly discussed in the text. In conclusion, the current status and possible perspective ways to improve the CO₂ capture process in industrial CO₂ gas separation applications are described in this review.

A review on chitosan-based membranes for sustainable CO2 separation applications: Mechanism, issues, and the way forward

Effective carbon dioxide (CO₂) separation by nominal energy utilization is the factual attempt in the present era of energy scarcity and environmental calamity. In this perspective, the membrane- based gas separation technology is a budding endeavour owing to its cost -effectiveness, ease of operational maintenance and compact modular design. Among various membrane materials, bio-based polymers are of interest as they are abundant and can be obtained from renewable resources, and can also reduce our dependency on exhaustible fossil fuel-based sources. In this review, the structure-property relationship of chitosan and some of its film-forming derivatives has been critically studied for the first time in view of the fundamental properties required for gas separation applications. Various factors affecting the gas permeation performance of chitosan-based membranes have been highlighted along with prospects and propositions for the design of a few novel bio-based membranes based on the exhaustive analyses.

Graphene-Incorporated Biopolymeric Mixed-Matrix Membrane for Enhanced CO2 Separation by Regulating the Support Pore Filling

The CO₂ separation performance by a membrane is influenced essentially by film thickness, temperature, moisture, and pressure. Pore formation on the active layer and pore clogging of the membrane support are critical factors that impedes the CO₂ separation performance. This study involves the development of a novel nanocomposite membrane (CS/SF/GNP) consisting of chitosan (CS), silk fibroin (SF), and graphene nanoparticles (GNP). The CS acts as the matrix, SF contributes to the CO₂ facilitated transport by its inherent amines as carriers, and GNP helped in counteracting the support pore blockage during the gas separation test. The positive effect of GNP in the CS/SF/GNP was further apparent in the CO₂ permeance inconsequential drop of ∼7% during the initial 12 h in the presence of moisture and pressure. The detailed characterizations including FESEM, AFM, and swelling were performed for the membranes. The effect of sweep water flow rate, temperature, and feed absolute pressure on CO₂ separation performance from binary gas were performed. The CS/SF/GNP membrane exhibited CO₂ permeance of 159 GPU and CO₂/N₂ selectivity of 93 at 90 °C and a feed absolute pressure of 2 bar having a sweep side water flow rate of 0.05 mL/min. Further, when CS/SF/GNP membrane was tested to separate CO₂ from ternary gas mixture (CO₂/N₂/H₂), it displayed excellent CO₂ permeance of 126 GPU and selectivity for CO₂/N₂ and CO₂/H₂ as 104 and 52, respectively. The TGA isotherm and XPS analysis of CS/SF/GNP membrane suggested a thermal stability of the prepared membrane that establishes its suitability for the gas permeation at different temperature.