Performance and Mechanism of Co and Mn Loaded on Fe-Metal-Organic Framework Catalysts with Different Morphologies for Simultaneous Degradation of Acetone and NO by Photothermal Coupling

VOCs can be used instead of ammonia as a reducing agent to remove NO, achieving the effect of removing VOCs and NO simultaneously. Due to the high energy consumption and low photocatalytic efficiency required for conventional thermocatalytic purification, photothermal coupled catalytic purification can integrate the advantages of photocatalysis and thermocatalysis in order to achieve the effect of pollutants being treated efficiently with a low energy consumption. In this study, samples loaded with Co and Mn catalysts were prepared using the hydrothermal method on Fe-MOF with various morphologies. The catalytic performance of each catalyst was analyzed by studying the effects of their physicochemical properties through various characterizations, including XRD, SEM, BET, XPS, H2-TPR, TEM and O2-TPD. The characterization results demonstrated that the specific surface area, pore volume, high valence Co and Mn atoms, surface adsorbed oxygen and the abundance of oxygen lattice defects in the catalysts were the most critical factors affecting the performance of the catalysts. Based on the results of the performance tests, the catalysts prepared with an octahedral-shaped Fe-MOF loaded with Co and Mn showed a better performance than those loaded with Co and Mn on a rod-shaped Fe-MOF. The conversions of acetone and NO reached 50% and 64%, respectively, at 240 °C. The results showed that the catalysts were capable of removing acetone and NO at the same time. Compared with the pure Fe-MOF without Co and Mn, the loaded catalysts showed a significantly higher ability to remove acetone and NO simultaneously under the combination of various factors. The key reaction steps for the catalytic conversion of acetone and NO on the catalyst surface were investigated according to the Mars-van Krevelen (MvK) mechanism, and a possible mechanism was proposed. This study presents a new idea for the simultaneous removal of acetone and NOx by photothermal coupling.

Hierarchical Porous Carbon Cobalt Nanocomposites-Based Sensor for Fructose

3D hierarchical graphitic carbon nanowalls encapsulating cobalt nanoparticles HPC-Co were prepared in high yield from solid-state pyrolysis of cobalt 2,2′-bipyridine chloride complex. Annealing of HPC-Co in air gave HPC-CoO, which consists of a mixture of crystallite Co3O4 nanospheres and nanorods bursting out of mesoporous carbon. Both nanocomposites were fully characterized using SEM, TEM, BET, and powder X-ray diffraction. The elemental composition of both nanocomposites examined using SEM elemental mapping and TEM elemental mapping supports the successful doping of nitrogen. The powder X-ray diffraction studies supported the formation of hexagonal cobalt in HPC-Co, and cubic crystalline Co3O4 with cubic cobalt in HPC-CoO. HPC-Co and HPC-CoO can be used as a modified carbon electrode in cyclic voltammetry experiments for the detection of fructose with limit of detection LOD 0.5 mM. However, the single-frequency impedimetric method has a wider dynamic range of 8.0–53.0 mM and a sensitivity of 24.87 Ω mM−1 for the electrode modified with HPC-Co and 8.0–87.6 mM and a sensitivity of 1.988 Ω mM−1 for the electrode modified with HPC-CoO. The LOD values are 3 and 4 mM, respectively. The effect of interference increases in the following order: ascorbic acid, ethanol, urea, and glucose. A simple method was used with negligible interference from glucose to measure the percentage of fructose in a corn syrup sample with an HPC-CoO electrode. A specific capacitance of 47.0 F/g with 76.6% retentivity was achieved for HPC-Co and 28.2 F/g with 87.9% for HPC-CoO for 3000 charge–discharge cycles. Thus, (1) has better sensitivity and specific capacitance than (2), because (1) has a higher surface area and less agglomerated cobalt nanoparticles than (2).

Galvanic displacement assembly of ultrathin Co3O4 nanosheet arrays on nickel foam for a high-performance supercapacitor

High-performance supercapacitors are very desirable for many portable electronic devices, electric vehicles and high-power electronic devices. Herein, a facile and binder-free synthesis method, galvanic displacement of the precursor followed by heat treatment, is used to fabricate ultrathin Co₃O₄ nanosheet arrays on nickel foam substrate. When used as a supercapacitor electrode the prepared Co₃O₄ on nickel foam exhibits a maximum specific capacitance of 1095 F g^-1 at a current density of 1 A g^-1 and good cycling stability of 71% retention after 2000 cycling tests. This excellent electrochemical performance can be ascribed to the high specific surface area of each Co₃O₄ nanosheet that comprises numerous nanoparticles.

Co3O4/RGO/Co3O4 pseudocomposite grown in situ on a Co foil for high-performance supercapacitors

A Co₃O₄/RGO/Co₃O₄ pseudocomposite was grown in situ on a Co substrate using a one-step hydrothermal process and exhibited excellent electrochemical performances.

Facile morphology controlled synthesis of nanostructured Co3O4 films on nickel foam and their pseudocapacitive performance

The as-synthesized 3D hierarchically porous Co₃O₄ network film on nickel foam shows prominent pseudocapacitive performance.