Magnetic ZnFe2O4 composite advances SERS assay for Patent blue V

BACKGROUND

Patent blue V (PbV) an Azo colorant because of its high toxicity to children has been severely limited in food industry. However, frequently the abuse of PbV in some artificial foods is still exposed by media. Current methods for the detection of PbV have to perform tedious pre-processing and the detection sensitivity and speed are required to be further improved.

RESULTS

In this work, we immobilize gold nanoparticles (Au NPs) on the surface of ZnFe2O4 with aid of Inositol hexaphosphate (IP6) to prepare a novel magnetic surface-enhanced Raman scattering (SERS) substrate (designated as ZnFe2O4-IP6-Au NPs) for rapid detection of PbV in beverages. Synergistic effect of magnetic enrichment, magnetic inducing improvement effect (MIIE) and efficient charge transfer (CT) enables ZnFe2O4-IP6-Au NPs-based SERS assay to achieve limit of detection of PbV down to 1.31 × 10-8 mol/L and a concentration linear relationship ranging from 8.6 × 10-4 to 8.6 × 10-8 mol/L. The detection recoveries for PbV in beverages locate in the range from 98.1 to 102.5 %, meaning the feasibility of method. In addition, the presence of IP6 protection greatly improves the storage stability of ZnFe2O4-IP6-Au NPs.

SIGNIFICANCE

ZnFe2O4-IP6-Au NPs substrates with excellent SERS performance could on-site, rapidly and sensitively detect PbV. As a perspective, magnetic-composite-based SERS assay has great scenario in food safety by using portable Raman spectrometer.

Thin layer chromatography coupled with surface enhanced Raman scattering for rapid separation and on-site detection of multi-components

The separation and detection of multi-component mixtures has always been a challenging task. Traditional detection methods often suffer from complex operation, high cost, and low sensitivity. Surface enhanced Raman scattering (SERS) technique is a high sensitivity, powerful and rapid detection tool, which can realize the specific detection of single substance components, but it must solve the problem that multi-component mixtures cannot be accurately determined. Thin layer chromatography (TLC) technology, as a high-throughput separation technology, uses chromatographic plate as the stationary phase, and could select different developing phases for separation experiments. The advantages of TLC technology in short distance and rapid separation are widely used in protein, dye and biomedical fields. However, TLC technology has limitations in detection ability and difficulty in obtaining ideal signal intensity. The combination of TLC technology and SERS technology made the operation procedure simple and the sample size small, which can achieve rapid on-site separation and quantitative detection of mixtures. Due to the rapid development of TLC-SERS technology, it has been widely used in the investigation of various complex systems. This paper reviews the application of TLC-SERS technology in food science, environmental pollution and biomedicine.

Combining surface-accessible Ag and Au colloidal nanomaterials with SERS for in situ analysis of molecule-metal interactions in complex solution environments

The interactions between molecules and noble metal nanosurfaces play a central role in many areas of nanotechnology. The surface chemistry of noble metal surfaces under ideal, clean conditions has been extensively studied; however, clean conditions are seldom met in real-world applications. We developed a sensitive and robust characterization technique for probing the surface chemistry of nanomaterials in the complex environments that are directly relevant to their applications. Surface-enhanced Raman spectroscopy (SERS) can be used to probe the interaction of plasmonic nanoparticles with light to enhance the Raman signals of molecules near the surface of nanoparticles. Here, we explain how to couple SERS with surface-accessible plasmonic-enhancing substrates, which are capped with weakly adsorbing capping ligands such as citrate and chloride ions, to allow molecule-metal interactions to be probed in situ and in real time, thus providing information on the surface orientation and the formation and breaking of chemical bonds. The procedure covers the synthesis and characterization of surface-accessible colloids, the preliminary SERS screening with agglomerated colloids, the synthesis and characterization of interfacial nanoparticle assemblies, termed metal liquid-like films, and the in situ biphasic SERS analysis with metal liquid-like films. The applications of the approach are illustrated using two examples: the probing of π-metal interactions and that of target/ligand-particle interactions on hollow bimetallic nanostars. This protocol, from the initial synthesis of the surface-accessible plasmonic nanoparticles to the final in situ biphasic SERS analysis, requires ~14 h and is ideally suited to users with basic knowledge in performing Raman spectroscopy and wet synthesis of metal nanoparticles.

Raman Spectroscopy and Surface Enhanced Raman Scattering (SERS) for the Analysis of Blue and Black Writing Inks: Identification of Dye Content and Degradation Processes

Raman spectroscopy and Surface Enhanced Raman Scattering (SERS) were applied to the analysis of blue and black writing inks. SERS was performed by application of plasmonic nanopastes constituted by Ag nanoparticles and Au nanorods directly on inks deposited on paper substrates under laser irradiation of 514 nm. It was found that SERS spectra were largely enhanced compared to Raman spectra and that Ag nanopastes produced much larger enhancements than Au nanopastes, due to a combination of plasmonic resonance, charge transfer, and molecular resonance effects. All analyzed writing inks resulted constituted by Crystal Violet and other triarylmethane dye mixtures, to which sometimes phthalocyanine dyes were also added (for example in Bic pens). SERS was also used for the identification of degradation processes occurring in artificially aged blue pens deposited on paper substrates. It was found that color alteration changed from ink to ink and varied from darkening to discoloration to slight fading, depending on the initial chemical composition. For inks containing Crystal Violet, two mechanisms associated to de-methylation and photo-reduction of excited dye to colorless leuco forms were identified.

Arsenic Speciation on Silver Nanofilms by Surface-Enhanced Raman Spectroscopy

Surface-enhanced Raman spectroscopy (SERS), as a nondestructive and fast detection technique, is a promising alternative approach for arsenic detection, particularly for in situ applications. SERS-based speciation analysis according to the fingerprint SERS signals of different arsenicals has the potential to provide a superior technique in species preservation over the conventional chromatographic separation methods, albeit with some difficulties due to the similarity in SERS patterns. In this study, we explored a novel SERS method for arsenic speciation by using the separation potential of the coffee ring effect on negatively charged silver nanofilms (AgNFs). Four arsenic species, including arsenite (As^III), arsenate (As^V), monomethylarsonic acid (MMA^V), and dimethylarsinic acid (DMA^V), were measured for fingerprint SERS signals in solution and on the films. Significant enhancement of SERS signals on the dried coffee ring stains by the AgNFs were observed except for As^III, and more importantly, arsenicals migrated varying distances during coffee ring development, promoting better speciation. Sodium dodecyl sulfate was then introduced into the droplet to reduce the droplet surface tension, facilitating the migration of solution into the peripheral region. Under the combined interactions of arsenicals with the AgNFs, solvent, and surfactant, enhanced separation between arsenicals was observed as a result of the formation of two concentric rings. Combining the SERS fingerprint signals and physical separation of arsenicals on the surface, arsenic speciation was achieved using the AgNFs substrate-based SERS technology, demonstrating the potential of the coffee ring effect for rapid separation and analysis of small molecules by SERS.

Direct and comprehensive analysis of dyes based on integrated molecular and structural information via laser desorption laser postionization mass spectrometry

Laser desorption laser postionization time-of-flight mass spectrometry (LDPI-TOFMS) was employed for direct analysis and determination of typical basic dyes. It was also used for the analysis and comprehensive understanding of complex materials such as blue ballpoint pen inks. Simultaneous emergences of fragmental and molecular information largely simplify and facilitate unambiguous identification of dyes via variable energy of 266nm postionization laser. More specifically, by optimizing postionization laser energy with the same energy of desorption laser, the structurally significant results show definite differences in the fragmentation patterns, which offer opportunities for discrimination of isomeric species with identical molecular weight. Moreover, relatively high spectra resolution can be acquired without the expense of sensitivity. In contrast to laser desorption/ionization mass spectrometry (LDI-MS), LDPI-MS simultaneously offers valuable molecular information about dyes in traces, solvents and additives about inks, thereby offering direct determination and comprehensive understanding of blue ballpoint inks and giving a high level of confidence to discriminate the complicated evidentiary samples. In addition, direct analysis of the inks not only allows the avoidance of the tedious sample preparation processes, significantly shortening the overall analysis time and improving throughput, but allows minimized sample consumption which is important for rare and precious samples.