Eggshell membranes coated chitosan decorated with metal nanoparticles for the catalytic reduction of organic contaminates

This study focusses on the effect of chitosan coating with eggshell membranes for the reduction of different organic pollutants. Chickens eggs were collected from the local market and utilized to extract the enrich eggshell membranes (ESM). The chicken eggshell membranes are abundant waste material which is inexpensive and illustrates remarkable physiognomies for many possible applications. Fresh fibers/strips coated by chitosan (CS) were prepared by mixing the eggshell membranes with CS solution (2 wt%/v) in different proportions i.e., 10 %, 30 %, 50 %, 60 %, 70 %, 80 %, and 90 %. These strips were then templated with copper and iron metal nanoparticles by putting them in their metal ions aqueous solution to adsorb the metals ions and were then reduced to zero-valent metal nanoparticles (MNPS) by using NaBH₄ aqueous solution. These prepared materials (MNPS@ESM-CS) were characterized by using XRD, XPS, FE-SEM, and EDS to confirm the successful preparation of MNPs over the surface of ESM coated with CS. Afterwards, these prepared materials were investigated as a catalyst for the reduction of different organic pollutants, such as 4-nitroaniline (4-NA), 4-nitrophenol (4-NP) and methylene blue (MB) dye. The catalytic efficiency of ESM was enhanced 5.7-fold by adding only 20 % CS solution. It was observed that Cu@ESM-CS-80 % took 7 min for reduction of 4-NA, 6 min for 4-NP, and 7 min for MB dye. The reusability of the catalytic strip was also investigated for four cycles and found efficient and can be easily recovered by simply pulling it from the reaction mixture.

Bi-Metal Phosphide NiCoP: An Enhanced Catalyst for the Reduction of 4-Nitrophenol

Porous phosphide NixCoyP composite nanomaterials are successfully synthesized at different Ni/Co ratios (=0, 0.5, 1, and 2) to reduce 4-nitrophenol. The X-ray diffraction and X-ray photoelectron spectroscopy results demonstrate that the products are CoP, NiCoP/CoP, NiCoP, and NiCoP/Ni₂P when the Ni/Co ratio is 0, 0.5, 1, and 2, respectively. The products exhibit different catalytic performance for reduction of 4-nitrophenol at room temperature. Among them, the pure NiCoP delivers a better catalytic efficiency with k app = 677.4 × 10 - 2   min - 1 and k = 338.7   ( Lg - 1 min - 1 ) , due to the synergy between Ni and Co atoms. The sequence of catalytic efficiency of different samples is CoP < NiCoP/CoP < NiCoP/Ni₂P < NiCoP.

MnCo2O4+x nanowire arrays grown on carbon sponge: improved electrochemical and catalytic performances

MnCo₂O_4+x nanowire arrays with improved electrochemical and catalytic performances were successfully grown on carbon sponge via a hydrothermal–pyrolysis route.

Porous CoP nanosheets converted from layered double hydroxides with superior electrochemical activity for hydrogen evolution reactions at wide pH ranges

Simple etching and phosphidation of LDHs to form porous CoP for superior electrocatalyst HER performance over wide pH ranges.

Chitosan coated cotton cloth supported zero-valent nanoparticles: Simple but economically viable, efficient and easily retrievable catalysts

A simple, economically viable and fast method has been utilized for the preparation of highly active metal nanoparticles (MNPs) in coating layer of chitosan (CH) over cellulose microfibers of cotton cloth (CC). 2 wt% of CH solution was used for the coating of CC strips (CC-CH), and were kept in aqueous solutions of metal salts to adsorb metal ions. The CC-CH templated with metal ions were then treated with aqueous solution of NaBH₄ to reduce the metal ions into zero-valent metal nanoparticles (M⁰). The CC-CH strips loaded with M⁰ were characterized by XRD, XPS, ATR-FTIR, FE-SEM and TGA, which indicates the successful synthesis of MNPs by this method. The M⁰/CC-CH strips were used as an efficient catalyst for the model reduction reaction of nitrophenol and toxic organic dyes. Among all the prepaped samples, Fe/CC-CH showed good catalytic activity for 4-NP and Rh-B dye reduction in the presence of NaBH₄ with rate constants of 0.2937 min^-1 and 0.3804 min^-1, respectively. Moreover Fe/CC-CH has good catalytic reduction ability for MO and MB having rate constants equal to 0.1698 and 0.2802 min^-1, respectively. Beside the good catalytic ability, it could be easily recoverable as compared to other available techniques. The recovery was completed by simply pulling the strip from the reaction matrix after completion of the reaction and can be used several times.