Highly Porous SnO2/TiO2 Heterojunction Thin-Film Photocatalyst Using Gas-Flow Thermal Evaporation and Atomic Layer Deposition

Highly porous heterojunction films of SnO2/TiO2 were prepared using gas-flow thermal evaporation followed by atomic layer deposition (ALD). Highly porous SnO2 was fabricated by introducing an inert gas, Ar, during thermal evaporation. To build heterogeneous structures, the TiO2 layers were conformally deposited on porous SnO2 with a range of 10 to 100 cycles by means of ALD. The photocatalytic properties for different TiO2 thicknesses on the porous SnO2 were compared using the degradation of methylene blue (MB) under UV irradiation. The comparisons showed that the SnO2/TiO2-50 heterostructures had the highest photocatalytic efficiency. It removed 99% of the MB concentration, and the decomposition rate constant (K) was 0.013 min−1, which was approximately ten times that of the porous SnO2. On the other hand, SnO2/TiO2-100 exhibited a lower photocatalytic efficiency despite having a TiO2 layer thicker than SnO2/TiO2-50. After 100 cycles of TiO2 ALD deposition, the structure was transferred from the heterojunction to the core–sell structure covered with TiO2 on the porous SnO2, which was confirmed by TEM analysis. Since the electrons photogenerated by light irradiation were separated into SnO2 and produced reactive oxygen, O2−, the heterojunction structure, in which SnO2 was exposed to the surface, contributed to the high performance of the photocatalyst.

N-Doped Yellow TiO2 Hollow Sphere-Mediated Visible-Light-Driven Efficient Esterification of Alcohol and N-Hydroxyimides to Active Esters

Herein we report a simple synthetic protocol for N-doped yellow TiO₂ (N-TiO₂ ) hollow spheres as an efficient visible-light-active photocatalyst using aqueous titanium peroxocarbonate complex (TPCC) solution as precursor and NH₄ OH. In the developed strategy, the ammonium ion of TPCC and NH₄ OH acts as nitrogen source and structure-directing agent. The synthesized N-TiO₂ hollow spheres are capable of promoting the synthesis of active esters of N-hydroxyimide and alcohol through simultaneous selective oxidation of alcohol to aldehyde followed by cross-dehydrogenative coupling (CDC) under ambient conditions upon irradiation of visible light. It is possible to develop a novel and cost-effective one-pot strategy for the synthesis of important esters and amides on gram scale using the developed strategy. The catalytic activity of N-TiO₂ hollow spheres is much superior to that of other reported N-TiO₂ samples as well as TiO₂ with varying morphology.

Phase and morphology transformation from assembled hexagonal HTiOF3 prisms to {001} faceted TiO2 nanosheets

A three-stage synthesis method was developed for the preparation of TiO₂ nanosheets with exposed {001} facets by a solvothermal process.