Low-temperature open-air synthesis of PVP-coated NaYF4:Yb,Er,Mn upconversion nanoparticles with strong red emission

Cubic (α-phase) NaYF₄:Yb,Er upconversion nanoparticles (UCNPs) are uniquely suited to biophotonics and biosensing applications due to their near-infrared excitation and visible red emission (λ _ex approx. 660 nm), enabling detection via thick overlying tissue with no bio-autofluorescence. However, UCNP synthesis typically requires high temperatures in combination with either high pressure reaction vessels or an inert atmosphere. Here, we report synthesis of α-phase NaYF₄:Yb,Er,Mn UCNPs via the considerably more convenient PVP40-mediated route; a strategy that requires modest temperatures and relatively short reaction time (160°C, 2 h) in open air, with Mn²⁺ co-doping serving to greatly enhance red emission. The optimal Mn²⁺ co-doping level was found to be 35 mol %, which decreased the average maximum UCNP Feret diameter from 42 ± 11 to 36 ± 15 nm; reduced the crystal lattice parameter, a, from 5.52 to 5.45 Å; and greatly enhanced UCNP red/green emission ratio in EtOH by a factor of 5.6. The PVP40 coating enabled dispersal in water and organic solvents and can be exploited for further surface modification (e.g. silica shell formation). We anticipate that this straightforward UCNP synthesis method for producing strongly red-emitting UCNPs will be particularly beneficial for deep tissue biophotonics and biosensing applications.

Enhancing upconversion of manganese through spatial control of energy migration for multi-level anti-counterfeiting

The upconversion of manganese (Mn²⁺) exhibits a green light output with a much longer lifetime than that of lanthanide ions, showing great potential in the frontier applications like information security and anti-counterfeiting. Mn²⁺ can be activated by energy migration upconversion. However, there exists serious quenching interactions between Mn²⁺ and the lanthanides at the core-shell interfacial area, which would markedly reduce the role of Tm³⁺ as a ladder to facilitate the up-transition and subsequently limit the upconversion of Mn²⁺. Here, we propose a mechanistic strategy to enhance the upconversion luminescence of Mn²⁺ by spatial control of energy migration among Gd sublattice through introducing an additional migratory NaGdF₄ interlayer within the commonly used core-shell nanostructure. This design can not only isolate the interfacial quenching interactions between the sensitized core and luminescent shell, but also allow an efficient channel for energy transport, resulting in enhanced upconversion of Mn²⁺. Moreover, the relatively long lifetime of Mn²⁺ (around 32.861 ms) provides new possibilities to utilize the temporal characteristic for the frontier application of multi-level anti-counterfeiting through combining the time-gating technology.

NaGdF4:Yb,Er-Ag nanowire hybrid nanocomposite for multifunctional upconversion emission, optical imaging, MRI and CT imaging applications

The effect of novel silver nanowire encapsulated NaGdF₄:Yb,Er hybrid nanocomposite on the upconversion emission and bioimaging properties has been investigated. The upconvension nanomaterials were synthesised by polyol method in the presence of ethylene glycol, PVP and ethylenediamine. The NaGdF₄:Yb,Er-Ag hybrid was formed with upconverting NaGdF₄:Yb,Er nanoparticles of size ~ 80 nm and silver nanowires of thickness ~ 30 nm. The surface plasmon induced by the silver ion in the NaGdF₄:Yb,Er-Ag nanocomposite resulted an intense upconversion green emission at 520 nm and red emission at 660 nm by NIR diode laser excitation at 980 nm wavelength. The UV-Vis-NIR spectral absorption at 440 nm and 980 nm, the intense Raman vibrational modes and the strong upconversion emission results altogether confirm the localised surface plasmon resonance effect of silver ion in the hybrid nanocomposite. MRI study of both NaGdF₄:Yb,Er nanoparticle and NaGdF₄:Yb,Er-Ag nanocomposite revealed the T1 relaxivities of 22.13 and 10.39 mM^-1 s^-1, which are larger than the commercial Gd-DOTA contrast agent of 3.08 mM^-1 s^-1. CT imaging NaGdF₄:Yb,Er-Ag and NaGdF₄:Yb,Er respectively showed the values of 53.29 HU L/g and 39.51 HU L/g, which are higher than 25.78 HU L/g of the CT contrast agent Iobitridol. The NaGdF₄:Yb,Er and NaGdF₄:Yb,Er-Ag respectively demonstrated a negative zeta potential of 54 mV and 55 mV, that could be useful for biological application. The in vitro cytotoxicity of the NaGdF₄:Yb,Er tested in HeLa and MCF-7 cancer cell line by MTT assay demonstrated a cell viability of 90 and 80 %, respectively. But, the cell viability of NaGdF₄:Yb,Er-Ag slightly decreased to 80 and 78%. The confocal microscopy imaging showed that the UCNPs are effectively up-taken inside the nucleolus of the cancer cells, and it might be useful for NIR laser-assisted phototherapy for cancer treatment. Graphical abstract.

808 nm excited energy migration upconversion nanoparticles driven by a Nd3+-Trinity system with color-tunability and superior luminescence properties

We have developed energy migration upconversion (EMU) nanoparticles (UCNPs) with optimal Nd³⁺-sensitization under excitation of an 808 nm laser to avoid over-heating effects caused by a 980 nm laser while maximizing the excitation efficiency. To realize efficient 808 nm sensitization, a "Nd³⁺-Trinity system" was implemented in the energy migration upconversion (EMU) cores (NaGdF₄:Yb,Tm@NaGdF₄:Yb,X, X = Eu/Tb), resulting in a core-multishell structure of EMU cores (accumulation layer@activation layer)@transition layer@harvest layer@activation layer. The spatially separated dopants and optimized Yb³⁺/Nd³⁺ content effectively prevented severe quenching events in the UCNPs and their Nd³⁺-sensitized EMU-based photoluminescence mechanism was studied under 808 nm excitation. These Nd³⁺-Trinity EMU system UCNPs presented enhanced upconversion luminescence and prolonged lifetime compared to the 980 nm excited UCNPs of the EMU system. It is proposed that 975 nm and 1056 nm NIR photons induced from the Nd³⁺ → Yb³⁺ energy transfer facilitate the Tm³⁺ accumulation process due to the matched energy gaps, which contributes to the extended lifetimes. More importantly, the synthesized UCNPs had a small average size of sub-15 nm and they not only exhibited color-tunability via Eu³⁺/Tb³⁺ activators, but also released a larger portion of Tm³⁺ red emission at 647 nm and had better penetration ability in water under 808 nm excitation, which are favorable for bioimaging applications.