The Synthesis of Poly(Vinyl Alcohol) Grafted with Fluorinated Protic Ionic Liquids Containing Sulfo Functional Groups

There has been an ongoing need to develop polymer materials with increased performance as proton exchange membranes (PEMs) for middle- and high-temperature fuel cells. Poly(vinyl alcohol) (PVA) is a highly hydrophilic and chemically stable polymer bearing hydroxyl groups, which can be further altered. Protic ionic liquids (proticILs) have been found to be an effective modifying polymer agent used as a proton carrier providing PEMs' desirable proton conductivity at high temperatures and under anhydrous conditions. In this study, the novel synthesis route of PVA grafted with fluorinated protic ionic liquids bearing sulfo groups (-SO₃H) was elaborated. The polymer functionalization with fluorinated proticILs was achieved by the following approaches: (i) the PVA acylation and subsequent reaction with fluorinated sultones and (ii) free-radical polymerization reaction of vinyl acetate derivatives modified with 1-methylimidazole and sultones. These modifications resulted in the PVA being chemically modified with ionic liquids of protic character. The successfully grafted PVA has been characterized using ¹H, ¹⁹F, and ¹³C-NMR and FTIR-ATR. The presented synthesis route is a novel approach to PVA functionalization with imidazole-based fluorinated ionic liquids with sulfo groups.

Photoresponse of CdSe-PVA nanocomposite films at low magnetic fields

A set of nanocomposite films of poly-vinyl alcohol (PVA) and 0.1-0.4 wt% CdSe nanoparticles (NPs) were developed by spin coating and their surface resistance (R) was measured as a function of light illumination intensity (I_L ) and applied magnetic field (H). The ferromagnetic CdSe NPs were synthesized by a facile chemical method which ensured in situ surface stabilization with a skinny layer of graphitic carbon. The CdSe NPs were uniformly dispersed in an aqueous solution of 2.0 wt% PVA and spin-coated on fluorine-doped tin oxide coated glass substrates. The photoresponse of the nanocomposite films at low H exhibits their efficacy for pertinent applications in optoelectronics.