Nanoreinforcements of Two-Dimensional Nanomaterials for Flame Retardant Polymeric Composites: An Overview

Polymer materials are ubiquitous in daily life. While polymers are often convenient and helpful, their properties often obscure the fire hazards they may pose. Therefore, it is of great significance in terms of safety to study the flame retardant properties of polymers while still maintaining their optimal performance. Current literature shows that although traditional flame retardants can satisfy the requirements of polymer flame retardancy, due to increases in product requirements in industry, including requirements for durability, mechanical properties, and environmental friendliness, it is imperative to develop a new generation of flame retardants. In recent years, the preparation of modified two-dimensional nanomaterials as flame retardants has attracted wide attention in the field. Due to their unique layered structures, two-dimensional nanomaterials can generally improve the mechanical properties of polymers via uniform dispersion, and they can form effective physical barriers in a matrix to improve the thermal stability of polymers. For polymer applications in specialized fields, different two-dimensional nanomaterials have potential conductivity, high thermal conductivity, catalytic activity, and antiultraviolet abilities, which can meet the flame retardant requirements of polymers and allow their use in specific applications. In this review, the current research status of two-dimensional nanomaterials as flame retardants is discussed, as well as a mechanism of how they can be applied for reducing the flammability of polymers.

Effects of α-ZrP on Crystallinity and Flame-Retardant Behaviors of PA6/MCA Composites

Novel flame-retardant Polyamide6/Melamine cyanurate-alpha-zirconium phosphate (PA6/MCA-α-ZrP) composites were prepared via the incorporation of the modified MCA (MCA-α-ZrP) into PA6. MCA-α-ZrP were synthesized through the self-assembly of α-ZrP, Melamine (ME), and cyanuric acid (CA) molecules. The results of differential scanning calorimetry (DSC) and X-ray diffraction (XRD) showed that the incorporation of enough α-ZrP (30 wt% MCA) caused the increased crystallinity of PA6 and tended to form γ phase. The thermogravimetric analysis (TGA) and heat distortion temperature (HDT) test illustrated that the α-ZrP could increase the residue and HDT values of PA6/MCA and showed a synergistic effect with MCA. The combination of MCA and α-ZrP caused the enhancement of vertical burning test (UL-94) rating. Cone calorimeter test (CCT) gave clear evidences that PA6/MCA-10α-ZrP composites with low heat release rate (HRR), low total heat release (THR), and high amounts of char residues after combustion compared with PA6/MCA and PA6/MCA-30α-ZrP. What is more, excellent mechanical properties were kept even though MCA and α-ZrP were dispersed not as good as expected.

Preparation of a flame retardant phosphorus-containing polyacrylate/α-zirconium phosphate nanocomposite through in situ emulsion polymerization

An acrylamide modified α-zirconium phosphate was prepared by intercalating acrylamide into the α-zirconium phosphate, and was utilized to synthesize a flame retardant phosphorus-containing nanocomposite via in situ emulsion polymerization.