Orives JR, Viali WR, Santagneli SH, Afonso CRM, Carvalho MH, de Oliveira AJA, Nalin M. Phosphate glasses via coacervation route containing CdFe
2O
4 nanoparticles: structural, optical and magnetic characterization.
Dalton Trans 2018;
47:5771-5779. [PMID:
29637950 DOI:
10.1039/c8dt00560e]
[Citation(s) in RCA: 9] [Impact Index Per Article: 1.5] [Reference Citation Analysis] [Abstract] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 11/21/2022]
Abstract
CdFe2O4 nanoparticles of around 3.9 nm were synthesized using the coprecipitation method and protected by a silica layer. The nanoparticles were mixed with a coacervate and transformed into phosphate glasses with 1, 4 and 8% in mass of nanoparticles by the melt-quenching method. TEM images confirm that the nanoparticles were successfully incorporated into the matrix without inducing crystallization. 31P NMR and Raman spectral analyses show that new P-O-Si bonds are formed in the glasses containing nanoparticles. The glass transition increases as a function of the nanoparticle content due to an increase in the connectivity of the phosphate glass chains. The UV-Vis spectra show bands at 415 and 520 nm assigned to Fe3+ ions and at 1025 nm, characteristic of Fe2+ ions, indicating that some of the nanoparticles dissolve during the melting process. The sample with 8% CdFe2O4 presents a paramagnetic behavior. The glasses obtained are transparent, non-hygroscopic and possess enormous thermal stability which is important for the production of optical devices.
Collapse