A new method for the preparation of MgAl layered double hydroxide-copper metal-organic frameworks structures: application to electrocatalytic oxidation of formaldehyde

In this research, we present a novel design protocol for the in-situ synthesis of MgAl layered double hydroxide-copper metal-organic frameworks (LDH-MOFs) nanocomposite based on the electrocoagulation process and chemical method. The overall goal in this project is the primary synthesis of para-phthalic acid (PTA) intercalated MgAl-LDH with Cu (II) ions to produce the paddle-wheel like Cu-(PTA) MOFs nanocrystals on/in the MgAl-LDH structure. The physicochemical properties of final product; Cu-(PTA) MOFs/MgAl-LDH, were characterized by the surface analysis and chemical identification methods (SEM, EDX, TEM, XRD, BET, FTIR, CHN, DLS, etc.). The Cu-(PTA) MOFs/MgAl-LDH nanocomposite was used to modification of the carbon paste electrode (CPE); Cu-(PTA) MOFs/MgAl-LDH/CPE. The electrochemical performance of Cu-(PTA) MOFs/MgAl-LDH/CPE was demonstrated through the utilization of electrochemical methods. The results show a stable redox behavior of the Cu (III)/Cu (II) at the surface of Cu-(PTA) MOFs/MgAl-LDH/CPE in alkaline medium (aqueous 0.1 M NaOH electrolyte). Then, the Cu-(PTA) MOFs/MgAl-LDH/CPE was used as a new electrocatalyst toward the oxidation of formaldehyde (FA). Electrochemical data show that the Cu-(PTA) MOFs/MgAl-LDH/CPE exhibits superior electrocatalytic performance on the oxidation of FA. Also the diffusion coefficient, exchange current density (J°) and mean value of catalytic rate constant (Kcat) were found to be 1.18 × 10-6 cm2 s-1, 23 mA cm-2 and 0.4537 × 104 cm3 mol-1 s-1, respectively. In general, it can be said the Cu-(PTA) MOFs/MgAl-LDHs is promising candidate for applications in direct formaldehyde fuel cells.

Effect of the Alloying Metal on the Corrosion Resistance of Pd-Rich Binary Alloys with Pt, Rh, and Ru in Sulfuric Acid

The paper presents the study of the corrosion resistance of electrodeposited Pd and its binary alloys with Pt, Rh, and Ru on a polycrystalline Au substrate. The corrosion resistance was tested in 0.5 M sulfuric acid at room temperature using potentiodynamic polarization and electrochemical impedance spectroscopy techniques. The morphology/composition and work function values were determined by scanning electron microscopy/energy-dispersive X-ray spectroscopy and scanning Kelvin probe, respectively. The obtained results revealed that the Pd electrode is the most resistant to corrosion, whereas the Pd-Ru electrode is the most susceptible to dissolution. It was found that the corrosion resistance of Pd-binary alloys decrease in the following order: Pd > Pd-Pt > Pd-Rh > Pd-Ru. This effect was assigned mainly to the difference in surface roughness factor of tested electrodes.