Synthesis and characterization of macrodiols and non-segmented poly(ester-urethanes) (PEUs) derived from α,ω-hydroxy telechelic poly(ε-caprolactone) (HOPCLOH): effect of initiator, degree of polymerization, and diisocyanate

Nine different macrodiols derived from α,ω-hydroxy telechelic poly(ε-caprolactone) (HOPCLOH) were prepared by ring-opening polymerization of ε-caprolactone (CL) using three linear aliphatic diols (HO-(CH2) n -OH, where n = 4, 8, and 12) as initiators and catalyzed by ammonium decamolybdate (NH4)8[Mo10O34]. The crystallization temperature (T c) and crystallinity (x i) were relatively high for HOPCLOH species with a long aliphatic chain [-(CH2)12-] in the oligoester. Also, HOPCLOH was the precursor of twenty-seven different poly(ester-urethanes) (PEUs) with various degrees of polymerization (DP) of HOPCLOH and three types of diisocyanates such as 1,6-hexamethylene diisocyanate (HDI), methylene diphenyl diisocyanate (MDI), and 4,4'-methylenebis (cyclohexyl isocyanate) (HMDI). HOPCLOH exhibited the melting temperature (T m) and crystallinity (x i) with a proportional dependency to the degree of polymerization (DP). PEUs showed significant thermal and mechanical properties, which had a direct correlation in terms of the type of DP and diisocyanate. PEUs derived from HDI versus MDI or HMDI exhibited an apparent effect where aliphatic diisocyanate (HDI) induced a significant x i with respect to aromatic and cyclic diisocyanate (MDI or HMDI). The profile of PEUs films according to mechanical properties is mainly a plastic behavior. The chemical nature and properties of HOPCLOH and PEUs were characterized by NMR, FT-IR, GPC, MALDI-TOF, DSC, and mechanical properties.

Analytical Methods for the Assessment of Curing Kinetics of Polyurethane Binders for High-Energy Composites

Polyurethane (PU) elastomers are largely utilized in the field of high-energy composites such as polymer-bonded explosives (PBXs) and solid rocket grains, due to their distinguished characteristics. Curing kinetics assessment is a crucial parameter to take into account to comprehend the processes to develop new high-energy composites. A comprehensive analytical characterization of curing kinetics is of fundamental importance to produce PU polymers with the most suitable and attractive properties. Moreover, to attain the optimal curing conditions, accurate analytical techniques, and strategies are essential to effectively evaluate their kinetic properties. This paper gives an overview on experimental tools, which can be used for a convenient analysis of kinetic behavior of these binders. The employment of each tool is showed and discussed by appropriate examples from the literature.

Fabrication of a Postfunctionalizable, Biorepellent, Electroactive Polyurethane Interface on a Gold Surface by Surface-Assisted Polymerization

This study describes surface-assisted (SurfAst) urethane polymerization, providing a modular/postfunctionalizable, biorepellent, electroactive ∼10 to 100 nm-thick polyurethane (PU) interface on a gold surface. SurfAst is a functionalization methodology based on sequential incubation steps of alkane diisocyanates and alkanediol monomers. The gold surface is functionalized by alkane diisocyanates in the first incubation step, and our theoretical calculations reveal that while the isocyanate group atoms (N, C, and O) at one end of the molecule exhibits strong interactions (∼900 meV) with surface atoms, the other end group remains unreacted. After the first incubation step, sequential alkanediol and alkane diisocyanate incubations provide formation of the PU interface. The extensive analysis of the PU interface has been conducted via X-ray photoelectron spectroscopy, and the chemical mapping verifies that the interface is made of PU moieties. The topographical analysis of the surface conducted by the atomic force microscopy shows that the PU interface consists of mostly a nanoporous texture with 150 nm total roughness. The adherence force mapping of the PU interface reveals that the nanoporous matrix exhibits an adhesion force of about 14 nN. The electrostatic force microscopy characterizing long-range electrostatic interactions (40 nm) shows that the PU interface has been attracted by positively charged species as compared to negative objects. Finally, it is demonstrated that the PU interface is readily postfunctionalizable by polyethylene glycol (PEG 1000), serving as a biorepellent interface and preserving electroactivity. We foresee that SurfAst polymerization will have potential for the facile fabrication of a postfunctionalizable and modular biointerface which might be utilized for biosensing and bioelectronic applications.