Synthesis of 5-Fluorouracil Polymer Conjugate and 19F NMR Analysis of Drug Release for MRI Monitoring

To monitor the release of fluorinated drugs from polymeric carriers, a novel 19F MRI enzyme-responsive contrast agent was developed and tested. This contrast agent was prepared by conjugation of 5-fluorouracil (5-FU) to hyperbranched poly(N,N-dimethylacrylamide) (HB-PDMA) via an enzyme-degradable peptide linker. Due to the different molecular sizes, the release of 5-FU from the 5-FU polymer conjugate resulted in a sufficiently substantial difference in spin-spin T2 19F NMR/MRI relaxation time that enabled differentiating between attached and released drug states. The 5-FU polymer conjugate exhibited a broad signal and short T2 relaxation time under 19F NMR analysis. Incubation with the enzyme induced the release of 5-FU, accompanied by an extension of T2 relaxation times and an enhancement in the 19F MRI signal. This approach is promising for application in the convenient monitoring of 5-FU drug release and can be used to monitor the release of other fluorinated drugs.

Chain-Extendable Crosslinked Hydrogels Using Branching RAFT Modification

Functional crosslinked hydrogels were prepared from 2-hydroxyethyl methacrylate (HEMA) and acrylic acid (AA). The acid monomer was incorporated both via copolymerization and chain extension of a branching, reversible addition–fragmentation chain-transfer agent incorporated into the crosslinked polymer gel. The hydrogels were intolerant to high levels of acidic copolymerization as the acrylic acid weakened the ethylene glycol dimethacrylate (EGDMA) crosslinked network. Hydrogels made from HEMA, EGDMA and a branching RAFT agent provide the network with loose-chain end functionality that can be retained for subsequent chain extension. Traditional methods of surface functionalization have the downside of potentially creating a high volume of homopolymerization in the solution. Branching RAFT comonomers act as versatile anchor sites by which additional polymerization chain extension reactions can be carried out. Acrylic acid grafted onto HEMA–EGDMA hydrogels showed higher mechanical strength than the equivalent statistical copolymer networks and was shown to have functionality as an electrostatic binder of cationic flocculants.

Effect of poly(acrylic acid) architecture on setting and mechanical properties of glass ionomer cements

OBJECTIVE

This work focuses on the influence of poly(acrylic acid) (PAA) architecture (linear or branched) on setting behavior and compressive strength of glass ionomer cements (GICs).

METHODS

Branched and linear poly(acrylic acid)s were synthesized according to the Strathclyde methodology or by free radical polymerization. They were characterized by ¹H-NMR spectroscopy and size exclusion chromatography to determine their molecular weight and size distribution. GIC setting was characterized by oscillating rheometry and time-dependent FTIR spectroscopy. In addition, compressive strength was tested on cylindrical samples (6 × 4 mm; n = 8/cement composition) after storage in deionized water at 37 °C for one day.

RESULTS

We used two different routes to prepare PAA. One direct route in order to provide straightforward access to branched PAA and a two-step approach in order to get more control about the PAA molecular weight using tert-butyl acrylate (tBA) for polymerization with subsequent deprotection. Using the second approach we obtained several linear PAA of which a mixture was used in order to mimic the molecular weight and size distribution of branched PAA. This allowed the direct comparison of properties relying only on the polymer architecture. Comparing linear PAA to branched samples in general led to faster setting but at the same time decreased the compressive strength. Increasing molecular weight of branched PAA resulted in even faster GIC setting while increasing compressive strength and this correlates well with the trends reported for linear PAA in literature. Mixing of branched and linear PAA, however, turned out to be an effective way of tailoring GIC properties.

SIGNIFICANCE

our results suggest that both molecular weight and dispersity need to be considered when choosing suitable PAA architecture for obtaining specific GIC properties.