Flake-like InVO4 modified TiO2 nanofibers with longer carrier lifetimes for visible-light photocatalysts

InVO4 nanosheets decorated with ZnWO4 nanorods: A novel composite and its enhanced photocatalytic performance under solar light

InVO₄ is the most attractive inorganic new-generation material for advanced scientific research, especially in the fields of energy and environmental science. In theory, this stable, non-toxic, energy-efficient metal vanadate semiconductor is expected to exhibit significant catalytic activity owing to its narrow bandgap energy. However, this has not been achieved in practice because of its inherent defects in terms of the separation and migration of charge carriers. In fact, the exploration of this material is still in its infancy, and more research is needed to improve its efficiency and speed up its commercialization. Band gap engineering using heterojunction formation offers better results than other methods, such as morphological variations and doping efforts. In this context, the present study offers a significant solution substantiated by experimental results. This includes the successful synthesis of a novel nanocomposite of InVO₄ nanosheets decorated with ZnWO₄ nanorods with a unique improved light absorption ability. Three composites with 26.48-33.85 nm crystal sizes and 11.74-19.98 m²/g surface area were prepared with tailor-made bandgap energies in the range of 2.52-2.97 eV. Furthermore, they produced high photoexcitation currents with low EIS resistance with respect to their constituents. The as-prepared InVO₄-based novel catalyst almost completely (98.33%) decomposed tetracycline (TC) antibiotic in just 90 min, proving its high efficacy. The enhanced performance of the novel catalyst is 7.6 times that of InVO₄ and 10 times that of ZnWO₄. Moreover, the catalyst intake was significantly small (15 mg/100 mL TC solution).

Effect of Cu doping on the photocatalytic activity of InVO4 for hazardous dye photodegradation under LED light and its mechanism

Cu doped InVO₄ (xCu-InVO₄ (x = 0.06-0.15 wt %) was synthesized by a facile one-pot hydrothermal method for the removal of methylene blue (MB) under LED light irradiation. The X-ray photoelectron spectroscopy (XPS) analysis indicated the coexistence of V⁵⁺ and V⁴⁺ species due to the O-deficient nature of the xCu-InVO₄. The synthesized photocatalysts displayed a morphology of spherical and square shaped particles (20-40 nm) and micro-sized rectangle rods with a length range of 100-200 μm. The xCu-InVO₄ exhibited superior adsorption and photodegradation efficiency compared to pristine InVO₄ and TiO₂ due to the presence of O₂ vacancies, V⁴⁺/V⁵⁺ species, and Cu dopant. The optimum reaction conditions were found to be 5 mg L^-1 (MB concentration), pH 6, and 100 mg of photocatalyst mass with a removal efficiency and mineralization degree of 100% and 96.67%, respectively. The main active species responsible for the degradation of MB were ^•OH radicals and h⁺. Reusability studies indicated that the 0.13Cu-InVO₄ was deactivated after a single cycle of photocatalytic reaction due to significant leaching of V⁴⁺ and Cu²⁺ species.

Electrospun Mesoporous InVO4 /TiO2 Nanobelts with Enhanced Photocatalytic Properties

In the present paper, mesoporous InVO₄ /TiO₂ nanobelts with diameter about 400 nm have been synthesized by elaborately designed electrospinning process. The microstructures of InVO₄ /TiO₂ nanobelts are characterized in detail, and their photoelectrocatalytic properties are comprehensively investigated by the photocatalytic degradation tests with tetracycline (TTC) and rhodamine B (RhB) waste water. Furthermore, the energy bandgap and density of states of orthorhombic InVO₄ and anatase TiO₂ are modeled and analyzed by density functional theory. Compared with single InVO₄ nanobelts and TiO₂ nanofibers, mesoporous InVO₄ /TiO₂ nanobelts possess the extraordinary photocatalytic efficiencies and exceptional cycle performances, which may be ascribed to the successful construction of heterostructures between InVO₄ and TiO₂ and unique one-dimensional belt structures.