State of the Art and Perspectives of Hierarchical Zeolites: Practical Overview of Synthesis Methods and Use in Catalysis

Microporous zeolites have proven to be of great importance in many chemical processes. Yet, they often suffer from diffusion limitations causing inefficient use of the available catalytically active sites. To address this problem, hierarchical zeolites have been developed, which extensively improve the catalytic performance. There is a multitude of recent literature describing synthesis of and catalysis with these hierarchical zeolites. This review attempts to organize and overview this literature (of the last 5 years), with emphasis on the most important advances with regard to synthesis and application of such zeolites. Special attention is paid to the most common and important 10- and 12-membered ring zeolites (MTT, TON, FER, MFI, MOR, FAU, and *BEA). In contrast to previous reviews, the research per zeolite topology is brought together and discussed here. This allows the reader to instantly find the best synthesis method in accordance to the desired zeolite properties. A summarizing graph is made available to enable the reader to select suitable synthesis procedures based on zeolite acidity and mesoporosity, the two most important tunable properties.

Combining Soft- and Hard-Templating Approaches in MWW-Type Zeolites

A combination of hard-templating (HT) and soft-templating (ST) approaches was studied to obtain MWW-type materials with intermediate physicochemical properties. The HT methodology involved the introduction of carbon particles as hard templates during gel synthesis to obtain a layered zeolitic precursor (LZP) with particles possessing a microspherical morphology. The LZP obtained was treated with surfactants as soft templates to expand the layers of the LZP, followed by a pillaring procedure. The materials were characterized by X-ray diffraction, transmission and scanning electron microscopy, elemental analysis and N₂ adsorption. The results demonstrate that the obtained material possesses intermediate properties from both approaches, with interparticle mesopores/macropores and pore sizes between 18 and 46 Å. However, the ST procedure causes a partial disruption of some microspheres, forming small crystallite aggregates, and results in a decrease in the number of interparticle mesopores/macropores previously formed by the HT method. All synthesized solids presented catalytic activity, which was evaluated by the cracking of low-density polyethylene (LDPE) as a probe reaction.