Fe-Pd nanoflakes decorated on leached graphite disks for both methanol and formic acid electrooxidation with excellent electrocatalytic performance

This paper introduces a unique and simple method for fabricating of inexpensive electrocatalysts for use in direct methanol fuel cells. The leached Fe1-Pd1 NFs/graphite (leached Fe1-Pd1/graphite) disk electrode was successfully obtained via uniform dispersion of Zn powder into the matrix of commercial graphite powder (98%), pressing under optimized pressure followed by the treatment in H2SO4 solution containing Fe+2 and Pd+2 cations, leading to the partial leaching out of Zn from graphite matrix, as well as partial electroless substitution of Fe-Pd nanoflakes with Zn metal. Based on the morphology studies, binary Fe-Pd nanoflakes with a large surface area uniformly dispersed on the leached graphite disk. The leached Fe-Pd/G disk showed the exceptional electrocatalytic activity toward methanol and formic acid oxidation without electrocatalyst poisoning being observed, in contrast to the leached Pd/graphite and leached Fe/graphite disks. This is due to the high surface area, and synergistic effect of Pd and Fe. The findings of this work may be used for the mass manufacture of graphite-based disks for commercial fuel cell applications using available graphite powders. The linear range of washed Fe1-Pd1/G electrocatalyst for measuring methanol was about 0.1-1.3 M, and its detection limit was calculated at about 0.03 M. Furthermore, the linear range of the nanocatalyst for measuring formic acid was about 0.02-0.1 M, and its detection limit was calculated at about 0.006 M.

Molybdenum Carbide/Ni Nanoparticles Embedded into Carbon Nanofibers as an Effective Non-Precious Catalyst for Green Hydrogen Production from Methanol Electrooxidation

Molybdenum carbide co-catalyst and carbon nanofiber matrix are suggested to improve the nickel activity toward methanol electrooxidation process. The proposed electrocatalyst has been synthesized by calcination electrospun nanofiber mats composed of molybdenum chloride, nickel acetate, and poly (vinyl alcohol) under vacuum at elevated temperatures. The fabricated catalyst has been characterized using XRD, SEM, and TEM analysis. The electrochemical measurements demonstrated that the fabricated composite acquired specific activity for methanol electrooxidation when molybdenum content and calcination temperature were tuned. In terms of the current density, the highest performance is attributed to the nanofibers obtained from electrospun solution having 5% molybdenum precursor compared to nickel acetate as a current density of 107 mA/cm² was generated. The process operating parameters have been optimized and expressed mathematically using the Taguchi robust design method. Experimental design has been employed in investigating the key operating parameters of methanol electrooxidation reaction to obtain the highest oxidation current density peak. The main effective operating parameters of the methanol oxidation reaction are Mo content in the electrocatalyst, methanol concentration, and reaction temperature. Employing Taguchi's robust design helped to capture the optimum conditions yielding the maximum current density. The calculations revealed that the optimum parameters are as follows: Mo content, 5 wt.%; methanol concentration, 2.65 M; and reaction temperature, 50 °C. A mathematical model has been statistically derived to describe the experimental data adequately with an R² value of 0. 979. The optimization process indicated that the maximum current density can be identified statistically at 5% Mo, 2.0 M methanol concentration, and 45 °C operating temperature.

Significant promotion effects of Ag oxide towards Pd catalysis for ethanol and methanol oxidation reactions

Ag oxides play a crucial role in promoting the catalysis of Pd both for ethanol and methanol oxidation reactions.