Development of Biodegradable Polyesters: Study of Variations in Their Morphological and Thermal Properties through Changes in Composition of Alkyl-Substituted (ε-DL) and Non-Substituted (ε-CL, EB, L-LA) Monomers

Three series of polyesters based on monomer combinations of ε-caprolactone (ε-CL), ethylene brassylate (EB), and l-Lactide (LLA) with the alkyl substituted lactone ε-decalactone (ε-DL) were synthesized at different molar ratios. Copolymers were obtained via ring opening polymerization (ROP) employing TBD (1,5,7-triazabicyclo-[4.4.0]-dec-5-ene), an organic catalyst which can be handled under normal conditions, avoiding the use of glove box equipment. The molar monomer composition of resulting copolymers differed from theoretical values due to lower ε-DL reactivity; their M_n and M_w values were up to 14 kDa and 22.8 kDa, respectively, and distributions were (Ɖ) ≤ 2.57. The thermal stability of these materials suffered due to variations in their ε-DL molar content. Thermal transitions such as melting (T_m) and crystallization (T_c) showed a decreasing tendency as ε-DL molar content increased, while glass transition (T_g) exhibited minor changes. It is worth mentioning that changes in monomer composition in these polyesters have a strong impact on their thermal performance, as well as in their crystallization degree. Consequently, variations in their chemical structure may have an effect on hydrolyic degradation rates. It should be noted that, in future research, some of these copolymers will be exposed to hydrolytic degradation experiments, including characterizations of their mechanical properties, to determine their adequacy in potential use in the development of soft medical devices.

Green and sustainable synthesis of poly(δ-valerolactone) with a TBD catalyzed ring-opening polymerization reaction

A green and sustainable method is proposed for the TBD catalyzed ring-opening polymerization of δ-valerolactone.

High pressure as a novel tool for the cationic ROP of γ-butyrolactone

In this study, we report the acid-catalyzed and high pressure assisted ring-opening polymerization (ROP) of γ-butyrolactone (GBL). The use of a dually-catalyzed approach combining an external physical factor and internal catalyst (trifluoromethanesulfonic acid (TfOH) or p-toluenesulfonic acid (PTSA)) enforced ROP of GBL, which is considered as hardly polymerizable monomer still remaining a challenge for the modern polymer chemistry. The experiments performed at various thermodynamic conditions (T = 278–323 K and p = 700–1500 MPa) clearly showed that the high pressure supported polymerization process led to obtaining well-defined macromolecules of better parameters (M_n = 2200–9700 g mol⁻¹; Đ = 1.05–1.46) than those previously reported. Furthermore, the parabolic-like dependence of both the molecular weight (M_W) and the yield of obtained polymers on variation in temperature and pressure at either isobaric or isothermal conditions was also noticed, allowing the determination of optimal conditions for the polymerization process. However, most importantly, this strategy allowed to significantly reduce the reaction time (just 3 h at room temperature) and increase the yield of obtained polymers (up to 0.62 g_PGBL/g_GBL). Moreover, despite using a strongly acidic catalyst, synthesized polymers remained non-toxic and biocompatible, as proven by the cytotoxicity test we performed in further analysis. Additional investigation (including MALDI-TOF measurements) showed that the catalyst selection affected not only M_W and yield but also the linear/cyclic form content in obtained macromolecules. These findings show the way to tune the properties of PGBL and obtain polymer suitable for application in the biomedical industry.

Well-defined poly(γ-butyrolactone) was synthesized with great efficiency via high pressure assisted cationic ROP of hardly polimerizable γ-butyrolactone.

Iodine-mediated photo-controlled atom transfer radical polymerization (photo-ATRP) and block polymerization combined with ring-opening polymerization (ROP) via a superbase

Most organocatalysts for photo-controlled atom transfer radical polymerization (photo-ATRP) are metal complexes or synthetically elaborate organic dyes, which are toxic and expensive.