The Influence of the Comonomer Ratio and Reaction Temperature on the Mechanical, Thermal, and Morphological Properties of Lignin Oil-Sulfur Composites

Although lignin is a plentiful biomass resource, it continually exists as an underutilized component of biomass material. Elemental sulfur is another abundant yet underutilized commodity produced as a by-product resulting from the refining of fossil fuels. The current study presents a strategy for preparing five durable composites via a simple one-pot synthesis involving the reaction of lignin oil and elemental sulfur. These lignin oil-sulfur composites LOSx@T (where x = wt. % sulfur, ranging from 80 to 90, and T represents the reaction temperature in °C) were prepared via the reaction of elemental sulfur and lignin oil (LO) with elemental sulfur. The resulting composites could be remelted and reshaped several times without the loss of mechanical strength. Mechanical, thermal, and morphological studies showed that LOSx@T possesses properties competitive with some mechanical properties of commercial building materials, exhibiting favorable compressive strengths (22.1-35.9 MPa) and flexural strengths (5.7-6.5 MPa) exceeding the values required for many construction applications of ordinary Portland cement (OPC) and brick formulations. While varying the amount of organic material did not result in a notable difference in mechanical strength, increasing the reaction temperature from 230 to 300 °C resulted in a significant increase in compressive strength. The results reported herein reveal potential applications of both lignin and waste sulfur during the ongoing effort toward developing recyclable and sustainable building materials.

Durable composites by vulcanization of oleyl-esterified lignin

Productive utilization of lignocellulosic biomass is critical to the continued advancement of human civilization. Whereas the cellulose component can be efficiently upconverted to automotive fuel-grade ethanol, the lack of upconversion methods for the lignin component constitutes one of the grand challenges facing science. Lignin is an attractive feedstock for structural applications, in which its highly-crosslinked architecture can endow composite structures with high strengths. Prior work suggests that high-strength composites can be prepared by the reaction of olefin-modified lignin with sulfur. Those studies were limited to ≤5 wt% lignin, due to phase-separation of hydrophilic lignin from hydrophobic sulfur matrices. Herein we report a protocol to increase lignin hydrophobicity and thus its incorporation into sulfur-rich materials. This improvement is affected by esterifying lignin with oleic acid prior to its reaction with sulfur. This approach allowed preparation of esterified lignin-sulfur (ELS) composites comprising up to 20 wt% lignin. Two reaction temperatures were employed such that the reaction of ELS with sulfur at 180 °C would only produce S-C bonds at olefinic sites, whereas the reaction at 230 °C would produce C-S bonds at both olefin and aryl sites. Mechanistic analyses and microstructural characterization elucidated two ELS composites having compressive strength values (>20 MPa), exceeding the values observed with ordinary Portland cements. Consequently, this new method represents a way to improve lignin utilization to produce durable composites that represent sustainable alternatives to Portland cements.

Influence of Component Ratio on Thermal and Mechanical Properties of Terpenoid-Sulfur Composites

Terpenoids are potentially sustainable replacements for petrochemical olefins. Sulfur is a waste product produced in large quantities from fossil fuel refining. Several composites with attractive properties have recently been made from terpenoids and sulfur. This report details the extent to which the ratio of sulfur to terpenoid and the terpenoid olefin content influences the thermal and mechanical properties of such terpenoid-sulfur composites. The terpenoids selected were diunsaturated geraniol and triunsaturated farnesol that, upon their inverse vulcanization with elemental sulfur, yield composites GerSx and FarSx, respectively (x = wt % sulfur). The wt % sulfur in the monomer feed was varied from 30–95 for this study, providing twelve materials. Mechanical analysis of these materials was undertaken by compressive and tensile strength techniques. Differential scanning calorimetric analysis revealed both polymeric and orthorhombic sulfur present in the materials with glass transition temperatures (Tg) of −37 °C to −13 °C and melt temperatures (Tm) of 119 to 104 °C. The crystallinity of composites decreases as the weight fraction of sulfur decreases and composites having the highest olefin content exhibit no detectable crystalline microstructures. The compressive strength of the materials showed increasing strength for higher olefin-content materials for both GerSx (with compressive strength of up to 32 MPa) and FarSx (with compressive strength of up to 43 MPa). The improved strength with increasing olefin content levels off at around 80–85% of terpenoid, after which point both tensile and compressive strength diminish.

Lithium-Sulfur Batteries: Advances and Trends

A review with 132 references. Societal and regulatory pressures are pushing industry towards more sustainable energy sources, such as solar and wind power, while the growing popularity of portable cordless electronic devices continues. These trends necessitate the ability to store large amounts of power efficiently in rechargeable batteries that should also be affordable and long-lasting. Lithium-sulfur (Li-S) batteries have recently gained renewed interest for their potential low cost and high energy density, potentially over 2600 Wh kg−1. The current review will detail the most recent advances in early 2020. The focus will be on reports published since the last review on Li-S batteries. This review is meant to be helpful for beginners as well as useful for those doing research in the field, and will delineate some of the cutting-edge adaptations of many avenues that are being pursued to improve the performance and safety of Li-S batteries.