Highly efficient blue-emitting phosphor of Sr[B8O11(OH)4]:Eu2+ prepared by a self-reduction method

Enhanced Fluorescence Characteristics of SrAl2O4: Eu2+, Dy3+ Phosphor by Co-Doping Gd3+ and Anti-Counterfeiting Application

A series of long-afterglow luminescent materials (SrAl₂O₄: Eu²⁺ (SAOE), SrAl₂O₄: Eu²⁺, Dy³⁺ (SAOED) and SrAl₂O₄: Eu²⁺, Dy³⁺, Gd³⁺ (SAOEDG)) was synthesized via the combustion method. Temperature and concentration control experiments were conducted on these materials to determine the optimal reaction temperature and ion doping concentration for each sample. The crystal structure and luminescent properties were analyzed via X-ray diffraction (XRD), photoluminescence (PL), and afterglow attenuation curves. The outcomes demonstrate that the kind of crystal structure and the location of the emission peak were unaffected by the addition of ions. The addition of Eu²⁺ to the matrix's lattice caused a broad green emission with a central wavelength of 508 nm, which was attributed to the characteristic 4f⁶5d¹ to 4f⁷ electronic dipole, which allowed the transition of Eu²⁺ ions. While acting as sensitizers, Dy³⁺ and Gd³⁺ could produce holes to create a trap energy level, which served as an electron trap center to catch some of the electrons produced by the excitation of Eu²⁺ but did not itself emit light. After excitation ceased, this allowed them to gently transition to the ground state to produce long-afterglow luminescence. It was observed that with the addition of sensitizer ions, the luminous intensity of the sample increased, and the afterglow duration lengthened. The elemental structure and valence states of the doped ions were determined with an X-ray photoelectron spectrometer (XPS). Scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDX) were used to characterize the samples. The results show that the sample was synthesized successfully, and the type and content of ions in the fluorescent powder could be determined. The fluorescence lifetime, quantum yield, bandgap value, afterglow decay time, and coordinate position in the coherent infrared energy (CIE) diagram of the three best sample groups were then analyzed and compared. Combining the prepared phosphor with ink provides a new idea and method for the field of anti-counterfeiting through screen printing.

Ca[B8 O11 (OH)4 ] : Eu2+ - A Highly Efficient Deep Blue-Emitting Phosphor Prepared by Low-Temperature Self-reduction

Highly efficient inorganic phosphors are crucial for solid-state lighting. In this paper, a new method of low-temperature self-reduction was used for preparing a highly efficient deep blue-emitting phosphor of Ca[B₈ O₁₁ (OH)₄ ] : Eu²⁺ (CBH : Eu²⁺ ). The crystal structure, morphology, chemical state, and photoluminescence (PL) properties of the CBH : Eu²⁺ phosphor have been investigated. By using the screened hybrid function (HSE06), the band gap (E_g ) of CBH was calculated to be 7.48 eV, which is a necessary condition for achieving high quantum yield phosphors. The experiment results show that almost all the added raw materials of Eu³⁺ can be reduced to Eu²⁺ in CBH crystal under a non-reducing atmosphere. The CBH : Eu²⁺ phosphor shows a broad excitation spectrum centered at 277 and 327 nm in the range of 220 to 400 nm, and a narrow-band emission spectrum centered at 428 nm in the range of 400 to 500 nm, with a full width at half maximum (fwhm) of 42.35 nm. Under UV radiation, the CBH : 2 %Eu²⁺ exhibits high photoluminescence quantum yield (PLQY=95.0 %), high external quantum efficiency (EQE=31.1 %), and ultra-high color purity (97.6 %). The PL intensity of CBH : 2 %Eu²⁺ remains 62.6 % of the initial intensity at 150 °C. Finally, the white light-emitting diodes (WLED) fabricated by CBH : 2 %Eu²⁺ , excited by a 365 nm chip, presents outstanding performances with a luminous efficacy (LE) of 13.9 lm/W, a color rendering index (CRI) of 89.4, and a correlated color temperature (CCT) of 5825 K. The above results show that CBH : Eu²⁺ can be used as a promising blue phosphor for WLED. This new method of low-temperature self-reduction can be applied to design and prepare other new types of highly efficient phosphors.