Impact of Compression on the Textural and Structural Properties of CPO-27(Ni)

The employment of metal-organic frameworks in powder form is undesirable from an industrial perspective due to process and safety issues. This work is devoted to evaluating the impact of compression on the textural and structural properties of CPO-27(Ni). For this purpose, CPO-27(Ni) was synthesized under hydrosolvothermal conditions and characterized. Then, the resulting powder was compressed into binderless pellets using variable compression forces ranging from 5-90 kN (37-678 MPa) and characterized by means of nitrogen adsorption/desorption, thermogravimetric analysis and powder X-ray diffraction to evaluate textural, thermal and structural changes. Both textural and structural properties decreased with increasing compression force. Thermal stability was impacted in pellets compressed at forces over 70 kN. CPO-27(Ni) pelletized at 5, 8 and 10 kN, and retained more than 94% of its initial textural properties, while a loss of about one-third of the textural property was observed for the two most compressed samples (70 and 90 kN) compared to the starting powder.

Impedance-Based Detection of NO2 Using Ni-MOF-74: Influence of Competitive Gas Adsorption

Chemically robust, low-power sensors are needed for the direct electrical detection of toxic gases. Metal-organic frameworks (MOFs) offer exceptional chemical and structural tunability to meet this challenge, though further understanding is needed regarding how coadsorbed gases influence or interfere with the electrical response. To probe the influence of competitive gases on trace NO2 detection in a simulated flue gas stream, a combined structure-property study integrating synchrotron powder diffraction and pair distribution function analyses was undertaken, to elucidate how structural changes associated with gas binding inside Ni-MOF-74 pores correlate with the electrical response from Ni-MOF-74-based sensors. Data were evaluated for 16 gas combinations of N2, NO2, SO2, CO2, and H2O at 50 °C. Fourier difference maps from a rigid-body Rietveld analysis showed that additional electron density localized around the Ni-MOF-74 lattice correlated with large decreases in Ni-MOF-74 film resistance of up to a factor of 6 × 103, observed only when NO2 was present. These changes in resistance were significantly amplified by the presence of competing gases, except for CO2. Without NO2, H2O rapidly (<120 s) produced small (1-3×) decreases in resistance, though this effect could be differentiated from the slower adsorption of NO2 by the evaluation of the MOF's capacitance. Furthermore, samples exposed to H2O displayed a significant shift in lattice parameters toward a larger lattice and more diffuse charge density in the MOF pore. Evaluating the Ni-MOF-74 impedance in real time, NO2 adsorption was associated with two electrically distinct processes, the faster of which was inhibited by competitive adsorption of CO2. Together, this work points to the unique interaction of NO2 and other specific gases (e.g., H2O, SO2) with the MOF's surface, leading to orders of magnitude decrease in MOF resistance and enhanced NO2 detection. Understanding and leveraging these coadsorbed gases will further improve the gas detection properties of MOF materials.

Chiral Lanthanum Metal-Organic Framework with Gated CO2 Sorption and Concerted Framework Flexibility

A metal–organic framework (MOF) CTH-17 based on lanthanum(III) and the conformationally chiral linker 1,2,3,4,5,6-hexakis(4-carboxyphenyl)benzene, cpb^6–: [La₂(cpb)]·1.5dmf was prepared by the solvothermal method in dimethylformamide (dmf) and characterized by variable-temperature X-ray powder diffraction (VTPXRD), variable-temperature X-ray single-crystal diffraction (SCXRD), and thermogravimetric analysis (TGA). CTH-17 is a rod-MOF with new topology och. It has high-temperature stability with Sohncke space groups P6₁22/P6₅22 at 90 K and P622 at 300 and 500 K, all phases characterized with SCXRD and at 293 K also with three-dimensional (3D) electron diffraction. VTPXRD indicates a third phase appearing after 620 K and stable up to 770 K. Gas sorption isotherms with N₂ indicate a modest surface area of 231 m² g^–1 for CTH-17, roughly in agreement with the crystal structure. Carbon dioxide sorption reveals a gate-opening effect of CTH-17 where the structure opens up when the loading of CO₂ reaches approximately ∼0.45 mmol g^–1 or 1 molecule per unit cell. Based on the SCXRD data, this is interpreted as flexibility based on the concerted movements of the propeller-like hexatopic cpb linkers, the movement intramolecularly transmitted by the π–π stacking of the cpb linkers and helped by the fluidity of the LaO₆ coordination sphere. This was corroborated by density functional theory (DFT) calculations yielding the chiral phase (P622) as the energy minimum and a completely racemic phase (P6/mmm), with symmetric cpb linkers representing a saddle point in a racemization process.

Elucidating pore chemistry within metal–organic frameworks via single crystal X-ray diffraction; from fundamental understanding to application

The application of metal–organic frameworks (MOFs) to diverse chemical sectors is aided by their crystallinity, which permits the use of X-ray crystallography to characterise their pore chemistry and provides invaluable insight into their properties.