Peculiarities of high-pressure hydrogen adsorption on Pt catalyzed Cu-BTC metal-organic framework

Enhancement of Hydrogen Adsorption on Spray-Synthesized HKUST-1 via Lithium Doping and Defect Creation

We prepared HKUST-1 (Cu3BTC2; BTC3- = 1,3,5-benzenetricarboxylate) using a spray synthesis method with Li doping and defect created via partial replacement of H3BTC with isophthalic acid (IP) to enhance the H2 adsorption capacity. Li-doping was performed by incorporating LiNO3 in HKUST-1 via spray synthesis and subsequent thermal treatment for decomposing NO3-, which enhances H2 uptake at 77 K and 1 bar per unit mass and per unit area from 2.37 wt% and 4.16 molecules/nm2 for undoped HKUST-1 to 2.47 wt% and 4.33 molecules/nm2, respectively. Defect creation via the replacement of the BTC3- linker with the IP2- linker slightly in HKUST-1 skeleton did not affect H2 uptake. Both Li-doping and defect creation significantly enhanced H2 uptake to 3.03 wt%, which was caused by the coordination of Li ions with free carboxylic groups of the created defects via IP replacement.

Pd-doped HKUST-1 MOFs for enhanced hydrogen storage: effect of hydrogen spillover

Extensive research has been devoted to developing metal nanoparticle (NP) doped porous materials with large hydrogen storage capacity and high hydrogen release pressure at ambient temperature. The ultra-sound assisted double-solvent approach (DSA) was applied for sample synthesis. In this study, tiny Pd NPs are confined into the pore space of HKUST-1, affording Pd@HKUST-1-DS with minimizing the aggregation of Pd NPs and subsequently the formation of Pd NPs on the external surface of HKUST-1. The experimental data reveal that the obtained Pd NP doped Pd@HKUST-1-DS possessed an outstanding hydrogen storage capacity of 3.68 wt% (and 1.63 wt%) at 77 K and 0.2 MPa H₂ (and 298 K and 18 MPa H₂), in comparison with pristine HKUST-1 and impregnated Pd/HKUST-1-IM. It is found that the storage capacity variation is not only ascribed to the different textural properties of materials but is also illustrated by the hydrogen spillover induced by different electron transport from Pd to the pores of MOFs (Pd@HKUST-1-DS > Pd/HKUST-1-IM), based on X-ray photoelectron spectroscopy and temperature desorption spectra. Pd@HKUST-1-DS, featuring high specific surface area, uniform Pd NP dispersion and strong interaction of Pd with hydrogen in the confined pore spaces of the support, displays the high hydrogen storage capacity. This work highlights the influence of spillover caused by Pd electron transport on the hydrogen storage capacity of metal NPs/MOFs, which is governed by both physical and chemical adsorption.