Shou T, Wu Y, Yin D, Hu S, Wu S, Zhao X, Zhang L. In-situ self-crosslinking strategy for super-tough polylactic acid/ bio-based polyurethane blends. Int J Biol Macromol 2024; 261:129757. [PMID: 38281538 DOI: 10.1016/j.ijbiomac.2024.129757] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 09/17/2023] [Revised: 01/11/2024] [Accepted: 01/24/2024] [Indexed: 01/30/2024]
Abstract
As a bio-based degradable plastic, polylactic acid (PLA) is highly commercialized, but its inherent brittleness limits its widespread use. In-situ polymerization techniques are effective in improving the toughness of PLA. However, the enhancement of the toughening effect in polyurethanes (PUs) through in-situ self-crosslinking still requires improvement and heavily relies on petroleum-derived feedstocks in certain approaches. In this paper, 1,3-polypropanediol (PO3G) of bio-based origin rather than conventional polyols like polyethylene glycol (PEG) and poly propylene glycol (PPG) was used. PLA/PO3G-PU blends were prepared via an in-situ self-crosslinking strategy. With a notch impact and tensile strength of 55.95 kJ/m2 and 47.77 MPa (a retention rate of 68.9 % compared with pure PLA), respectively, PLA/PO3G-PU blends achieved a better balance between stiffness and toughness. This work provides a new option for PLA to achieve a stiffness-toughness balance and get rid of dependence on petrochemical resources.
Collapse
Affiliation(s)
- Tao Shou
- State Key Laboratory of Organic-Inorganic Composites, Beijing University of Chemical Technology, Beijing, 100029, China
| | - Yaowen Wu
- State Key Laboratory of Organic-Inorganic Composites, Beijing University of Chemical Technology, Beijing, 100029, China
| | - Dexian Yin
- State Key Laboratory of Organic-Inorganic Composites, Beijing University of Chemical Technology, Beijing, 100029, China
| | - Shikai Hu
- State Key Laboratory of Organic-Inorganic Composites, Beijing University of Chemical Technology, Beijing, 100029, China; Key Laboratory of Carbon Fiber and Functional Polymers, Ministry of Education, Beijing University of Chemical Technology, Beijing, 10029, China.
| | - Sizhu Wu
- State Key Laboratory of Organic-Inorganic Composites, Beijing University of Chemical Technology, Beijing, 100029, China; Key Laboratory of Carbon Fiber and Functional Polymers, Ministry of Education, Beijing University of Chemical Technology, Beijing, 10029, China
| | - Xiuying Zhao
- State Key Laboratory of Organic-Inorganic Composites, Beijing University of Chemical Technology, Beijing, 100029, China; Key Laboratory of Carbon Fiber and Functional Polymers, Ministry of Education, Beijing University of Chemical Technology, Beijing, 10029, China.
| | - Liqun Zhang
- State Key Laboratory of Organic-Inorganic Composites, Beijing University of Chemical Technology, Beijing, 100029, China; Key Laboratory of Carbon Fiber and Functional Polymers, Ministry of Education, Beijing University of Chemical Technology, Beijing, 10029, China; Institute of Emergent Elastomers, School of Materials Science and Engineering, South China University of Technology, Guangzhou, Guangdong, 510640, China
| |
Collapse
|
2
|
Aoki D, Lossada F, Hoenders D, Ajiro H, Walther A. Efficient Softening and Toughening Strategies of Cellulose Nanofibril Nanocomposites Using Comb Polyurethane. Biomacromolecules 2022; 23:1693-1702. [PMID: 35362317 DOI: 10.1021/acs.biomac.1c01625] [Citation(s) in RCA: 1] [Impact Index Per Article: 0.5] [Reference Citation Analysis] [Abstract] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 12/23/2022]
Abstract
Cellulose nanofibrils (CNFs) have attracted attention as building blocks for sustainable materials owing to their high performance and the advantages of their abundant natural resources. Bioinspired CNF/polymer nanocomposites, consisting of a soft polymer phase and a high fraction (>50 wt %) of CNF reinforcement, have been focused on excellent mechanical properties, including Young's modulus, mechanical strength, and toughness, mimicking the energy dissipation system in nature. However, efficient softening and toughening with a small amount of the soft phase is still a challenge because a large amount of the polymer phase (nearly 50%) is still required to provide ductility and toughness. Here, we describe a topological strategy in the polymer phase for efficient toughening of bioinspired CNF nanocomposites with a water-soluble comb polyurethane (PU). The comb PU provided higher elongation at break and more efficient flexibility for the nanocomposite than the linear PU, even at a small content. Moreover, CNF nanocomposites with 30 wt % of PU content and tetrabutylammonium as bulky counterions showed enhanced toughness (180% higher) and strain at break (250% higher) when compared to pure CNF due to the promotion of slippage between nanofibrils. Scanning electron microscopy (SEM) images of the fracture surface for CNF/comb PU nanocomposites displayed the pull-out of mesoscale layers and nanofibrils, supporting that the comb topology promotes the slippage between fibrils. Furthermore, the rheological study revealed that the comb PU has an entanglement plateau modulus lower than linear PU by 1 order of magnitude, related to the loosened entanglements. Our study establishes an efficient softening and toughening strategy while using small amounts of polymer phase addition, promoting interfibrillar slippage with the loosely entangled comb PU phase.
Collapse
Affiliation(s)
- Daisuke Aoki
- Graduate School of Materials Science, Nara Institute of Science and Technology, 8916-5 Takayama-cho, Ikoma, Nara 630-0192, Japan
| | - Francisco Lossada
- Department of Chemistry, A3BMS Lab-Active, Adaptive and Autonomous Bioinspired Material Systems, 55128 Mainz, Germany
| | - Daniel Hoenders
- Department of Chemistry, A3BMS Lab-Active, Adaptive and Autonomous Bioinspired Material Systems, 55128 Mainz, Germany
| | - Hiroharu Ajiro
- Graduate School of Materials Science, Nara Institute of Science and Technology, 8916-5 Takayama-cho, Ikoma, Nara 630-0192, Japan
| | - Andreas Walther
- Department of Chemistry, A3BMS Lab-Active, Adaptive and Autonomous Bioinspired Material Systems, 55128 Mainz, Germany
| |
Collapse
|
3
|
Aoki D, Miyake A, Tachaboonyakiat W, Ajiro H. Remarkable diastereomeric effect on thermoresponsive behavior of polyurethane based on lysine and tartrate ester derivatives. RSC Adv 2021; 11:35607-35613. [PMID: 35493186 PMCID: PMC9043254 DOI: 10.1039/d1ra05877k] [Citation(s) in RCA: 1] [Impact Index Per Article: 0.3] [Reference Citation Analysis] [Abstract] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 08/03/2021] [Accepted: 10/23/2021] [Indexed: 11/24/2022] Open
Abstract
This study describes the long-distance diastereomeric effect on thermoresponsive properties in water-soluble diastereomeric polyurethanes (PUs) composed of an l-lysine ethyl ester diisocyanate and a trimethylene glycol l-/d-tartrate ester, which have differences in spatial arrangements of the ethyl esters in the mirror image. The PUs based on l-lysine and l-/d-tartrate ester, named l-PU and d-PU, were synthesized with various number average molecular weights from 4700 to 13 100. In turbidimetry, l-PU showed a steep phase transition from 100%T to 0%T within about 10 °C at 4 g L−1, whereas d-PU did not change completely to 0%T transmittance even at 80 °C at 4 g L−1. In addition, the thermoresponsive properties of l-PU were less affected by concentration than those of d-PU. This long-distance diastereomeric effect on thermoresponsive behavior between l-PU and d-PU appeared in common among 6 samples with 4700 to 13 100 number average molecular weight. In the dynamic light scattering experiments at each transmittance, the hydrodynamic diameter (Dh) of l-PU increased up to 1000 nm, while the Dh of d-PU remained almost at 200–300 nm. The C
Created by potrace 1.16, written by Peter Selinger 2001-2019
]]>
O stretching vibration of FT-IR spectra showed that d-PU has more hydrogen-bonded ester groups than L-PU. Thus, we speculated that the difference in the retention of polymer chains in the micelle to promote intermicellar bridging generates the long-distance diastereomeric effect. The long-distance diastereomeric effect on thermoresponsive properties in a polyurethane system consisting of chiral monomers was reported.![]()
Collapse
Affiliation(s)
- Daisuke Aoki
- Division of Materials Science, Graduate School of Science and Technology, Nara Institute of Science and Technology 8916-5 Takayama-cho Ikoma Nara 630-0192 Japan
| | - Akihiro Miyake
- Division of Materials Science, Graduate School of Science and Technology, Nara Institute of Science and Technology 8916-5 Takayama-cho Ikoma Nara 630-0192 Japan
| | - Wanpen Tachaboonyakiat
- Department of Materials Science, Faculty of Science, Chulalongkorn University Phayathai, Pathumwan Bangkok 10330 Thailand
| | - Hiroharu Ajiro
- Division of Materials Science, Graduate School of Science and Technology, Nara Institute of Science and Technology 8916-5 Takayama-cho Ikoma Nara 630-0192 Japan .,Data Science Center, Nara Institute of Science and Technology 8916-5 Takayama-cho Ikoma Nara 630-0192 Japan
| |
Collapse
|