Oxide modified aluminum for removal of methyl orange and methyl blue in aqueous solution

Efficient Removal of Nitrate in Neutral Solution Using Zero-Valent Al Activated by Soaking

Nitrate is a contaminant widely found in surface water, and a high concentration of nitrate can pose a serious threat to human health. Zero-valent iron is widely used to reduce nitrate in aqueous solution, but an acidic condition is required. Zero-valent aluminum has a much lower redox potential (E₀(Al³⁺/Al⁰) = -1.662 V) than zero-valent iron (E₀(Fe²⁺/Fe⁰) = -0.44 V), making it a better choice for reduction of nitrate. However, a passive oxide film covering on Al surfaces inhibits its electron transfer. In this work, metal Al powder was activated by a soaking procedure in deionized water. It was found that nitrate in neutral solution can be efficiently and completely reduced by soaked Al, even if the concentration of nitrate-N was up to 100 mg L^-1. Using an optimal soaking time, the soaked Al can remove >90% of nitrate in aqueous solution within ∼2 h at 50 °C. Furthermore, the nitrate reduction efficiency increased with increasing reaction temperature and dosage of Al powder. After reaction, only ∼50% of pristine N content was left in the form of ammonia ions (NH₄⁺) in aqueous solution. Mechanism analyses showed that after soaking, Al particle surfaces were covered by a layer of loose and fine Al(OH)₃ grains, which can shorten the induction time for the beginning of the reaction between inner Al and outside ions or molecules. This is the reason why soaked Al has a high efficiency for nitrate removal. The present results indicate that soaking is an effective way to activate Al to remove nitrate in water.

Sono-degradation of Reactive Blue 19 in aqueous solution and synthetic textile industry wastewater by nanoscale zero-valent aluminum

Reactive dyes, which are commonly used in the textile industry, are toxic and carcinogenic for the ecosystem and human health. The objective of this study was to investigate the removal of Reactive Blue 19 (RB19) from aqueous solution and synthetic textile industry wastewater using nanoscale zero-valent aluminum (nZVAl), ultrasonic bath (US-40 kHz), and combined US/nZVAl through the consideration of varying experimental parameters such as pH, nZVAl dosage, contact time, and initial RB19 dye concentration. The acidic pH value was an effective parameter to degrade RB19. As the nZVAl dosage and contact time increased, the degradation of RB19 dye from aqueous solution and synthetic textile industry wastewater increased using combined US/nZVAl process. A similar result was obtained for RB19 removal with combined US/nZVAl using 0.10 g dosage at 30 min, whereas it was obtained with nZVAl alone using 0.20 g dosage at 60 min. The sono-degradation process activated the nZVAl surface depending on US cavitation effect and shock waves, and increased RB19 dye uptake capacity with a shorter contact time and lower nZVAl dosage. Increasing the initial dye concentration decreased the removal efficiency for RB19. According to the obtained reusability results, nZVAl particles could be reused for four and two consecutive cycles of combined US/nZVAl and nZVAl alone, respectively.

Polyethyleneimine grafted starch nanocrystals as a novel biosorbent for efficient removal of methyl blue dye

In this paper, a novel biosorbent of SNCs-PEI was successfully prepared by grafting polyethylenimine (PEI) onto the starch nanocrystals (SNCs) using glutaraldehyde as a crosslinking agent. The optimal preparation conditions of SNCs-PEI were determined by the orthogonal experiments of the three-factor and three-level, and the SNCs-PEI was characterized by Fourier transform infrared spectroscopy (FT-IR), energy-dispersive X-ray spectroscopy (EDAX), X-ray diffraction (XRD), and scanning electron microscopy (SEM). The zeta potential of SNCs-PEI was +26.3 mV (pH 7), which had a good adsorption performance for the anionic dye methyl blue (MB). The adsorption kinetics and isotherm of MB by SNCs-PEI were studied. At the temperature of 25, 30 and 35 °C, its maximum adsorption capacity was 337.84, 377.36 and 383.14 mg g^-1, respectively. The adsorption of MB by the SNCs-PEI was a spontaneous and endothermic process according to the thermodynamic analysis.