In vitro biocompatibility of a sandblasted, acid-etched HA composite coating on ultrafine-grained titanium

Influence of Sandblasting Process on Tribological Properties of Titanium Grade 4 in Artificial Saliva for Dentistry Applications

Titanium Grade 4 (Ti G4) is widely used in medicine for dental implants. The failure-free life of implants depends on their properties such as resistance to wear and friction processes. This paper presents an analysis of the influence of sandblasting on tribological wear of commercial dental implants made of TiG4 in artificial saliva. Tribological wear measurements were performed in a reciprocating motion in the ball-on-disc system. The scanning electron microscopy/energy-dispersive X-ray spectroscopy (SEM/EDS) method was used to characterize the surface of the implants before and after the tribological wear test. The microhardness of Ti G4 was measured before and after sandblasting by the Vickers method. The contact angle was determined by the method of sitting drop in air. The residual stress test using the X-Ray Diffraction (XRD) single-{hkl} sin2ψ method was carried out. The compressive residual stress of 324(7) MPa and surface hardening of Ti G4 was revealed after sandblasting with Al2O3 particles of 53-75 μm in diameter. It was found that sandblasting changes the surface wettability of Ti G4. The intermediate wettability of the mechanically polished surface and the hydrophobicity of the sandblasted surface was revealed. Sandblasting reduces the tribological wear and friction coefficient of Ti G4 surface in saliva. The three-body abrasion wear mechanism was proposed to explain the tribological wear of Ti G4 in saliva.

Biomimetic Deposition of Hydroxyapatite Layer on Titanium Alloys

Over the last decade, researchers have been concerned with improving metallic biomaterials with proper and suitable properties for the human body. Ti-based alloys are widely used in the medical field for their good mechanical properties, corrosion resistance and biocompatibility. The TiMoZrTa system (TMZT) evidenced adequate mechanical properties, was closer to the human bone, and had a good biocompatibility. In order to highlight the osseointegration of the implants, a layer of hydroxyapatite (HA) was deposited using a biomimetic method, which simulates the natural growth of the bone. The coatings were examined by scanning electron microscopy (SEM), X-ray diffraction (XRD), micro indentation tests and contact angle. The data obtained show that the layer deposited on TiMoZrTa (TMZT) support is hydroxyapatite. Modifying the surface of titanium alloys represents a viable solution for increasing the osseointegration of materials used as implants. The studied coatings demonstrate a positive potential for use as dental and orthopedic implants.