Mechanochemical synthesis of pure phase mixed-cation/anion (FAPbI3) x (MAPbBr3)1-x hybrid perovskite materials: compositional engineering and photovoltaic performance

Thermal stability and decomposition kinetics of mixed-cation halide perovskites

Organic-inorganic halide perovskites (OIHPs) have emerged as one of the most efficient photovoltaic materials due to their superior properties. However, improving their stability remains a key challenge. Herein, we investigate the thermal decomposition properties of OIHP FAxMA1-xPbI3 with mixed cations of formamidinium (FA) and methylammonium (MA). Using thermogravimetric analysis together with Fourier transform infrared spectroscopy, we identify and monitor the gaseous decomposition products as a function of temperature and cation composition. Thermal decomposition products of both MA and FA cations were observed at all stages of the thermal decomposition process, contrary to previous expectations. The yield, release sequence and kinetics of the organic gaseous products were found to depend strongly on the ratio between FA and MA cations. Furthermore, cesium ion doping was investigated as a potential strategy to improve the thermal stability of mixed cation perovskites. These results provide new insights into the effect of cation mixing on perovskite stability, suggesting that optimizing the cation ratios and decomposition pathways can guide approaches to boost the stability and performance of mixed cation perovskites.

A Study to Improve the Performance of Mixed Cation-Halide Perovskite-Based UVC Photodetectors

Photodetectors convert optical signals into electrical signals and demonstrate application potential in various fields, such as optical communication, image detection, environmental monitoring, and optoelectronics. In this study, a mixed cation-halide perovskite-based ultraviolet C photodetector was fabricated using a solution process. The higher the mobility of the perovskite carrier, which is one of the factors affecting the performance of electronic power devices, the better the carrier diffusion. The on/off ratio and responsivity indicate the sensitivity of the response, and together with the detectivity and external quantum efficiency, these parameters demonstrate the performance of the detector. The detector fabricated in this study exhibited a mobility of 202.2 cm2/Vs and a high on/off ratio of 105% at a -2 V bias, under 254 nm light irradiation with an intensity of 0.6 mW/cm2. The responsivity, detectivity, and external quantum efficiency of the as-fabricated detector were 5.07 mA/W, 5.49 × 1011 Jones, and 24.8%, respectively. These findings demonstrate that the solution process employed in this study is suitable for the fabrication of mixed cation-halide perovskites which show immense potential for use as photodetectors.