One-step synthesis of amorphous nickel iron phosphide hierarchical nanostructures for water electrolysis with superb stability at high current density

Interfacial engineering of POM-stabilized Ni quantum dots on porous titanium mesh for high-rate and stable alkaline hydrogen production

The development of low-cost, high-efficiency, and stable electrocatalysts for the alkaline hydrogen evolution reaction (HER) is a key challenge because the alkaline HER kinetics is slowed by an additional water dissociation step. Herein, we report an interfacial engineering strategy for polyoxometalate (POM)-stabilized nickel (Ni) quantum dots decorated on the surface of porous titanium mesh (POMs-Ni@PTM) for high-rate and stable alkaline hydrogen production. Benefiting from the strong interfacial interactions among POMs, Ni atoms, and PTM substrates, as well as unique POM-Ni quantum dot structures, the optimized POMs-Ni@PTM electrocatalyst exhibits a remarkable alkaline HER performance with an overpotential (η10) of 30.1 mV to reach a current density of 10 mA cm-2, which is much better than those of bare Ni decorated porous titanium mesh (Ni@PTM) (η10 = 171.1 mV) and POM decorated porous titanium mesh (POMs@PTM) electrocatalysts (η10 = 493.6 mV), comparable to that of the commercial 20 wt% platinum/carbon (20% Pt/C) electrocatalyst (η10 = 20 mV). Moreover, the optimized POMs-Ni@PTM electrocatalyst demonstrates excellent stability under continuous alkaline water-splitting at a current density of ∼100 mA cm-2 for 100 h, demonstrating great potential for its practical application.

Concurrent electrocatalytic hydrogen evolution and polyethylene terephthalate plastics reforming by self-supported amorphous cobalt iron phosphide electrode

The electrocatalytic hydrogen evolution reaction (HER) coupled with oxidative transformation of plastics into commodity chemical is a promising tactic to relieve the energy shortage and white pollution problems via sustainable and profitable manner, which necessitates highly active bifunctional catalytic electrode and meticulous construction of electrolysis system. Herein, a self-supported amorphous cobalt iron phosphide onto nickel foam (NF) substrate, labeled as CoFe-P/NF, was prepared by electrodeposition, which served as bifunctional catalytic electrode for alkali hydrogen evolution reaction (HER) and selective electrooxidation of polyethylene terephthalate (PET) plastic hydrolysate toward formate. Benefiting from the abundant catalytic sites within amorphous structure, the interelement synergy and sufficient exposure of catalyst to electrolyte, the self-supported CoFe-P/NF electrode displayed low overpotential (η100 of 168 mV at current density of J = 100 mA cm-2), decent stability for HER and fine tolerance to PET monomers. The CoFe-P/NF electrode could also catalyze selective electrooxidation of ethylene glycol (EG) component in PET hydrolysate to formate with high productivity (0.1 mmol cm-2h-1) and faradaic efficiency (FE, 90 %) at 1.5 V. The PET hydrolysate electrolysis system based on CoFe-P/NF enabled coproduction of H2 and value added formate at lower voltage (1.52 V at J = 20 mA cm-2) and energy consumption (84 % at J = 200 mA cm-2) relative to water electrolysis. This work showcases the coproduction of H2 fuel and formate by electrolysis of PET hydrolysate via rational design of bifunctional catalytic electrode. We believe such type of versatile catalytic electrodes can find application scenarios in electrosynthesis of more commodity chemicals and energy devices beyond the case herein.

Self-supported amorphous phosphide catalytic electrodes for electrochemical hydrogen production coupling with methanol upgrading

Efficient catalytic electrodes for cathodic hydrogen evolution reaction (HER) and anodic oxygen evolution reaction (OER) are pivotal for massive production of green hydrogen from water electrolysis, and the further replacement of kinetically sluggish OER by tailored elecrooxidation of certain organics is a promising way to co-produce hydrogen and value-added chemicals via a more energy-saving and safer manner. Herein, amorphous Ni-Co-Fe ternary phosphides (Ni_xCo_yFe_z-Ps) with different Ni:Co:Fe ratios electrodeposited onto Ni foam (NF) substrate were served as self-supported catalytic electrodes for alkaline HER and OER. The Ni₄Co₄Fe₁-P electrode deposited in solution at Ni:Co:Fe ratio of 4:4:1 displayed low overpotential (61 mV at -20 mA cm^-2) and acceptable durability for HER, while the Ni₂Co₂Fe₁-P electrode fabricated in deposition solution at Ni:Co:Fe ratio of 2:2:1 showed good OER efficiency (overpotential of 275 mV at 20 mA cm^-2) and robust durability, the further replacement of OER by anodic methanol oxidation reaction (MOR) enabled selective production of formate with 110 mV lower anodic potential at 20 mA cm^-2. The HER-MOR co-electrolysis system based on Ni₄Co₄Fe₁-P cathode and Ni₂Co₂Fe₁-P anode could save 1.4 kWh of electric energy per cubic meter of H₂ relative to mere water electrolysis. The current work offers a feasible approach to co-produce H₂ and value-upgraded formate via an energy-saving manner by rational design of catalytic electrodes and construction of co-electrolysis system, and paves the way for cost-effective co-preparation of more value-added organics and green hydrogen via electrolysis.

Prussian blue analog-derived nickel iron phosphide-reduced graphene oxide hybrid as an efficient catalyst for overall water electrolysis

Efficient and bifunctional nonprecious catalysts for oxygen evolution reaction (OER) and hydrogen evolution reaction (HER) are essential for the production of green hydrogen via water electrolysis. Transition metal (Ni, Co, Fe, etc.) phosphides are frequently documented HER catalysts, whereas their bimetallic oxides are efficient OER catalysts, thus enabling bifunctional catalysis for water electrolysis via proper operation. Herein, phosphide-reduced graphene oxide (rGO) hybrids were prepared from graphene oxide (GO)-incorporated bimetal Prussian blue analog (PBA) precursors. The hybrids could experience partial surface oxidation to create oxide layers with OER activities, and the hybrids also possessed considerable HER properties, therefore enabling bifunctional catalytic features for water electrolysis. The typical NiFeP-rGO hybrid demonstrated an overpotential of 250 mV at 10 mA cm^-2 and good durability for OER, as well as moderate HER catalytic features (overpotential of 165 mV at -10 mA cm^-2 and acceptable catalytic stability). Due to the bifunctional catalytic features, the NiFeP-rGO-based symmetric water electrolyzer demonstrated a moderate input voltage and high faradaic efficiency (FE) for O₂ and H₂ production. The current work provides a feasible way to prepare OER and HER bifunctional catalysts by facile phosphorization of PBA-associated precursors and spontaneous surface oxidation. Given the oxidation/reduction bifunctional catalytic behaviors, phosphide-rGO hybrid catalysts have great potential for widespread application in fields beyond water electrolysis, such as electrochemical pollution abatement, sensors, energy devices and organic syntheses.