Enhanced Replenishment of Active Lattice Oxygen Using Chiral Copper Oxide

Effective catalytic performance of the transition metal oxide is attributed to high specific surface areas, abundant surface oxygen atoms, and balanced valence ratios. Although the chirality of the transition metal has attracted attention, most studies have focused on optical application. A few chiral transition metal oxides were used as electrocatalysts and photocatalysts. The influence of the chiral catalysts on the thermal catalysis process has been less explored. In this study, Mn-loaded chiral (M/l-CuO and M/d-CuO) and achiral CuO (M/a-CuO) were synthesized and compared in the catalytic oxidization of toluene. Spectrally analyzed Mn was well-dispersed on both chiral and achiral CuO. l-CuO and d-CuO showed nanoflower-like chirality. The angles between each (001) plane of CuO were the source of chirality. The toluene turnover frequency (TOF) of the samples was in the order of Mn/d-CuO (5.6 × 10-5 s-1) > Mn/l-CuO (4.4 × 10-5 s-1) > Mn/a-CuO (3.2 × 10-5 s-1) at 240 °C, consistent with the order of the oxygen replenishment rate. The as-prepared catalysts had similar ratios of lattice oxygen/surface adsorbed oxygen, Mn3+/Mn4+, and Cu+/Cu2+. A higher TOF was attributed to chirality, which increased the lattice oxygen replenishment speed from the gaseous phase to the solid surface. Our study indicates gas-solid catalysis from a structure-activity viewpoint.

Nanomaterials Based Multifunctional Bioactivities of V2O5 and Mesoporous Carbon@V2O5 Composite: Preparation and Characterization

Nanocarriers have attracted considerable interest due to their prospective applications in the delivery of anticancer medications and their distinct bioactivities. Biogenic nanostructures can be effective nanocarriers for delivering drugs as a consequence of sustainable and biodegradable biomass-derived nanostructures that perform specific functions. In this case, a vanadium oxide (V2O5) and mesoporous carbon@V2O5 (C@V) composite was developed as a possible drug delivery system, and its bioactivities, including antioxidant, antibacterial, and anticancer, were investigated. Doxorubicin (DOX), an anticancer drug, was introduced to the nanoparticles, and the loading and release investigation was conducted. Strong interfacial interactions between mesoporous carbon (MC) and V2O5 nanostructures have been found to improve performance in drug loading and release studies and bioactivities. After incubation, the potent anticancer effectiveness was seen based on C@V nanocomposite. This sample was also utilized to research potential biomedical uses as an antioxidant, antibacterial, and anticancer. The most effective antioxidant, the C@V sample (61.2%), exhibited a higher antioxidant activity than the V-2 sample (44.61%). The C@V sample ultimately attained a high DOX loading efficacy of 88%, in comparison to a pure V2O5 sample (V-2) loading efficacy of 80%. Due to the combination of mesoporous carbon and V2O5, which increases specific surface area and surface sites of action as well as the morphology, it proved that the mesoporous carbon@V2O5 composite (C@V) sample demonstrated greater efficacy.

Synthesis, Characterization, and In Vivo Toxicological Evaluation of Copper (II) Oxide Containing Herbometallic Siddha Nanocomplex “Thamira Parpam”

“Thamira parpam” (TP), a copper-based herbometallic oxide (copper (II) oxide) nanodrug has been used in Siddha medicine for centuries because of its anti-ulcerogenic property. However, the physicochemical properties and in vivo toxicity of TP still remain elusive. Rigorous clinical translation requires deciphering these vital properties. We have synthesized TP following a gold standard protocol in the traditional Siddha methodology. We assessed the size, phase, elemental constituents, and thermal stability of TP by SEM and TEM, XRD, EPR, and EDAX analyses, respectively. The results depicted the conversion of metallic copper into copper (II) oxide in the final stages of TP preparation and exhibited nanodimensions ranging between 10 and 50 nm. The XPS spectra revealed the presence of oxygen-deficient state and a carbonaceous coating was found on the surface of TP using TEM analysis. In vivo safety was studied in rat toxicity models by adopting OECD guidelines. Body weight changes, feed, and water intake were unaltered upon TP administration. Hematological, biochemical profiling, and histopathological findings also suggested its nontoxic nature with no abnormalities in major organs and its functions. Interestingly, we found that the metal toxicity could have been subdued because of the carbonaceous coating around the nanoparticle copper (II) oxide, confirming that the drug is safe at a low dose. Overall, our study has enlightened the safety of TP supporting the use of Siddha formulations.