High-strength alginate fibers wet-spun from pre-crosslinked sodium alginate solutions

Facing the severe problem of microplastic pollution, there is an urgent need to develop biodegradable fibers to replace the petrochemical fibers. Sodium alginate, a biomass polysaccharide, has gained widespread attentions recently for the fiber manufacture. However, the limited mechanical strength of alginate fibers restricts their usages as load-bearing fabrics and reinforcement fibers. Here, we develop a novel strategy to prepare alginate multifilaments using pre-crosslinked sodium alginate solutions. The increase in the pre-crosslinking ratio effectively hinders the disentanglement of sodium alginate chains at high stretches, causing an increase in the shear viscosity of the solution ascertained from the capillarity-driven thinning process from 4.5 Pa·s to 9.9 Pa·s and facilitating the high alignment and orientation of sodium alginate chains. The resultant fibers possess a breaking strength of 474 MPa, elongation at break of 16 %, Young's modulus of 14.4 GPa, and toughness of 51.8 MJ/m3, exceeding most biomass fibers without reinforcement additives. The high orientation degree of 0.865 and high spinnability of alginate multifilaments enable their applications in multi-channel encryption fabrics that exhibit distinct information under various optical conditions. This rheological regulation of spinning solutions provides a facile yet effective strategy to enhance the mechanical performance and broaden application scenarios of alginate fibers.

Efficient and rapid adsorption of methylene blue dyes by novel metal-organic frameworks and organic/inorganic hybrid alginate-based dual network gel composites

To address the limitations of gel-based adsorbents, such as inadequate mechanical strength, low adsorption capacity, and limited reusability, this study presents an innovative approach employing a dual network gel. The dual network consists of calcium alginate (CA) ionic crosslinked organic networks, and vinyl silica-based nanoparticles (VSNP) as crosslinking agents in acrylic acid (AA) free radical polymerization networks (denoted as P (AA-co-VSNP), abbreviated as PAV). After freeze-drying, ultimately yielding an organic/inorganic hybrid dual network gel (referred to as CA/P(AA-co-VSNP), abbreviated as CPAV), enriched with abundant functional groups, thereby enhancing material reusability. To further enhance the adsorption capacity, CPAV undergoes hydrothermal reactions to obtain metal-organic frameworks (MOFs) composite dual network gel adsorbent (UiO-66@CPAV). UiO-66@CPAV exhibited a density of 0.165 g/cm3 and showcased a unique pore structure with nested macropores and mesopores, featuring a uniform distribution of pore holes. Notably, the specific surface area was measured at 96.3 m2/g, and an average pore diameter was 17.9 nm. Most impressively, the actual maximum adsorption capacity reached 841.7 mg/g, and even after 10 cycles of use, the adsorption capacity remained 91.9 % of its initial value. Overall, this research introduced a novel methodology for the development of dual network MOFs@gel adsorbents, showcasing promising advancements in the field.

Quantitative study on the performance of CMCS/SA composite fibers by regulating the hydrogen bonding proportions

CMCS/SA composite fibers with various intermolecular hydrogen bonding (inter-MHB) proportions are prepared via a physical blending method.