Block Copolymer Self-assembly: Exploitation of Hydrogen Bonding for Nanoparticle Morphology Control via Incorporation of Triazine Based Comonomers by RAFT Polymerization

Synthesis of polymeric nanoparticles of controlled non-spherical morphology is of profound interest for a wide variety of potential applications. Self-assembly of amphiphilic diblock copolymers is an attractive bottom-up approach to prepare such nanoparticles. In the present work, RAFT polymerization is employed to synthesize a variety of poly(N,N-dimethylacrylamide)-b-poly[butyl acrylate-stat-GCB] copolymers, where GCB represents vinyl monomer containing triazine based Janus guanine-cytosine nucleobase motifs featuring multiple hydrogen bonding arrays. Hydrogen bonding between the hydrophobic blocks exert significant influence on the morphology of the resulting nanoparticles self-assembled in water. The Janus feature of the GCB moieties makes it possible to use a single polymer type in self-assembly, unlike previous work exploiting, e.g., thymine-containing polymer and adenine-containing polymer. Moreover, the strength of the hydrogen bonding interactions enables use of a low molar fraction of GCB units, thereby rendering it possible to use the present approach for copolymers based on common vinyl monomers for the development of advanced nanomaterials.

Effect of Added Salt on the RAFT Polymerization of 2-Hydroxyethyl Methacrylate in Aqueous Media

We report the effect of added salt on the reversible addition-fragmentation chain transfer (RAFT) polymerization of 2-hydroxyethyl methacrylate (HEMA) in aqueous media. More specifically, poly(2-(methacryloyloxy)ethyl phosphorylcholine) (PMPC26) was employed as a salt-tolerant water-soluble block for chain extension with HEMA targeting PHEMA DPs from 100 to 800 in the presence of NaCl. Increasing the salt concentration significantly reduces the aqueous solubility of both the HEMA monomer and the growing PHEMA chains. HEMA conversions of more than 99% could be achieved within 6 h at 70 °C regardless of the NaCl concentration when targeting PMPC26-PHEMA800 vesicles at 20% w/w solids. Significantly faster rates of polymerization were observed at higher salt concentration owing to the earlier onset of micellar nucleation. Transmission electron microscopy (TEM) was used to construct a pseudo-phase diagram for this polymerization-induced self-assembly (PISA) formulation. High-quality images required cross-linking of the PHEMA chains with glutaraldehyde prior to salt removal via dialysis. Block copolymer spheres, worms, or vesicles can be accessed at any salt concentration up to 2.5 M NaCl. However, only kinetically trapped spheres could be obtained in the presence of 3 M NaCl because the relatively low HEMA monomer solubility under such conditions leads to an aqueous emulsion polymerization rather than an aqueous dispersion polymerization. In this case, dynamic light scattering studies indicated a gradual increase in z-average diameter from 26 to 86 nm when adjusting the target PHEMA degree of polymerization from 200 to 800. When targeting PMPC26-PHEMA800 vesicles, increasing the salt content up to 2.5 M NaCl leads to a systematic reduction in the z-average diameter from 953 to 92 nm. Similarly, TEM analysis and dispersion viscosity measurements indicated a gradual reduction in worm contour length with increasing salt concentration for PMPC26-PHEMA600 worms. This new PISA formulation clearly illustrates the importance of added salt on aqueous monomer solubility and how this affects (i) the kinetics of polymerization, (ii) the morphology of the corresponding diblock copolymer nano-objects, and (iii) the mode of polymerization in aqueous media.

Polymeric Nanofibers of Various Degrees of Crosslinking as Fillers in Poly(styrene-stat-n-butyl acrylate) Nanocomposites: Overcoming the Trade-Off between Tensile Strength and Stretchability

dummy This article is protected by copyright. All rights reserved.