Ceramic-on-polyethylene: The experience of the Ranawat Orthopaedic Center

Wear Rates With Large Metal and Ceramic Heads on a Second Generation Highly Cross-Linked Polyethylene at Mean 6-Year Follow-Up

BACKGROUND

Bearing surface wear and osteolysis are major factors limiting the durability of total hip arthroplasty (THA). Second generation annealed highly cross-linked polyethylene (HXLPE) and ceramics were introduced to THA for their excellent wear rates. However, there is little data comparing the wear rates of metal and ceramic heads on second generation HXLPE.

METHODS

Sixty patients who received a noncemented THA with a 32- or 36-mm delta ceramic head were matched with 60 THAs with a 32- or 36-mm metal head based on gender, head size, follow-up, and University of California, Los Angeles activity score. Linear and volumetric wear rates were measured.

RESULTS

At mean 6-year follow-up, the mean linear wear rates were 0.012 mm/y (standard deviation [SD] 0.045; 95% confidence interval [CI] 0.001-0.024) and 0.018 mm/y (SD 0.025; 95% CI 0.012-0.025) for the ceramic and metal groups, respectively (P = .724). The mean volumetric wear rates for the ceramic and metal head groups were 11.9 (SD 43.0; 95% CI 0.7-23.0) and 17.3 (SD 23.9; 95% CI 11.1-23.4), respectively. No significant differences were detectable in either the mean linear or volumetric wear rates (P = .380 and P = .398, respectively).

CONCLUSION

Second generation HXLPE had low wear rates and we were unable to detect a significant difference in wear rates with 32- or 36-mm metal and ceramic heads. We believe that this is due to the excellent tribological properties of second generation HXLPE. We continue to use ceramic as standard of care because of issues of trunnionosis with metal heads.

Ceramics in THR Bearings: Behavior under Off-Normal Conditions

The use of ceramics bearings in total hip joint replacement (THR) has increased markedly in the last ten years thanks to the optimum wear behaviour of ceramic-on-ceramic bearings and of the high biological safety of ceramic wear debris. As the number of ceramic THR bearings is increasing, also the number of implants that experience off-normal working conditions, e.g. edge loading, third bodies in the joint, soft tissues laxity, dislocation/subluxation of the joint, increases. Under all such conditions the surface of the bearing can be damaged to variable extent, leading eventually to a limitation of the expected performances of the implant.