Fracture Resistance of Immature Incisors Following Root Filling with Various Bioactive Endodontic Cements Using an Experimental Bovine Tooth Model

Fracture Resistance of Simulated Immature Teeth Filled with Three Types of Calcium Silicate Cement after Intracanal Medication with Ca(OH)2: An Ex Vivo Study

Objectives

The aim of this study was to evaluate the 1-day fracture resistance of simulated immature teeth with an apical plug with ProRoot MTA, MTA Angelus, and RetroMTA after calcium hydroxide intracanal medication.

Materials and Methods

Sixty extracted, single-rooted human mandibular premolars were randomly divided into six groups of 10 teeth each. Firstly, to standardize the 9 mm root length, the crowns were cut off at and 9 mm below the cementoenamel junction transversely. Simulations for immature apices were carried out by using No. 1-6 Peeso reamers to pass through the apex to obtain a diameter of 1.7 mm at the apical opening. One group served as a negative control without any treatment, while the other groups received 30 days of calcium hydroxide intracanal medication. Four groups were plugs with 4 mm of ProRoot MTA, MTA Angelus, RetroMTA, and gutta-percha, respectively. The last one was served as a positive control group without filling inside. After 1 day of incubation, specimens were vertically loaded in a universal testing machine at a crosshead speed of 1 mm/min until fracture occurred. The peak load to fracture (Newton) and fracture pattern were recorded. A one-way analysis of variance (ANOVA) followed by Tukey's HSD test was used for data analysis.

Results

The highest mean load to fracture was shown in the negative control group (543.33 ± 37.17 N), followed by ProRoot MTA (432.82 ± 68.06 N), MTA Angelus (396.92 ± 59.93 N), RetroMTA (389.08 ± 56.25 N), and gutta-percha (283.28 ± 43.40 N), and the lowest belonged to the positive control group (239.98 ± 27.19 N). The significant differences were found between both the control and experimental groups with an apical plug with calcium silicate cement (p  < 0.05). There were no significant differences among those three apical plugs (p  > 0.05).

Conclusion

Apical plugs with ProRoot MTA, MTA Angelus, and RetroMTA had an immediate strengthening effect on simulated immature teeth after calcium hydroxide intracanal medication had been used.

Evaluation of Fracture Strength after Repair of Cervical External Resorption Cavities with Different Materials

INTRODUCTION

The aim was to evaluate the stress distributions on dentin and repair materials caused by static force applied to teeth, with cervical external root resorption (CER) after repair with different materials using finite element analysis.

METHODS

This study was performed with the 3-dimensional finite element analysis method. Access cavity, root canal cavity dimensions, and supporting tissues other than cementum were modeled in the maxillary central tooth. The CER cavity was created on the labial side of the tooth model. The coronal side of the resorption cavity was restored with composite, and the radicular side with different materials (MTA, Biodentine, BioAggregate, calcium-enriched cement [CEM], glass ionomer cement [GIC], and resin-modified glass ionomer cement [RMGIC]). A static force of 300 N was applied to the palatal surface of the crown at an angle of 135° to the long axis of the tooth. The stress distributions in dentin and repair materials were analyzed.

RESULTS

The highest stress in dentin was seen in the fFigmodel with unrepaired CER. In the models repaired with MTA, GIC, and RMGIC, von Mises stress values in dentin were greater than for repairs with Biodentine, BioAggregate, and CEM materials. The von Mises stress on the repair materials applied to the root were highest for the BioAggregate material. This was followed by CEM, Biodentine, MTA, RMGIC, and GIC materials, respectively.

CONCLUSION

The repair of CER in the tooth significantly decreased the stress values in dentin. Biodentine, BioAggregate, and CEM absorbed more force and caused less stress to be transmitted to dentin compared to MTA, GIC, and RMGIC.

Effect of MTA versus CEM apical plugs on fracture resistance of endodontically treated simulated immature teeth restored with cast metal posts: an in-vitro study

BACKGROUND

Endodontically treated immature teeth which are restored with cast metal posts are of the most susceptible teeth to fracture. An apical plug is usually used as root end filling in order to seal the wide apical foramen. The current study was performed to evaluate the effect of different apical plug materials (MTA and Calcium enriched mixture cement) at varied thicknesses on fracture resistance of teeth restored with cast metal posts.

METHODS

A total of 40 extracted intact single-rooted human mandibular premolars (removed for orthodontic reasons) were used in the study. The coronal part of each tooth was removed and root canal preparation was performed. A size 4 Gates Glidden drill was used to enlarge the canal and was passed through the apical foramen in order to simulate an immature apex. Samples were randomly divided into 5 groups (n = 8) according to apical plug (control group: No plug, group MTA5: 5 mm MTA plug, group CEM5: 5 mm CEM plug, group MTA3: 3 mm MTA plug, group CEM3: 3 mm CEM plug). Post-space preparations were performed and cast metal post-and-cores were fabricated and cemented. Fracture resistance was assessed using a universal testing machine. Fracture thresholds were recorded and data were analyzed using One-way ANOVA and Dunnett's T3 tests with significance level at P value < 0.05.

RESULTS

The analysis showed a significant difference of fracture resistance between groups (P value < 0.05). The mean fracture resistance of samples in control group was significantly lower than MTA5 (P value = 0.003). There was no significant difference between other groups (P value > 0.05).

CONCLUSIONS

Within the limits of this study, the evidence indicated that placement of a 5 mm MTA apical plug increased the fracture resistance in simulated immature teeth which are restored with cast metal posts, compared to control group (gutta-percha and sealer). While the results were not as promising for a 3 mm MTA apical plug or either 3 or 5 mm CEM apical plug.

Effect of mineral trioxide aggregate and biodentine™ on fracture resistance of immature teeth dentine over time: in vitro study

PURPOSE

The aim of this in vitro study was to evaluate the effect of root filling with White Mineral Trioxide Aggregate (WMTA) and Biodentine™ (BD) on the fracture resistance of simulated immature teeth over different time periods.

METHODS

Sixty sound-extracted human single-rooted premolars were randomly allocated into 3 groups, 2 experimental and 1 control group, with 20 teeth each. Simulation of roots into immature apices were done using Peeso reamers. After preparation, the root canals of teeth in the experimental groups were completely filled with either WMTA or BD. The control group was subdivided into positive controls (n = 10) which received no treatment and negative controls (n = 10) which were prepared the same way and filled with normal saline. The specimens were subjected to fracture testing using a universal testing machine after 2 weeks and 3 months. The peak load to fracture and the fracture location were recorded.

RESULTS

Regarding fracture resistance, the MTA group had the highest fracture resistance at 2 weeks testing, while at 3 months there was no significant difference between the groups (P > 0.05). Regarding fracture location, at 2 weeks there was no significant difference in the fracture location between the groups, while at 3 months, the difference was significant (P < 0.05), the middle root fracture being the most frequent (63.3%).

CONCLUSION

No significant difference in fracture resistant of simulated immature teeth was observed after 3 months when they were filled with Biodentine or WMTA, indicating that Biodentine could be a suitable substitute for MTA. There was no difference in the possible fracture location at 2 weeks, while after 3 months middle root fractures were more frequent.

Effect of Casein Phosphopeptide-Amorphous Calcium Phosphate on Fracture Resistance of Reattached Tooth Fragments Using Conventional and Self-Adhesive Bioactive Flowable Composite

Objectives  The present study aimed to investigate the effect of casein phosphopeptide–amorphous calcium phosphate (CPP-ACP) complex and the type of flowable composite (conventional or self-adhesive bioactive) on the fracture resistance of fractured incisors restored through reattachment technique.

Materials and Methods  In this experimental in vitro study, 60 extracted bovine central mandibular incisors were randomly divided into six groups ( n = 10) according to the reattachment technique. Their incisal edges were cut off to represent an enamel–dentin fracture. The fragment edges were reattached as follows: Group 1—selective etching and bonding followed by conventional flowable composite; Group 2—selective etching and bonding followed by bioactive flowable composite; Group 3 was like Group 2 but without applying bonding; Groups 4, 5, and 6 were similar to Groups 1, 2, and 3, respectively, but both tooth fragments were pretreated with CPP-ACP-containing paste for 3 minutes. Fracture resistance was assessed by a universal testing machine.

Statistical Analysis  Data were analyzed by SPSS—Statistical Package for the Social Sciences—software using one-way analysis of variance and Tukey post-hoc tests (α= 0.05).

Results  The highest and lowest fracture resistance was recorded in Groups 5 (15.96 MPa) and Group 6 (1.95 MPa), respectively, being significantly different from the other groups. The mean fracture resistance of Groups 3 and 6 was significantly lower than the other groups ( p < 0.05). However, Groups 1, 2, and 4 showed no difference in fracture resistance.

Conclusion  Bioactive composite was not superior to conventional composite for fragment reattachment, but using it in self-adhesive mode reduced the fracture strength significantly. Yet, pretreatment with CPP-ACP, followed by application of adhesive, improved the fracture resistance of bioactive composite.