Chou J, Komuro M, Hao J, Kuroda S, Hattori Y, Ben-Nissan B, Milthorpe B, Otsuka M. Bioresorbable zinc hydroxyapatite guided bone regeneration membrane for bone regeneration.
Clin Oral Implants Res 2014;
27:354-60. [PMID:
25363210 DOI:
10.1111/clr.12520]
[Citation(s) in RCA: 29] [Impact Index Per Article: 2.9] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Accepted: 10/10/2014] [Indexed: 01/09/2023]
Abstract
OBJECTIVES
The aim of this study was to investigate the bone regenerative properties of a heat treated cross-linked GBR membrane with zinc hydroxyapatite powders in the rat calvarial defect model over a 6-week period.
MATERIAL AND METHODS
In vitro physio-chemical characterization involved X-ray diffraction analysis, surface topology by scanning electron microscopy, and zinc release studies in physiological buffers. Bilateral rat calvarial defects were used to compare the Zn-HAp membranes against the commercially available collagen membranes and the unfilled defect group through radiological and histological evaluation.
RESULTS
The synthesized Zn-MEM (100 μm thick) showed no zinc ions released in the phosphate buffer solution (PBS) buffer, but zinc was observed under acidic conditions. At 6 weeks, both the micro-CT and histological analyses revealed that the Zn-MEM group yielded significantly greater bone formation with 80 ± 2% of bone filled, as compared with 60 ± 5% in the collagen membrane and 40 ± 2% in the unfilled control group.
CONCLUSION
This study demonstrated the use of heat treatment as an alternative method to cross-linking the Zn-MEM to be applied as a GBR membrane. Its synthesis and production are relatively simple to fabricate, and the membrane had rough surface features on one side, which might be beneficial for cellular activities. In a rat calvarial defect model, it was shown that new bone formation was accelerated in comparison with the collagen membrane and the unfilled defect groups. These results would suggest that Zn-MEM has the potential for further development in dental applications.