A Raman investigation of lead haloborate glasses

Third-order nonlinear spectra and optical limiting of lead oxifluoroborate glasses

We have determined two-photon absorption and nonlinear refraction spectra of the 50BO(1.5) - (50-x)PbF(2) - xPbO glasses (with x = 25, 35, 50 cationic %) at the range of the 470 and 1550 nm. The replacement of fluor atoms by oxygen leads to an increase in the third-order susceptibility, due to the formation of non-bridging oxygens (NBO). The nonlinear index of refraction is one order of magnitude higher than the one for fused silica, and it increases almost twice for the sample with x = 50. This sample has also shown promising features for all-optical switching as well as for optical limiting.

Rare earth-doped lead borate glasses and transparent glass-ceramics: structure-property relationship

Correlation between structure and optical properties of rare earth ions in lead borate glasses and glass-ceramics was evidenced by X-ray-diffraction, Raman, FT-IR and luminescence spectroscopy. The rare earths were limited to Eu(3+) and Er(3+) ions. The observed BO(3)↔BO(4) conversion strongly depends on the relative PbO/B(2)O(3) ratios in glass composition, giving important contribution to the luminescence intensities associated to (5)D(0)-(7)F(2) and (5)D(0)-(7)F(1) transitions of Eu(3+). The near-infrared luminescence and up-conversion spectra for Er(3+) ions in lead borate glasses before and after heat treatment were measured. The more intense and narrowing luminescence lines suggest partial incorporation of Er(3+) ions into the orthorhombic PbF(2) crystalline phase, which was identified using X-ray diffraction analysis.

Er-Doped Lead Borate Glasses and Transparent Glass Ceramics for Near-Infrared Luminescence and Up-Conversion Applications

Lead borate based glasses have been analyzed using Raman and infrared spectroscopy. The formation of different borate groups and the direction of BO3 <--> BO4 conversion strongly depends on the PbO- and/or PbF2-to-B2O3 ratio in chemical composition. PbF2-PbO-B2O3 based glasses containing Er3+ ions have been studied after annealing. The orthorhombic PbF2 crystallites are formed during thermal treatment, which was evidenced by X-ray diffraction analysis. Near-infrared luminescence at 1530 nm and green up-conversion at 545 nm have been registered for samples before and after annealing. The luminescence bands correspond to 4I13/2-4I15/2 and 4S3/2-4I15/2 transitions of Er3+ ions, respectively. In comparison to the precursor glasses, the luminescence intensities are higher in the studied transparent oxyfluoride glass ceramics. Simultaneously, the half-width of the luminescence lines slightly decreases. It can be the evidence that a small amount of the Er3+ ions is incorporated into the orthorhombic PbF2 phase.

Low-Frequency Raman Scattering and the Fast Relaxation Process in Glycerol

Ab initio molecular orbital calculations were used to determine the structure and vibrational frequencies of the cyclic glycerol trimer, which represents the region of medium-range ordering in liquid and supercooled glycerol. The calculations reproduced the experimentally observed low-frequency Raman scattering peak (or the "boson peak") at approximately50 per centimeter, which suggests that the peak results from the localized collective motions of the cooperatively hydrogen-bonded hydroxyl groups. The calculations also suggest that the fast relaxation process may result from the translational motion of each glycerol molecule in the cyclic structure. On the basis of these results, a model of the glass transition was developed.