In situ Brillouin study of sodium alumino silicate glasses under pressure

A-thermal elastic behavior of silicate glasses

Depending on the composition of silicate glasses, their elastic moduli can increase or decrease as function of the temperature. Studying the Brillouin frequency shift of these glasses versus temperature allows the a-thermal composition corresponding to an intermediate glass to be determined. In an intermediate glass, the elastic moduli are independent of the temperature over a large temperature range. For sodium alumino-silicate glasses, the a-thermal composition is close to the albite glass (NaAlSi3O8). The structural origin of this property is studied by in situ high temperature Raman scattering. The structure of the intermediate albite glass and of silica are compared at different temperatures between room temperature and 600 °C. When the temperature increases, it is shown that the high frequency shift of the main band at 440 cm(-1) in silica is a consequence of the cristobalite-like alpha-beta transformation of 6-membered rings. This effect is stronger in silica than bond elongation (anharmonic effects). As a consequence, the elastic moduli of silica increase as the temperature increases. In the albite glass, the substitution of 25% of Si(4+) ions by Al(3+) and Na(+) ions decreases the proportion of SiO2 6-membered rings responsible for the silica anomaly. The effects of the silica anomaly balance the anharmonicity in albite glass and give rise to an intermediate a-thermal glass. Different networks, formers or modifiers, can be added to produce different a-thermal glasses with useful mechanical or chemical properties.

Pressure-induced changes in interdiffusivity and compressive stress in chemically strengthened glass

Glass exhibits a significant change in properties when subjected to high pressure because the short- and intermediate-range atomic structures of glass are tunable through compression. Understanding the link between the atomic structure and macroscopic properties of glass under high pressure is an important scientific problem because the glass structures obtained via quenching from elevated pressure may give rise to properties unattainable under standard ambient pressure conditions. In particular, the chemical strengthening of glass through K(+)-for-Na(+) ion exchange is currently receiving significant interest due to the increasing demand for stronger and more damage-resistant glass. However, the interplay among isostatic compression, pressure-induced changes in alkali diffusivity, compressive stress generated through ion exchange, and the resulting mechanical properties are poorly understood. In this work, we employ a specially designed gas pressure chamber to compress bulk glass samples isostatically up to 1 GPa at elevated temperature before or after the ion exchange treatment of a commercial sodium-magnesium aluminosilicate glass. Compression of the samples prior to ion exchange leads to a decreased Na(+)-K(+) interdiffusivity, increased compressive stress, and slightly increased hardness. Compression after the ion exchange treatment changes the shape of the potassium-sodium diffusion profiles and significantly increases glass hardness. We discuss these results in terms of the underlying structural changes in network-modifier environments and overall network densification.