Evaluation of structural, mechanical, and cellular behavior of electrospun poly-3-hydroxybutyrate scaffolds loaded with glucosamine sulfate to develop cartilage tissue engineering

High performance filtration membranes from electrospun poly (3-hydroxybutyrate)-based fiber membranes for fine particulate protection

PM2.5 (particulate matter with a size of <2.5 μm) pollution has become a critical issue owing to its adverse health effects, including bronchitis, pneumonopathy, and cardiovascular diseases. Globally, around 8.9 million premature casualties related to exposure to PM2.5 were reported. Face masks are the only option that may restrict exposure to PM2.5. In this study, a PM2.5 dust filter was developed via the electrospinning technique using the poly (3-hydroxybutyrate) (PHB) biopolymer. Smooth and continuous fibers without beads were formed. The PHB membrane was further characterized, and the effects of the polymer solution concentration, applied voltage, and needle-to-collector distance were analyzed via the design of experiments technique, with three factors and three levels. The concentration of the polymer solution had the most significant effect on the fiber size and the porosity. The fiber diameter increased with increasing concentration, but decreases the porosity. The sample with a fiber diameter of ∼600 nm exhibited a higher PM2.5 filtration efficiency than the samples with a diameter of 900 nm, according to an ASTM F2299-based test. The PHB fiber mats fabricated at a concentration of 10%w/v, applied voltage of 15 kV, and needle tip-to-collector distance of 20 cm exhibited a high filtration efficiency of 95% and a pressure drop of <5 mmH2O/cm2. The tensile strength of the developed membranes ranged from 2.4 to 5.01 MPa, higher than those of the mask filters available in the market. Therefore, the prepared electrospun PHB fiber mats have great potential for the manufacture of PM2.5 filtration membranes.

Evaluation of Angiogenesis in an Acellular Porous Biomaterial Based on Polyhydroxybutyrate and Chitosan Using the Chicken Ex Ovo Chorioallantoic Membrane Model

Simple Summary

The chorioallantoic membrane (CAM) is an avian extraembryonic membrane widely used as an experimental assay to study angiogenesis and its inhibition in response to tissues, cells, or soluble factors. In recent years, the CAM has become popular in scientific studies focused on the use of its potential for the study of biocompatibility of materials for regenerative strategies and tissue engineering applications. Great research efforts are being made to develop innovative biomaterials able to treat hard tissue defects, including diseases such as a bone cancer. In this article, we describe an approach to detect the formation of blood vessels inside the porous acellular biopolymer polyhydroxybutyrate/chitosan (PHB/CHIT) scaffold using the CAM assay as an in vivo alternative animal model, including macroscopic, histological, immunohistochemical, and molecular evaluation of the biocompatibility.

Abstract

The chorioallantoic membrane (CAM) is a highly vascularized avian extraembryonic membrane widely used as an in vivo model to study angiogenesis and its inhibition in response to tissues, cells, or soluble factors. In recent years, the use of CAM has become an integral part of the biocompatibility testing process for developing biomaterials intended for regenerative strategies and tissue engineering applications. In this study, we used the chicken ex ovo CAM assay to investigate the angiogenic potential of innovative acellular biopolymer polyhydroxybutyrate/chitosan (PHB/CHIT) scaffold, which is intended for the treatment of hard tissue defects, depending on treatment with pro- and anti-angiogenic substances. On embryonic day (ED) 7, the experimental biomaterials were placed on the CAM alone or soaked in vascular endothelial growth factor (VEGF-A), saline solution (PHY), or tyrosine kinase inhibitor (SU5402). After 72 h, the formation of vessels was analyzed in the surrounding area of the scaffold and inside the pores of the implants, using markers of embryonic endothelium (WGA, SNA), myofibroblasts (α-SMA), and macrophages (KUL-01). The morphological and histochemical analysis showed strong angiogenic potential of untreated scaffolds without additional effect of the angiogenic factor, VEGF-A. The lowest angiogenic potential was observed in scaffolds soaked with SU5402. Gene expression of pro-angiogenic growth factors, i.e., VEGF-A, ANG-2, and VE-CAD, was upregulated in untreated scaffolds after 72 h, indicating a pro-angiogenic environment. We concluded that the PHB/CHIT has a strong endogenous angiogenic potential and could be promising biomaterial for the treatment of hard tissue defects.

How the Nonwoven Polymer Volume Microstructure Is Transformed under Tension in an Aqueous Environment

The fibrous porous structure of polymers can mimic the extracellular matrix of the native tissue, therefore such polymers have a good potential for use in regenerative medicine. Organs and tissues within the body exhibit different mechanical properties depending on their functionality, thus artificial scaffolds should have mechanical behaviors similar to the extracellular matrix in conditions like living organisms, primarily in aqueous media. Several methods have been investigated in aquatic environments, including noninvasive techniques based on ultrasonic focused beams for biological objectives. In this study we explored the tensile behavior of poly(L-lactide) nonwoven polymer scaffolds using high-frequency ultrasound microscopy combined with a horizontal testing machine, which provided a visualization of the reorganization and transformation of the dynamic volume microstructure. The mechanisms of unwinding, elongation, orientation, and deformation of polymer fibers under uniaxial tension were revealed. We observed an association between the lined plastic deformation from 100 to 400% and the formation of multiple necks in the fibers, which caused stress relaxation and significant rarefaction of the fibrous microstructure. It was shown that both peaks on the stress–strain curve corresponded to the microstructure of aligned fibers in terms of initial diameter and thinning fibers. We discuss the possible influence of these microstructure transformations on cell behavior.

Preparation of Polystyrene Microsphere-Templated Porous Monolith for Wastewater Filtration

Porous monoliths prepared using templates are highly sought after for filtration applications due to their good mass transport properties and high permeability. Current templates, however, often lead to the formation of dead-end pores and irregular pore distributions, which reduce the efficiency of the substrate flow across the monolith column. This study focused on the preparation of a microsphere-templated porous monolith for wastewater filtration. The optimal template/monomer ratio (50:50, 60:40, 70:30) was determined, and appropriate template removal techniques were assessed for the formation of homogenous pores. The physicochemical characteristics and pore homogeneity of the monoliths were examined. The 60:40 ratio was determined to result in monoliths with homogeneous pore distributions ranging from 1.9 μm to 2.3 μm. SEM and FTIR investigations revealed that solvent treatment was effective for removing templates from the resulting solid monolith. The water quality assessments revealed reductions in the turbidity and the total number of suspended particles in the tested wastewater of up to 96–99%. The findings of this study provide insightful knowledge regarding the fabrication of monoliths with homogenous pores that are beneficial for wastewater treatment.

Structure and biological compatibility of polycaprolactone/zinc-hydroxyapatite electrospun nanofibers for tissue regeneration

Although guided tissue regeneration (GTR) is a useful tool for regenerating lost tissue as bone and periodontal tissue, a biocompatible membrane capable of regenerating large defects has yet to be discovered. This study aimed to characterize the physicochemical properties and biological compatibility of polycaprolactone (PCL) membranes associated with or without nanostructured hydroxyapatite (HA) (PCL/HA) and Zn-doped HA (PCL/ZnHA), produced by electrospinning. PCL, PCL/HA, and PCL/ZnHA were characterized by field emission scanning electron microscopy (FESEM), transmission electron microscopy (TEM), energy dispersive X-ray spectroscopy (EDS), X-ray diffraction (XRD), thermal gravimetric analysis (TGA), and differential scanning calorimetry (DSC). Nanoparticles of HA or ZnHA were homogeneously distributed and dispersed inside the PCL fibers, which decreased the fiber thickness. At 1 wt% of HA or ZnHA, these nanoparticles acted as nucleating agents. Moreover, HA and ZnHA increased the onset of the degradation temperature and thermal stability of the electrospun membrane. All tested membranes showed no cytotoxicity and allowed murine pre-osteoblast adhesion and spreading; however, higher concentrations of PCL/ZnHA showed less cells and an irregular cell morphology compared to PCL and PCL/HA. This article presents a cytocompatible, electrospun, nanocomposite membrane with a novel morphology and physicochemical properties that make it eligible as a scaffold for GTR.

Development and thermochemical characterization of an antioxidant material based on polyhydroxybutyrate electrospun microfibers

The use of antioxidants such as curcumin (Cur) or quercetin (Que) in biomedical and biotechnological applications has been studied owing to their capability to prevent oxidative stress and inhibit free radicals. Using polyhydroxybutyrate (PHB) electrospun fibers is presented as a proper option to encapsulate curcumin and quercetin due to its biocompatibility and biodegradability characteristics. Electrospun fibers were obtained dissolving commercial PHB in chloroform:N,N-dimethylformamide (DMF) (4:1) at 7% m/V, and adding two different concentrations of antioxidant (Cur, and Que) 1%m/m, and 7% m/m. These polymeric solutions were electrospun at different conditions and the obtained fibers were characterized by scanning electron microscopy (SEM), thermogravimetric (TGA) analysis, and Fourier transform infrared spectroscopy (FT-IR). The curcumin and quercetin releases into phosphate buffer saline (PBS) at pH 7.4 were obtained in vitro and measured by spectrophotometry. Antioxidant activities were measured by spectrophotometry in a microplate reader using the 2,2-diphenyl-1-picrylhydrazyl (DPPH) method. Fibers obtained with different formulations presented a chemical composition in accordance with PHB according to FTIR spectra, the diameters fluctuate between 0.761 ± 0.123 and 1.803 ± 0.557 μm, with qualities over 0.95 according to their morphology, and the melting temperature resulted near 178 °C according to the bibliography. The crystallinity of fibers decreases while curcumin or quercetin concentration increases for the studied interval, indeed, quercetin showed a higher impact on the relative crystallinity of fibers. Antioxidant activity of active compounds is maintained after encapsulation in PHB electrospun fibers, and quercetin resulted in near four times antioxidant activity compared to curcumin according to DPPH analysis.

Chondroitin sulfate modified 3D porous electrospun nanofiber scaffolds promote cartilage regeneration

3D electrospun nanofibrous scaffolds have been developed for cartilage regeneration, however, there is no consensus on the preferable method for biocompatible scaffolds that enhance regeneration and attenuate inflammation. We designed a 3D porous electrospun polylactic acid (PLA) @gelatin-based scaffold by a novel method. Chondroitin sulfate (CS), commonly used in clinical cartilage treatment, is capable of regulating cartilage formation and inhibiting inflammation. Thus we further functionalized the 3D scaffold by crosslinking of CS, assuming that CS-functionalized scaffold (CSS) would promote cartilage regeneration and modulate inflammation. We confirmed that CSS exhibits not only appropriate reversible compressibility and mechanical property, but also appropriate biocompatibility, allowing cell proliferation. In vitro, the potential of CSS for chondrogenic differentiation was improved compared to control and PLA@gelatin scaffold as chondrogenic markers Collagen2 and Aggrecan was significantly increased. Meanwhile, significant reduction in two crucial inflammatory factors (NO and PGE2) in CSS group demonstrated inflammation inhibition. In vivo, rabbit cartilage defects were created and CSS effectively promoted cartilage repair. Additionally, superior anti-inflammation effect of CSS was demonstrated by reduction in iNOS and PGES, enzymes producing NO and PGE2, respectively by immunohistology. Our results indicated the preferable property of CSS for cartilage regeneration and its potential in immunoregulation.

Modified poly(3-hydroxybutyrate)-based scaffolds in tissue engineering applications: A review

As a member of the polyhydroxyalkanoate (PHAs) family, Poly(3-hydroxybutyrate) (PHB) has attracted much attention for a variety of medical applications because of its desirable properties such as high biocompatibility, nontoxic degradation products and high mechanical strength in comparison to other polymers in different fields including tissue engineering. There are different approaches such as making PHB alloy scaffolds, using PHB as a coating for ceramic-based scaffolds and producing composite scaffolds by using a mixture of PHB with ceramic particles utilized to improve hydrophobicity, degradation rate and brittleness. In this review, different applications of PHB, its alloys and composites in tissue engineering are explained based on the common methods of fabrication such as polymeric sponge replication, electrospinning and salt leaching.

Cartilage tissue engineering using injectable functionalized Demineralized Bone Matrix scaffold with glucosamine in PVA carrier, cultured in microbioreactor prior to study in rabbit model

Using 3D model of injectable scaffolds for cartilage tissue engineering is one of the challenges that should be addressed to avoid invasive surgery for treatment. For this purpose, chondrocytes on Demineralized Bone Matrix (DBM) scaffolds functionalized with glucosamine in 20% polyvinyl alcohol (PVA) as a carrier was applied to the micro-bioreactor in-vitro, then the study was continued on in-vivo stage. Scaffold biocompatibility tests were performed and the mechanical and physicochemical properties were studied showing the fact that DBM was functionalized by Glucosamine, scaffold degradation rate was 53% after 720 h and swelling ratio was 2.5 times after 16 h, injectable scaffold demonstrated better mechanical characteristics (P < 0.05) than other concentrations of PVA. Consequently, in-vitro tests, including live-dead imaging resulting in 99% viability after 14 days (P < 0.001), DAPI staining and scanning electron microscope imaging were performed to determine the number and viability of the cells on the scaffold, showing a cells proliferation property of this group compared with the control after 14 days (P < 0.0001), then relative gene expression was evaluated and protein expression was assessed. The overall chondrogenic gene expression improved (P < 0.05) compared to the control (2D culture). Subsequently, the scaffold were loaded with chondrocytes and injected into the cartilage lesion part After 24 weeks of surgery, MRI and immunocytochemistry were performed. Then all outputs proved that the scaffold plus cell group had a significantly higher topological score (P < 0.0001) than other groups compared to normal cartilage. Finally, studies have shown that transplantation of chondrocytes in DBM, polyvinyl alcohol and glucosamine scaffold through one surgical stage improves cartilage lesion and it can be considered as a breakthrough in tissue engineering.

Hybrid and Composite Scaffolds Based on Extracellular Matrices for Cartilage Tissue Engineering

IMPACT STATEMENT

Scaffolds fabricated from extracellular matrix (ECM) derivatives are composed of conducive structures for cell attachment, proliferation, and differentiation, but generally do not have proper mechanical properties and load-bearing capacity. In contrast, scaffolds based on synthetic biomaterials demonstrate appropriate mechanical strength, but the absence of desirable biological properties is one of their main disadvantages. To integrate mechanical strength and biological cues, these ECM derivatives can be conjugated with synthetic biomaterials. Hence, hybrid scaffolds comprising both advantages of synthetic polymers and ECM derivatives can be considered a robust vehicle for tissue engineering applications.