An improved method for the production of high purity silica from sugarcane bagasse ash obtained from a bioethanol plant boiler

Extraction of silica from sugarcane bagasse ash and its utilization in zeolite 4A synthesis for CO2 adsorption

Sugarcane bagasse ash (SCBA) is a solid waste containing a high amount of silica (SiO2) and is suitable to utilize as a silica source for synthesizing zeolite NaA. SCBA is typically calcined at high temperatures before silica extraction. The method is not environmentally friendly because it consumes energy and produces CO2. This work demonstrates an alternative extraction method of SiO2 from SCBA by treating it with hydrochloric (HCl) and sodium hydroxide (NaOH) solution. The obtained mixture was separated by paper filter No. 1 (P) and a combination of paper filter and syringe filter (PS). The solution was neutralized by HCl solution, producing silica (SiO2-P and SiO2-PS) with a purity of 98 wt%. Both SiO2 samples and SCBA were utilized to synthesize zeolite NaA for CO2 adsorption. The CO2 adsorption capacities of NaA-P and NaA-PS were 4.30 and 4.10 mmol gadsorbent -1, in the same range as commercial NaA. The capacity is influenced by the total basicity of zeolite. The CO2 adsorption behavior of all samples correlates well with the Toth model. The CO2 adsorption kinetics agrees well with the pseudo-second-order kinetic model. Overall, this work shows the successful extraction of silica via using a direct NaOH solution, yielding high-purity silica sufficient for synthesizing zeolite NaA, a promising adsorbent of CO2.

Green Synthesis of Crystalline Silica from Sugarcane Bagasse Ash: Physico-Chemical Properties

Sugarcane bagasse South Africa is an agricultural waste that poses many environmental and human health problems. Sugarcane bagasse dumps attract many insects that harm the health of the population and cause many diseases. Sugarcane ash is a naturally renewable source of silica. This study presents for the first time the extraction of nanosilica from sugar cane bagasse ash using L-cysteine hydrochloride monohydrate acid and Tetrapropylammonium Hydroxide. The structural, morphological, and chemical properties of the extracted silica nanoparticles was cross examined using XRD, FTIR, SEM, and TGA. SEM analysis presents agglomerates of irregular sizes. It is possible to observe the structure of nanosilica formed by the presence of agglomerates of irregular shapes, as well as the presence of some spherical particles distributed in the structure. XRD analysis has revealed 2θ angles at 20, 26, 36, 39, 50, and 59 which shows that each peak on the xrd pattern is indicative of certain crystalline cubic phases of nanosilica, similar to results reported in the literature by Jagadesh et al. in 2015. The crystallite size estimated by the Scherrer equation based on the aforementioned peaks for ca-silica and L-cys-silica for the extracted particles had an average diameter of 26 nm and 29 nm, respectively. Furthermore, it showed a specific surface area of 21.6511 m²/g and 116.005 m²/g for ca-silica and L-cys silica, respectively. The Infrared (IR) spectra showed peaks at 461.231 cm⁻¹, 787.381 cm⁻¹ and 1045.99 cm⁻¹ which corresponds to the Si~O~Si bending vibration, the Si~O~Si stretch vibration, and the Si~O~Si stretching vibration, respectively. This confirms the successful extraction of nanosilica from sugar cane bagasse ash. TGA analysis has revealed that the as received sugarcane bagasse has high loss on ignition (LOI) of 18%, corresponding to the presence of the unburnt or partial burnt particles, similar to results reported by Yadav et al. This study has shown that sugar cane bagasse ash is a natural resource of silica which should be harnessed for industrial purposes in south Africa.