Recovery of Platinum and Palladium from Spent Automobile Catalyst by Solvent-Impregnated Resins

A New Impregnated Adsorbent for Noble Metal Ion Sorption

Noble metals (NM) such as gold, platinum, palladium, and rhodium are widely applied in the electronics and automotive industries. Thus, the search for cheap and selective sorbents for noble metals is economically justified. Nitrolite does not sorb noble metal ions. A new impregnated sorbent was prepared. The natural sorbent Nitrolite was impregnated with Aliquat 336 using a new warm impregnation method. After the impregnation process, Nitrolite adsorbed platinum(IV), palladium(II), and gold(III) ions from the chloride solutions. The values of the sorption capacity for palladium(II) and platinum(IV) ions were 47.63 mg/g and 51.39 mg/g, respectively, from the 0.1 M HCl model solution. The sorption capacity for gold(III) ions was estimated to be 73.43 mg/g from the 0.1 M HCl model solution. An exhausted catalytic converter was leached, and platinum(IV), palladium(II), and rhodium(III) were transferred to the chloride solution. The impregnated sorbent Nitrolite-Aliquat 336 was used in the investigations of the platinum(IV), palladium(II), and rhodium(III) ions' sorption from a real solution. The impregnated sorbent Nitrolite-Aliquat 336 proved to be suitable for the recovery of platinum(IV) and palladium(II) ions, whereas rhodium ions were not sorbed from the leached solutions. Notably, 1 M thiourea in the 1 M HCl solution desorbed platinum(IV), palladium(II), and gold(III) above 94%.

Environmentally friendly Pd(II) recovery from spent automotive catalysts using resins impregnated with a pincer-type extractant

Extractant-impregnated resins have potential for recovering platinum group metals selectively and efficiently. Herein, 1,3-bis(2-(octylthio)propan-2-yl)benzene (1), a pincer-type extractant, was impregnated in Amberlite XAD-7 resin (1-EIR), and the batch Pd(II) sorption conditions, including impregnated amount, shaking time, Pd(II) concentration, HCl concentration, and Pd(II) desorption reagents, were optimized. The maximum Pd(II) sorption capacity of 1-EIR was 49 mg g⁻¹ after 24 h in a 700 ppm Pd(II) solution. Over 20 adsorption–desorption cycles, 1-EIR showed good reusability, with a sorption percentage (S%) of > 92%. However, not all Pd(II) was desorbed from 1-EIR. Complete Pd(II) collection was achieved by combining desorption with flaking of the Pd–extractant complex from Pd(II)-loaded 1-EIR by Soxhlet extraction, as ~ 13 mg g⁻¹ remained after the 20th adsorption–desorption cycle by absorptiometric method. The sorption mechanism was elucidated based on the Langmuir isotherm model, thermodynamic parameters, and sorption kinetics. Pd(II) sorption by 1-EIR was spontaneous and endothermic, and the sorption kinetics followed a pseudo-second-order model. Notably, 1-EIR also exhibited high selectivity for Pd(II) from a simulated mixed metal solution and a spent automotive catalyst leachate (S% = 98% and > 99%, respectively). Thus, this extractant-impregnated system is promising for selective Pd(II) recovery from spent automotive catalysts and other secondary resources.