Application of Modern Analytical Techniques to the Investigation of Cellulose Nitrates

Physical-Mechanical Properties of Nitrodopes Affected by Ultra-Violet Radiation

The FTIR spectroscopy has been employed in this research work to monitor the process of nitrodope photodegradation, by measuring surfaces of bands typical of a nitro group. Nitric esters are subject to degradation, which is reflected on a quantitative ratio of the surfaces of the IR bands that originate from the nitric ester. The obtained results show that the length of the UV rays' activity on the samples over the time periods of 240, 480 and 960 minutes directly affects the spectrum appearance of the same sample before and after the irradiation. The longer the action time of the UV rays and the higher a mass percentage of nitrocellulose in the nitrodope is, the smaller the bands' surfaces become, i.e. the level of degradation is higher. In order to confirm the degradation of nitrodope, the degree of crosslinking has also been examined by determining the König hardness and also the mean viscosity molar mass has been defined repeatedly applying the capillary viscosimetry method.

Direct dissolution of cellulose in NaOH/thiourea/urea aqueous solution

Untreated cellulose was directly and quickly dissolved in NaOH/thiourea/urea aqueous solution. The mechanism of dissolution was investigated by SEM, WXRD and (13)C NMR. The components of this solvent cannot dissolve cellulose on their own, and the interactions between NaOH and urea, as well as between NaOH and thiourea, play an important role in improving the dissolution of cellulose. Moreover, (13)C NMR spectra proved that NaOH, thiourea, and urea were bound to cellulose molecules, which brings cellulose molecules into aqueous solution to a certain extent and prevents cellulose macromolecules from associating. (13)C NMR spectra of the cellulose solution show that this novel mixture is a direct solvent. Optical microscopy and CP MAS (13)C NMR were used to study the process of dissolution. The results reveal that cellulose is dissolved completely and that cellulose I (cotton linter) first changes to amorphous cellulose chains in solution, and then to cellulose II during regeneration. Moreover, a new, more effective dissolution method is proposed, as confirmed by dynamic rheology measurements.

Rapid dissolution of cellulose in LiOH/urea and NaOH/urea aqueous solutions

Rapid dissolution of cellulose in LiOH/urea and NaOH/urea aqueous solutions was studied systematically. The dissolution behavior and solubility of cellulose were evaluated by using (13)C NMR, optical microscopy, wide-angle X-ray diffraction (WAXD), FT-IR spectroscopy, DSC, and viscometry. The experiment results revealed that cellulose having viscosity-average molecular weight ((overline) M eta) of 11.4 x 104 and 37.2 x 104 could be dissolved, respectively, in 7% NaOH/12% urea and 4.2% LiOH/12% urea aqueous solutions pre-cooled to -10 degrees C within 2 min, whereas all of them could not be dissolved in KOH/urea aqueous solution. The dissolution power of the solvent systems was in the order of LiOH/urea > NaOH/urea >> KOH/urea aqueous solution. The results from DSC and (13)C NMR indicated that LiOH/urea and NaOH/urea aqueous solutions as non-derivatizing solvents broke the intra- and inter-molecular hydrogen bonding of cellulose and prevented the approach toward each other of the cellulose molecules, leading to the good dispersion of cellulose to form an actual solution.