Oral prosthetic microbiology: aspects related to the oral microbiome, surface properties, and strategies for controlling biofilms

Application of organoselenium in inhibiting Candida albicans biofilm adhesion on 3D printed denture base material

PURPOSE

Denture Stomatitis, a chronic mucosal inflammation associated with Candida albicans, is common among denture wearers. Several health conditions have been linked to chronic Candida infections. The complex, multifactorial nature of denture stomatitis requires the continuous pursuit of effective long-term solutions. The present in vitro study investigated the effect of incorporating organoselenium into 3D-printed denture base resin on C. albicans adhesion and biofilm formation.

MATERIALS AND METHODS

Thirty disks were fabricated using 3D-printed denture base resin and assigned to three experimental groups (10/group): disks without organoselenium (control), disks with 0.5% organoselenium (0.5%SE), and disks with 1% organoselenium (1%SE). Each disk was incubated with approximately 1 × 106 cells/mL of C. albicans for 48 h. Microbial viability (CFU/mL) was quantified by the spread plate method, while Confocal laser scanning microscopy and scanning electron microscope were performed for quantifying the biofilm thickness and examining biofilm morphology, respectively. Data were analyzed using One-way ANOVA with Tukey's multiple comparisons test.

RESULTS

CFU/mL was significantly (p < 0.05) higher in Control when compared with 0.5%SE and 1%SE, but no significant difference between 0.5%SE and 1%SE. A similar trend was observed with biofilm thickness except that there was no significant difference between the Control and 0.5%SE. There was C. albicans biofilm adhesion on the Control disks, with yeast cells and hyphae formation, whereas on 0.5%SE and 1%SE, there was inhibition of yeast cells transition to hyphae formation.

CONCLUSIONS

Incorporation of organoselenium into 3D-printed denture base resin was effective in reducing C. albicans biofilm formation and growth on denture base material.

Characterization of pathogenic microbiome on removable prostheses with different levels of cleanliness using 2bRAD-M metagenomic sequencing

Background

The microbiomes on the surface of unclean removable prostheses are complex and yet largely underexplored using metagenomic sequencing technology.

Objectives

To characterize the microbiome of removable prostheses with different levels of cleanliness using Type IIB Restriction-site Associated DNA for Microbiome (2bRAD-M) sequencing and compare the Microbial Index of Pathogenic Bacteria (MIP) between clean and unclean prostheses.

Materials and Methods

Ninety-seven removable prostheses were classified into 'clean' and 'unclean' groups. All prosthesis plaque samples underwent 2bRAD metagenomic sequencing to characterize the species-resolved microbial composition. MIPs for clean and unclean prostheses were calculated based on the sum of the relative abundance of pathogenic bacteria in a microbiome using a reference database that contains opportunistic pathogenic bacteria and disease-associated information.

Results

Beta diversity analyses based on Jaccard qualitative and Bray-Curtis quantitative distance matrices identified significant differences between the two groups (p < 0.05). There was a significant enrichment of many pathogenic bacteria in the unclean prosthesis group. The MIP for unclean prostheses (0.47 ± 0.25) was significantly higher than for clean prostheses (0.37 ± 0.29), p = 0.029.

Conclusions

The microbial community of plaque samples from 'unclean' prostheses demonstrated compositional differences compared with 'clean' prostheses. In addition, the pathogenic microbiome in the 'unclean' versus 'clean' group differed.

Action of chitosan-based solutions against a model four-species biofilm formed on cobalt-chromium and acrylic resin surfaces

OBJECTIVE

To evaluate the anti-biofilm action of chitosan, nanoparticulate chitosan, and denture cleanser Nitradine™ against biofilms comprising Candida albicans, Candida glabrata, Staphylococcus aureus, and Streptococcus mutans.

BACKGROUND

Biofilm removal from removable partial dentures (RPD) is important for success in prosthetic rehabilitation.

MATERIALS AND METHODS

The anti-biofilm action of the experimental chitosan-based solutions and Nitradine™ was evaluated on acrylic resin and cobalt-chromium alloy through assessing cell viability, cell metabolism, residual aggregated biofilm, and extracellular polymeric substance and biofilm morphology.

RESULTS

Only chitosan reduced the viability of C. albicans on cobalt-chromium alloy surface, by 98% (a 1.7 log10 reduction in cfu). Chitosan-based solutions neither promoted substantial alteration of the metabolic activity of the four-species biofilm nor reduced the amount of the aggregated biofilm. After immersion in chitosan and nanoparticulate chitosan, viable microorganisms and extracellular polymeric substances distributed over the entire specimens' surfaces were observed. Nitradine™ reduced the viability and metabolic activity of biofilm grown on both surfaces, but it did not remove all aggregated biofilm and extracellular polymeric substances. After immersion in Nitradine™, approximately 35% of the specimens' surfaces remained covered by aggregated biofilm, mainly composed of dead cells.

CONCLUSION

Although chitosan and Nitradine™ promoted changes in the viability of microorganisms, neither solution completely removed the four-species biofilm from the Co-Cr and acrylic resin surfaces. Thus, isolated use of hygiene solutions is not indicated for biofilm control on RPDs; this requires complementary mechanical removal.

Trans-mucosal platforms for dental implants: Strategies to induce muco-integration and shield peri-implant diseases

OBJECTIVES

Trans-mucosal platforms connecting the bone-anchored implants to the prosthetic teeth are essential for the success of oral rehabilitation in implant dentistry. This region promotes a challenging environment for the successfulness of dental components due to the transitional characteristics between soft and hard tissues, the presence of bacteria, and mechanical forces. This review explored the most current approaches to modify trans-mucosal components in terms of macro-design and surface properties.

METHODS

This critical review article revised intensely the literature until July 2023 to demonstrate, discuss, and summarize the current knowledge about marketable and innovative trans-mucosal components for dental implants.

RESULTS

A large number of dental implant brands have promoted the development of several implant-abutment designs in the clinical market. The progress of abutment designs shows an optimistic reduction of bacteria colonization underlying the implant-abutment gap, although, not completely inhibited. Fundamental and preclinical studies have demonstrated promising outcomes for altered-surface properties targeting antibacterial properties and soft tissue sealing. Nanotopographies, biomimetic coatings, and antibiotic-release properties have been shown to be able to modulate, align, orient soft tissue cells, and induce a reduction in biofilm formation, suggesting superior abilities compared to the current trans-mucosal platforms available on the market.

SIGNIFICANCE

Future clinical implant-abutments show the possibility to reduce peri-implant diseases and fortify soft tissue interaction with the implant-substrate, defending the implant system from bacteria invasion. However, the absence of technologies translated to commercial stages reveals the need for findings to "bridge the gap" between scientific evidences published and applied science in the industry.

Nano-scaled surfaces and sustainable-antibiotic-release from polymeric coating for application on intra-osseous implants and trans-mucosal abutments

Multifunctional surfaces may display the potential to accelerate and promote the healing process around dental implants. However, the initial cellular biocompatibility, molecular activity, and the release of functionalized molecules from these novel surfaces require extensive investigation for clinical use. Aiming to develop and compare innovative surfaces for application in dental implants, the present study utilized titanium disks, which were treated and divided into four groups: machined (Macro); acid-etched (Micro); anodized-hydrophilic surface (TNTs); and anodized surface coated with a rifampicin-loaded polymeric layer (poly(lactide-co-glycolide), PLGA) (TNTsRIMP). The samples were characterized regarding their physicochemical properties and the cumulative release of rifampicin (RIMP), investigated at different pH values. Additionally, differentiated osteoblasts from mesenchymal cells were used for cell viability and qRT-PCR analysis. Antibacterial properties of each surface treatment were investigated against Staphylococcus epidermidis. TNTsRIMP demonstrated controlled drug release for up to 7 days in neutral pH environments. Osteogenic cell cultures indicated that all the evaluated surfaces showed biocompatibility. The TNTs group revealed up-regulated values for bone-related gene quantification in 7 days, followed by the TNTsRIMP group. Furthermore, the antibiotic-functionalized surface revealed effectiveness to inhibit S. epidermidis and stimulate promising conditions for osteogenic cell behavior. Characteristics such as nanomorphology and hydrophilicity were determinants for the up-regulated quantification of osteogenic biomarkers related to early bone maturation, encouraging application in intra-osseous implant surfaces; in addition, antibiotic-functionalized surfaces demonstrated significant higher antibacterial properties compared to the other groups. Our findings suggest that polymeric-antibiotic-loaded coating might be applied for the prevention of early infections, favoring its application in multifunctional surfaces for intra- and/or trans-mucosal components of dental implants, while, hydrophilic nanotextured surfaces promoted optimistic properties to stimulate early bone-related cell responses, favoring its application in bone-anchored surfaces.

Bacterial Biofilm Formation on Biomaterials and Approaches to Its Treatment and Prevention

Bacterial biofilms can cause widespread infection. In addition to causing urinary tract infections and pulmonary infections in patients with cystic fibrosis, biofilms can help microorganisms adhere to the surfaces of various medical devices, causing biofilm-associated infections on the surfaces of biomaterials such as venous ducts, joint prostheses, mechanical heart valves, and catheters. Biofilms provide a protective barrier for bacteria and provide resistance to antimicrobial agents, which increases the morbidity and mortality of patients. This review summarizes biofilm formation processes and resistance mechanisms, as well as the main features of clinically persistent infections caused by biofilms. Considering the various infections caused by clinical medical devices, we introduce two main methods to prevent and treat biomaterial-related biofilm infection: antibacterial coatings and the surface modification of biomaterials. Antibacterial coatings depend on the covalent immobilization of antimicrobial agents on the coating surface and drug release to prevent and combat infection, while the surface modification of biomaterials affects the adhesion behavior of cells on the surfaces of implants and the subsequent biofilm formation process by altering the physical and chemical properties of the implant material surface. The advantages of each strategy in terms of their antibacterial effect, biocompatibility, limitations, and application prospects are analyzed, providing ideas and research directions for the development of novel biofilm infection strategies related to therapeutic materials.

Potential Impact of Prosthetic Biomaterials on the Periodontium: A Comprehensive Review

The success of a prosthetic treatment is closely related to the periodontal health of the individual. The aim of this article was to review and present the importance of prosthetic restorative materials on the condition of the periodontium, the changes that occur in the composition of the subgingival microbiota and the levels of inflammatory markers in gingival crevicular fluid. Articles on the influence of different prosthetic restorative materials on subgingival microbiota and proinflammatory cytokines were searched for using the keywords "prosthetic biomaterials", "fixed prosthesis", "periodontal health", "subgingival microbiota", "periodontal biomarkers" and "gingival crevicular fluid" in PubMed/Medline, Science Direct, Scopus and Google Scholar. The type of material used for prosthesis fabrication together with poor marginal and internal fit can result in changes in the composition of the subgingival microbiota, as well as increased accumulation and retention of dentobacterial plaque, thus favoring the development of periodontal disease and prosthetic treatment failure. Biological markers have helped to understand the inflammatory response of different prosthetic materials on periodontal tissues with the main purpose of improving their clinical application in patients who need them. Metal-free ceramic prostheses induce a lower inflammatory response regardless of the fabrication method; however, the use of CAD/CAM systems is recommended for their fabrication. In addition, it is presumed that metal-ceramic prostheses cause changes in the composition of the subgingival microbiota producing a more dysbiotic biofilm with a higher prevalence of periodontopathogenic bacteria, which may further favor periodontal deterioration.

In vitro antimicrobial effects of chitosan on microcosm biofilms of oral candidiasis

OBJECTIVE

This study assessed the effects of chitosan (CS) on microcosm biofilms derived from saliva of patients with Candida-associated denture stomatitis.

METHODS

Five removable denture wearers with denture stomatitis were included in the study. The minimum inhibitory concentration (MIC) of CS against clinical isolates of Candida albicans was determined according to the broth microdilution method. Pooled saliva from the donors was used as an inoculum for the formation of biofilms, which were developed during 72 h on acrylic surfaces in the Amsterdam Active Attachment model. The biofilms were then treated with different concentrations of CS, and the antibiofilm effects were evaluated through the quantification of colony-forming units (CFUs), total biomass (TB), metabolic activity (MA), lactic acid production (LAP), and cell viability (by confocal laser scanning microscopy). Chlorhexidine, miconazole, and nystatin were tested as positive controls, while the negative control (NC) was the untreated biofilm. Data were analyzed by 1-way ANOVA and Fischer LSD's post hoc test (α=0.05).

RESULTS

MIC values of CS ranged from 500 to 800 µg/mL. For CFUs, 2500 µg/mL CS was the most effective treatment in reducing total anaerobes, mutans streptococci, and Lactobacillus spp., significantly differing from the controls. For C. albicans CFUs, CS and positive controls did not differ from each other but led to significant reductions compared to NC. Regarding TB, MA, LAP, and cell viability, 2500 µg/mL CS promoted the greatest reductions compared to NC.

CONCLUSION

CS has similar or superior effects to conventional active principles on important parameters of oral candidiasis microcosm biofilms.

CLINICAL RELEVANCE

The antibiofilm effects of CS show that this compound has great potential to improve the clinical condition of denture stomatitis patients, and formulations containing this natural polymer could be useful for controlling oral candidiasis.

In vitro study of surface properties and microbial adhesion of various dental polymers fabricated by different manufacturing techniques after thermocycling

OBJECTIVES

The study aims to investigate surface properties and microbial adhesion of various dental polymers fabricated by different manufacturing techniques before and after thermocycling.

MATERIALS AND METHODS

The following six materials were used to fabricate disk-shaped specimens: conventional denture polymer (Vertex Acrylic Resin, VAR), CAD/CAM denture polymer (Organic PMMA eco Pink, OP), conventional temporary polymer (Protemp™ 4, PT), CAD/CAM temporary polymer (Die Material, DM), conventional denture framework polymer (BioHPP, PB), and CAD/CAM denture framework polymer (breCAM.BioHPP, CB). The specimens were tested before and after thermocycling (5000 and 10,000 cycles, 5 °C/55 °C). Surface roughness (SR), hydrophobicity, and surface topography were determined by profilometry, water contact angle, and scanning electron microscopy (SEM). Then specimens were incubated with Staphylococcus aureus, Streptococcus mutans, and Candida albicans for 24 h, respectively. Microbial adhesion was assessed using colony-forming unit counts, XTT assay, and SEM.

RESULTS

SR and hydrophobicity of VAR group were higher than that of OP group. S. aureus and C. albicans adhesion on VAR and PT groups were higher than that on OP and DM groups, respectively. There was no difference in surface properties and microbial adhesion between PB and CB groups. After thermocycling, SR (expect OP group) of all materials increased and hydrophobicity decreased, and the amount and activity of S. aureus and C. albicans adhesion also increased. The adhesion of S. aureus and C. albicans showed a moderate positive correlation with SR, independent of hydrophobicity.

CONCLUSIONS

CAD/CAM denture polymers and temporary polymers showed less S. aureus and C. albicans adhesion when compared to conventional ones, which were mainly affected by surface roughness, independent of hydrophobicity. Thermocycling could increase surface roughness, decrease hydrophobicity, and affect microbial adhesion of the materials.

CLINICAL SIGNIFICANCE

CAD/CAM dental polymers may be a better choice for the manufacture of temporary restorations and dentures to reduce microbial adhesion.

The denture microbiome in health and disease: an exploration of a unique community

The United Nations suggests the global population of denture wearers (an artificial device that acts as a replacement for teeth) is likely to rise significantly by the year 2050. Dentures become colonized by microbial biofilms, the composition of which is influenced by complex factors such as patient’s age and health, and the nature of the denture material. Since colonization (and subsequent biofilm formation) by some micro‐organisms can significantly impact the health of the denture wearer, the study of denture microbiology has long been of interest to researchers. The specific local and systemic health risks of denture plaque are different from those of dental plaque, particularly with respect to the presence of the opportunist pathogen Candida albicans and various other nonoral opportunists. Here, we reflect on advancements in our understanding of the relationship between micro‐organisms, dentures, and the host, and highlight how our growing knowledge of the microbiome, biofilms, and novel antimicrobial technologies may better inform diagnosis, treatment, and prevention of denture‐associated infections, thereby enhancing the quality and longevity of denture wearers.

Extended Post-Curing Light Exposure and Sandblasting Effects on Surface Hydrophobicity of 3D-Printed Denture Base Resin

This in vitro study evaluated the surface hydrophobicity of 3D-printed denture base resin exposed to either an extended post-curing light exposure time or a sandblasting procedure. MATERIALS AND METHODS: Disk-shaped samples (diameter × height: 10 mm × 3 mm) were 3D-printed with stereolithography SLA technology using the denture-base resin. Samples were divided into three groups: control, extended UV-post-curing, and sandblasted. The surface roughness parameters for each group were calculated, and the surface hydrophobicity was evaluated by measuring the drop contact angle. Analysis was done using the T-test; significance was when p < 0.05. RESULTS: The comparison of surface roughness parameters showed significant differences between the control group and the sandblasted group (Sa: p = 0.001, Sz: p < 0.001, Str: p < 0.001, Spc: p = 0.044) as well as between the extended-cure group and the sandblasted group (Sa: p = 0.006, Sz: p < 0.001, Str: p < 0.001, Spc: p = 0.036) except for the Sdr measures. The surface hydrophobicity was also statistically lower in the sandblasted group compared to both the control and extended curing groups (p < 0.001). CONCLUSION: The sandblasting procedure created a less hydrophobic surface of the 3D-printed denture base resin, and the altered surface roughness could be a contributor to this observation.