Removal of lead and phosphate ions from aqueous solutions by organo-smectite

Modification of Bentonite with Cationic and Nonionic Surfactants: Structural and Textural Features

Surfactant-modified clay minerals are known for their good sorption properties of both organic and inorganic compounds from aqueous solutions. However, the current knowledge regarding the effect of both cationic and nonionic surfactants on the properties of bentonite is still insufficient. Bentonite, with montmorillonite as the base clay, was modified with hexadecethyltrimethylammonium bromide (a cationic surfactant) in the amount of 1.0 cation exchange capacity (CEC) of bentonite and varying concentrations of t-octylphenoxypolyethoxyethanol (Triton X-100, a nonionic surfactant). We aimed to improve the understanding of the effect of nonionic and cationic surfactants on clay minerals. The modified bentonites were characterized by X-ray diffraction (XRD), thermogravimetric analysis/differential thermal analysis (TG/DTA), Fourier transform infrared spectrometry (FTIR), field emission scanning electron microscopy (SEM) and specific surface area and pore volume (BET). According to our results, the presence of a cationic surfactant significantly increased the amount of the adsorbed nonionic surfactant. Moreover, an increase in the concentration of nonionic surfactants is also associated with an increase in the effectiveness of the modification process. Our results indicate that the amount of nonionic surfactant used has a significant effect on the properties of the obtained hybrid material. Modification of bentonite with a nonionic surfactant did not cause an expansion of the interlayer space of smectite, regardless of the presence of a cationic surfactant. The modification process was found to significantly decrease the specific surface area of bentonite. Improvement of hydrophobic properties and thermal stability was also observed.

Removal of Heavy Metals and Metalloids from Water Using Drinking Water Treatment Residuals as Adsorbents: A Review

Heavy metal contamination is one of the most important environmental issues. Therefore, appropriate steps need to be taken to reduce heavy metals and metalloids in water to acceptable levels. Several treatment methods have been developed recently to adsorb these pollutants. This paper reviews the ability of residuals generated as a by-product from the water treatment plants to adsorb heavy metals and metalloids from water. Water treatment residuals have great sorption capacities due to their large specific surface area and chemical composition. Sorption capacity is also affected by sorption conditions. A survey of the literature shows that water treatment residuals may be a suitable material for developing an efficient adsorbent for the removal of heavy metals and metalloids from water.

Sorption of Molybdates and Tungstates on Functionalized Montmorillonites: Structural and Textural Features

Montmorillonite—the most popular mineral of the smectite group—has been recognized as a low-cost, easily available mineral sorbent of heavy metals and other organic and inorganic compounds that pollute water. The aim of this work was to determine the sorption mechanism and to identify the reaction products formed on the surface of montmorillonite and organo-montmorillonite after sorption of molybdates (Mo(VI)) and tungstates (W(VI)). Montmorillonites are often modified to generate a negative charge on the surface. The main objective of the study was to investigate and compare the features of Na-montmorillonite (Na-M), montmorillonite modified with dodecyl trimethyl ammonium bromide (DDTMA-M), and montmorillonite modified with didodecyl dimethyl ammonium bromide (DDDDMA-M) before and after sorption experiments. The material obtained after sorption was studied by X-ray diffraction (XRD), Fourier-transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), and X-ray photoelectron spectroscopy (XPS). The XRD pattern showed the presence of a new crystallic phase in the sample that was observed under an SEM as an accumulation of crystals. The FTIR spectra showed bands related to Mo–O and W–O vibration (840 and 940 cm⁻¹, respectively). The obtained results suggest that molybdenum(VI) and tungsten(VI) ions sorb onto the organo-montmorillonite in the form of alkylammonium molybdates and tungstates.

Innovative root-end filling materials based on calcium-silicates and calcium-phosphates

This in vitro study evaluated the apical sealing ability, bioactivity and biocompatibility of an experimental calcium silicate-based and two light-curing calcium silicate/calcium-phosphate cements as potential root end filling materials. A calcium silicate Portland-based (Control PC), an experimental calcium silicate (Exp. PC) and two light-curing cements (LC-CaP; LC-Si/CaP) were assessed for their alkalinising activity (pH) and biocompatibility. Single-rooted human canines were endodontically treated, filled with gutta-percha and finally submitted to apicoectomy. Root end fillings were performed using all tested cements, and their apical sealing ability was evaluated up to 4 weeks of immersion in simulated body fluid (SBF). The mineral precipitation at the apical region and the cement adaptation to root dentine were also evaluated through non-destructive optical microscopy both at 24 h and after prolonged water storage (four week). LC-CaP and LC-Si/CaP had neutral pH, the greatest sealing ability (24 h) and excellent cytocompatibility. The Exp. PC cement presented sealing ability after two and four weeks, as well as biocompatibility after four and seven days, similar to LC-CaP and LC-Si/CaP. The control PC cement showed the lowest sealing ability and the greatest cytotoxicity. Mineral precipitation was observed in all groups, while some differences were seen in terms of cement adaptation along the root canal dentine walls. The experimental light-curable cements as well as the experimental PC might be suitable root end filling materials with appropriate (in vitro) sealing ability, biocompatibility and aptitude to induce mineral precipitation.