Membrane bioreactors troubleshooting through the preparation of a high antifouling PVDF ultrafiltration mixed-matrix membrane blended with O-carboxymethyl chitosan-Fe3O4 nanoparticles

Rapid Surface Modification of Ultrafiltration Membranes for Enhanced Antifouling Properties

In this work, several ultrafiltration (UF) membranes with enhanced antifouling properties were fabricated using a rapid and green surface modification method that was based on the plasma-enhanced chemical vapor deposition (PECVD). Two types of hydrophilic monomers—acrylic acid (AA) and 2-hydroxyethyl methacrylate (HEMA) were, respectively, deposited on the surface of a commercial UF membrane and the effects of plasma deposition time (i.e., 15 s, 30 s, 60 s, and 90 s) on the surface properties of the membrane were investigated. The modified membranes were then subjected to filtration using 2000 mg/L pepsin and bovine serum albumin (BSA) solutions as feed. Microscopic and spectroscopic analyses confirmed the successful deposition of AA and HEMA on the membrane surface and the decrease in water contact angle with increasing plasma deposition time strongly indicated the increase in surface hydrophilicity due to the considerable enrichment of the hydrophilic segment of AA and HEMA on the membrane surface. However, a prolonged plasma deposition time (>15 s) should be avoided as it led to the formation of a thicker coating layer that significantly reduced the membrane pure water flux with no significant change in the solute rejection rate. Upon 15-s plasma deposition, the AA-modified membrane recorded the pepsin and BSA rejections of 83.9% and 97.5%, respectively, while the HEMA-modified membrane rejected at least 98.5% for both pepsin and BSA. Compared to the control membrane, the AA-modified and HEMA-modified membranes also showed a lower degree of flux decline and better flux recovery rate (>90%), suggesting that the membrane antifouling properties were improved and most of the fouling was reversible and could be removed via simple water cleaning process. We demonstrated in this work that the PECVD technique is a promising surface modification method that could be employed to rapidly improve membrane surface hydrophilicity (15 s) for the enhanced protein purification process without using any organic solvent during the plasma modification process.

A novel polyethersulfone/modified activated carbon fiber composite membrane: potential for removal micropollutants from water under the electric field

This study aimed to develop a novel composite membrane based on polyethersulfone (PES) and modified activated carbon fibers (ACFs) to remove of sulfamethoxazole (SMZ) from water. The modification of ACFs was conducted by using acid, Fe, and Mn and was confirmed by Fourier transform infrared spectroscopy (FT-IR), energy dispersive X-ray spectroscopy (EDS), and water contact angle measurement. Later on, the composite membranes were prepared using PES (9 wt%), N-N-dimethylacetamide (DMAc) (75 wt%), polyethylene pyrrolidone (PVP) (5 wt%), anhydrous lithium chloride (LiCl) (1 wt%), and various types of modified ACFs (0.8 wt%) as additives. It was found that the contact angle of the membrane decreased by more than 20°, and the zeta potential decreased by more than 10 mV. ACF modified by Fe was used as an admixture, membrane obtained the high comprehensive performance. Especially bovine serum albumin (BSA) rejection rate and flux recovery ratio (FRR) reached 98.8% and 98.4%, respectively. And the removal rates of SMZ increased by 24.6% under the electric field. The degradation products were detected by high-performance liquid chromatography/mass spectrometry (HPLC/MS). Based on this result, the possible degradation pathways of SMZ are proposed.

Agricultural and Biomedical Applications of Chitosan-Based Nanomaterials

Chitosan has emerged as a biodegradable, nontoxic polymer with multiple beneficial applications in the agricultural and biomedical sectors. As nanotechnology has evolved as a promising field, researchers have incorporated chitosan-based nanomaterials in a variety of products to enhance their efficacy and biocompatibility. Moreover, due to its inherent antimicrobial and chelating properties, and the availability of modifiable functional groups, chitosan nanoparticles were also directly used in a variety of applications. In this review, the use of chitosan-based nanomaterials in agricultural and biomedical fields related to the management of abiotic stress in plants, water availability for crops, controlling foodborne pathogens, and cancer photothermal therapy is discussed, with some insights into the possible mechanisms of action. Additionally, the toxicity arising from the accumulation of these nanomaterials in biological systems and future research avenues that had gained limited attention from the scientific community are discussed here. Overall, chitosan-based nanomaterials show promising characteristics for sustainable agricultural practices and effective healthcare in an eco-friendly manner.

Polymeric Nanocomposites of Iron–Oxide Nanoparticles (IONPs) Synthesized Using Terminalia chebula Leaf Extract for Enhanced Adsorption of Arsenic(V) from Water

This study demonstrates the ecofriendly synthesis of iron–oxide nanoparticles (IONPs) and their stabilization with polymers, i.e., chitosan (C) and polyvinyl alcohol (PVA)–alginate (PA), along with a further investigation for the removal of arsenic(As(V)) from water. IONPs with an average diameter of less than 100 nm were prepared via a green synthesis process using an aqueous leaf extract of Terminalia chebula. Batch experiments were conducted to compare the removal efficiency of As(V) by these adsorbents. Factors such as pH and adsorbent dosages significantly affected the removal of arsenate As(V) by IONPs and polymer-supported reactive IONPs. Several adsorption kinetic models, such as pseudo first-order, and pseudo second-order Langmuir and Freundlich isotherms, were used to describe the adsorption of As(V). The removal of As(V) by IONPs follows the Langmuir adsorption isotherm. The highest monolayer saturation adsorption capacity as obtained from the Langmuir adsorption isotherm for IONPs was 28.57 mg/g. As(V) adsorption by polymer-supported IONPs best fit the Freundlich model, and maximum adsorption capacities of 34.4 mg/g and 40.3 mg/g were achieved for chitosan- and PVA–alginate-supported IONPs, respectively. However, among these absorbents, PVA–alginate-supported IONPs were found to be more effective than the other adsorbents in terms of adsorption, stability, and reusability.