The effects of manufacturing tolerances and assembly force on the volumetric wear at the taper junction in modular total hip arthroplasty

Mix and Match Use of Revision Universal Head-Neck Adapters in Hip Arthroplasty: A Complications and Survival Analysis of 306 Cases

BACKGROUND

Outcomes and safety of "mix and match" in total hip arthroplasty (THA) using universal head-neck adapters (UHNA) are a matter of ongoing discussion and concern due to legal affairs. This study aimed at analyzing the "mix and match" use of UHNA and evaluating complication and reoperation rates, possible risk factors, and the implant's survival.

METHODS

A total of 306 patients treated with THA (94.1% revisions) using a UHNA at our institution between 2006 and 2022 were identified and included. Diagnoses, comorbidities, implants, and UHNA specifications were retrospectively recorded. Outcomes, complications, and survival analyses were evaluated, taking into account various possible risk factors.

RESULTS

There were 19.9% of the 306 included cases (58.5% women; median age 74 years; median follow-up 57 months) that had at least 1 complication. There were 43 patients (14.1%) who had to receive ≥1 rerevision surgery. The most common complication was postoperative recurrent dislocation (n = 27, 8.8%). There was one case of a prosthetic stem-neck fracture that was registered. Statistically significant risk factors for postoperative recurrent dislocations and postoperative aseptic loosening were, respectively, dislocation as an indication for UHNA implantation (P < .001) and oversized neck lengths (≥2XL; P = .004). The overall revision-free survival was 92% after 1 year and 82% at ten years. Statistically significant better survival rates were registered in patients ≥60 years old, who had fewer comorbidities (<2), and normal neck lengths (S to XL).

CONCLUSIONS

The results of this study underline the overall safety of UHNA use in THA through "mix and match." Only one case of a stem-neck fracture was identified. The highlighted risk factors for failure must be kept in mind during the decision-making process with patients.

Advancement in total hip implant: a comprehensive review of mechanics and performance parameters across diverse novelties

The UK's National Joint Registry (NJR) and the American Joint Replacement Registry (AJRR) of 2022 revealed that total hip replacement (THR) is the most common orthopaedic joint procedure. The NJR also noted that 10-20% of hip implants require revision within 1 to 10 years. Most of these revisions are a result of aseptic loosening, dislocation, implant wear, implant fracture, and joint incompatibility, which are all caused by implant geometry disparity. The primary purpose of this review article is to analyze and evaluate the mechanics and performance factors of advancement in hip implants with novel geometries. The existing hip implants can be categorized based on two parts: the hip stem and the joint of the implant. Insufficient stress distribution from implants to the femur can cause stress shielding, bone loss, excessive micromotion, and ultimately, implant aseptic loosening due to inflammation. Researchers are designing hip implants with a porous lattice and functionally graded material (FGM) stems, femur resurfacing, short-stem, and collared stems, all aimed at achieving uniform stress distribution and promoting adequate bone remodeling. Designing hip implants with a porous lattice FGM structure requires maintaining stiffness, strength, isotropy, and bone development potential. Mechanical stability is still an issue with hip implants, femur resurfacing, collared stems, and short stems. Hip implants are being developed with a variety of joint geometries to decrease wear, improve an angular range of motion, and strengthen mechanical stability at the joint interface. Dual mobility and reverse femoral head-liner hip implants reduce the hip joint's dislocation limits. In addition, researchers reveal that femoral headliner joints with unidirectional motion have a lower wear rate than traditional ball-and-socket joints. Based on research findings and gaps, a hypothesis is formulated by the authors proposing a hip implant with a collared stem and porous lattice FGM structure to address stress shielding and micromotion issues. A hypothesis is also formulated by the authors suggesting that the utilization of a spiral or gear-shaped thread with a matched contact point at the tapered joint of a hip implant could be a viable option for reducing wear and enhancing stability. The literature analysis underscores substantial research opportunities in developing a hip implant joint that addresses both dislocation and increased wear rates. Finally, this review explores potential solutions to existing obstacles in developing a better hip implant system.

The effect of trunnionosis on the risk of re-revision following femoral head exchange in hip arthroplasty

BACKGROUND

Fretting corrosion at modular junctions contributes to arthroplasty failure. Currently, no evidence-based guidelines are available regarding the acceptable level of trunnion corrosion that can occur in vivo. We aimed to examine the relationship between trunnion corrosion and risk of re-revision to assist surgeons with intraoperative decision making.

METHOD

Grading by 3 independent examiners of revised and re-revised head components was performed using a modified Goldberg corrosion scale. Samples were separated into low-grade (LG) and high-grade (HG) corrosion. Mechanical testing determined the relationship between corrosion severity and pull-off strength at the head-stem junction.

RESULTS

529 retrieved femoral heads were analysed. A positive association was detected between males and HG corrosion (OR 2.07; 95% CI, 1.45-2.94; p < 0.001). No difference between the survivorship of LG and HG heads was detected (p-value = 0.247). In the re-revised sample, the first implant had a time in situ that was on average 7.97 years longer (95% CI, 5.4-10.6) than that of the subsequent re-revised femoral head. Severe corrosion on the first head was associated with a 37.5 (95% CI, 4.00-1944) fold increase of HG on the subsequent head (p < 0.001). Femoral disassembly force had a positive correlation with stem taper corrosion grade (p = 0.001).

CONCLUSIONS

A well-fixed stem with corrosion may remain in situ.

Revealing the composite fretting-corrosion mechanisms of Ti6Al4V alloy against zirconia-toughened alumina ceramic in simulated body fluid

The composite fretting-corrosion damage due to combinations of radial, tangential, rotational, and other fretting causes local adverse tissue reactions and failure of artificial joints. Previous studies have mainly focused on the single fretting mode, while ignoring the coupled effects of multimode fretting. The fretting-corrosion mechanisms between the components are not yet fully understood. In this study, the tangential-radial composite fretting was realized by applying a normal alternating load to the tangential fretting. The composite fretting corrosion behavior of zirconia toughened alumina ceramic/Ti6Al4V alloy used for the head-neck interface of an artificial hip joint under simulated body fluid was investigated. The effects of displacement and alternating load amplitude were considered. The alternating load amplitude was given by the maximum normal load and minimum normal load ratio R. The results showed that the composite fretting damage mechanisms of this pair were mainly abrasion and tribocorrosion. Cracking also existed under large displacement. The effect of alternating load on fretting corrosion was found to be mainly caused by changes in the contact area and instantaneous contact state. In addition, the alternating load during the composite fretting promoted the formation of the three-body layer in the contact area. A decrease in load ratio caused fretting to change from gross to partial slip. In the case of small displacement, the load ratio had little effect on the friction work or wear scar profile. The corrosion rate of materials and the concentration of metal ions released into the solution increased as load ratio decreased. In cases of large and medium displacement, load ratio reduction increased the friction work and expanded the wear scar. The reduction in load ratio also caused the corrosion rate of the material to increase and then decrease, and the metal ion concentration decreased.

Decomposition of micromotion at the head-neck interface in total hip arthroplasty during walking

Fretting corrosion as one of the leading causes for failure of modular hip prostheses has been associated with micromotion at head-neck taper junction. Decomposition of micromotion is helpful to promote the development of more realistic experiments investigating failure mechanisms of the head-neck junction in total hip arthroplasty. The aim of this study was to decompose the complex three-dimensional micromotion at the head-neck junction into multiple fundamental modes, including three translational and three rotational components. A three-dimensional finite element model composed of head-neck junction, liner and acetabular cup with a typical 12/14 taper size, as well as the taper mismatch of -4', was developed during walking. The analysis was divided into three procedures: a) the assembly simulation of the head and neck during surgery, b) verification with a simplified axisymmetric model, and c) three-dimensional modelling under normal walking. This study revealed that the main forms of micromotion contained circumferential, longitudinal micromotion and longitudinal rolling toggling, and were closely related to the state of motion. The maximum translational micromotion was predicted to be 10.9 μm during the walking gait, with the predominant modes of the circumferential translation of 9.6 μm, the longitudinal translation of 5.5 μm and the longitudinal rotation of 0.29° along the taper junction. These findings may provide design considerations for further experimental testing about fretting and facilitate the understanding of the fretting mechanisms in hip prostheses.

Design and Performance Evaluation of a Novel Spiral Head-Stem Trunnion for Hip Implants Using Finite Element Analysis

With an expectation of an increased number of revision surgeries and patients receiving orthopedic implants in the coming years, the focus of joint replacement research needs to be on improving the mechanical properties of implants. Head-stem trunnion fixation provides superior load support and implant stability. Fretting wear is formed at the trunnion because of the dynamic load activities of patients, and this eventually causes the total hip implant system to fail. To optimize the design, multiple experiments with various trunnion geometries have been performed by researchers to examine the wear rate and associated mechanical performance characteristics of the existing head-stem trunnion. The objective of this work is to quantify and evaluate the performance parameters of smooth and novel spiral head-stem trunnion types under dynamic loading situations. This study proposes a finite element method for estimating head-stem trunnion performance characteristics, namely contact pressure and sliding distance, for both trunnion types under walking and jogging dynamic loading conditions. The wear rate for both trunnion types was computed using the Archard wear model for a standard number of gait cycles. The experimental results indicated that the spiral trunnion with a uniform contact pressure distribution achieved more fixation than the smooth trunnion. However, the average contact pressure distribution was nearly the same for both trunnion types. The maximum and average sliding distances were both shorter for the spiral trunnion; hence, the summed sliding distance was approximately 10% shorter for spiral trunnions than that of the smooth trunnion over a complete gait cycle. Owing to a lower sliding ability, hip implants with spiral trunnions achieved more stability than those with smooth trunnions. The anticipated wear rate for spiral trunnions was 0.039 mm³, which was approximately 10% lower than the smooth trunnion wear rate of 0.048 mm³ per million loading cycles. The spiral trunnion achieved superior fixation stability with a shorter sliding distance and a lower wear rate than the smooth trunnion; therefore, the spiral trunnion can be recommended for future hip implant systems.

Interaction of surface topography and taper mismatch on head-stem modular junction contact mechanics during assembly in modern total hip replacement

Implant failure due to fretting corrosion at the head-stem modular junction is an increasing problem in modular total hip arthroplasty. The effect of varying microgroove topography on modular junction contact mechanics has not been well characterized. The aim of this study was to employ a novel, microgrooved finite element (FEA) model of the hip taper interface and assess the role of microgroove geometry and taper mismatch angle on the modular junction mechanics during assembly. A two-dimensional, axisymmetric FEA model was created using a modern 12/14 taper design of a CoCrMo femoral head taper and Ti6Al4V stem taper. Microgrooves were modeled at the contacting interface of the tapers and varied based on height and spacing measurements obtained from a repository of measured retrievals. Additionally, taper angular mismatch between the head and stem was varied to simulate proximal- and distal-locked engagement. Forty simulations were conducted to parametrically evaluate the effects of microgroove surface topography and angular mismatch on predicted contact area, contact pressure, and equivalent plastic strain. Multiple linear regression analysis was highly significant (p < 0.001; R2  > 0.74) for all outcome variables. The regression analysis identified microgroove geometry on the head taper to have the greatest influence on modular junction contact mechanics. Additionally, there was a significant second order relationship between both peak contact pressure (p < 0.001) and plastic strain (p < 0.001) with taper mismatch angle. These modeling techniques will be used to identify the implant parameters that maximize taper interference strength via large in-silico parametric studies.

Surface Analysis of Ti-Alloy Micro-Grooved 12/14 Tapers Assembled to Non-Sleeved and Sleeved Ceramic Heads: A Comparative Study of Retrieved Hip Prostheses

Ti6Al4V titanium alloy (Ti-alloy) sleeved ceramic heads have become widely used in revision surgery when the hip stem is left in situ. This solution guarantees a new junction between the bore of the ceramic head and the Ti-alloy sleeve, regardless of any possible, slight surface damage to the Ti-alloy taper of the stem. However, this solution introduces an additional Ti-alloy/Ti-alloy interface pairing, which is potentially susceptible to mechanically assisted crevice corrosion. This study evaluated both qualitatively and quantitatively the damage that occurred in vivo on Ti-alloy micro-grooved 12/14 tapers of (i) primary implants with non-sleeved ceramic heads (Group 1), (ii) secondary implants with non-sleeved ceramic heads (Group 2), and (iii) secondary implants with sleeved ceramic heads (Group 3). A total of 45 explants-15 for each group, including short-, medium- and long-neck heads-underwent optical evaluation for surface damage (Goldberg scoring), surface roughness analysis, and SEM/EDX analysis. The Goldberg scores did not reveal different patterns in the tapers' surface damage; surface damage was classified as absent or mild (surface damage score ≤2) in 94%, another 94%, and 92% of the analysed regions for Group 1, Group 2, and Group 3, respectively. Small but significant differences in morphological changes occurred in the tapers of the three groups: reductions no greater than a few percentage points in median values of roughness parameters were found in Group 1 and Group 2, while negligible changes were found in Group 3. SEM/EDX analysis revealed little (i.e., a slight increase in the oxygen content) to undetectable changes in the chemical composition on the Ti-alloy surface independently of the group. These results suggest that the Ti-alloy/Ti-alloy sleeve/taper junction is only mildly susceptible to mechanically assisted crevice corrosion. Assembling a sleeved ceramic head, with variable neck lengths up to a "long-neck", to a Ti-alloy micro-grooved 12/14 taper of a stem left in situ does not seem to increase the risk of revision due to trunnionosis, as long as junction stability (i.e., the proper seating of the sleeved ceramic head on the 12/14 taper) is achieved intraoperatively.

In vitro testing for hip head-neck taper tribocorrosion: A review of experimental methods

In vitro test methods are challenged by the multi-factorial nature of head-neck taper connection tribocorrosion due to the consequences of simplification. Incorrect study design and misinterpretation of results has led to contradictory findings regarding important factors affecting head-neck taper tribocorrosion. This review seeks to highlight important considerations when developing in vitro test methods, to help researchers strengthen their study design and analyze the implications of others' design decisions. The advantages, disadvantages, limitations and procedural considerations for finite element analyses, electrochemical studies and in vitro simulations related to head-neck taper connection tribocorrosion are discussed. Finite element analysis offers an efficient method for studying large ranges of mechanical parameters. However, they are limited by neglecting electrochemical, biological and fluid flow factors. Electrochemical studies may be preferred if these factors are considered important. Care must be taken in interpreting data from electrochemical studies, particularly when different materials are compared. Differences in material valence and toxicity affect clinical translation of electrochemical studies' results. At their most complex, electrochemical studies attempt to simulate all aspects of headneck taper connection tribocorrosion in a bench top study. Effective execution requires in-depth knowledge of the tribocorrosion phenomenon, the involved mechanisms, and their measures such that each study design decision is fully informed.

Catastrophic intraoperative failure of a ceramic femoral head

Approximately 17 years after a primary metal-on-metal total hip arthroplasty, a 59-year-old female developed pain, swelling, and weakness in her right hip accompanied by laboratory findings and imaging suggestive of an adverse local tissue reaction. Acetabular revision was performed to upsize the femoral head and improve hip stability. Upon impaction of the new, non-option ceramic femoral head onto the unsleeved retained stem, the head split into two pieces without fragmentation. The surgery was completed using a cobalt-chromium head, which was impacted without issue onto the stem’s taper. Although BIOLOX delta femoral heads do not require titanium sleeves, we believe that careful consideration should be given to their use in revision total hip arthroplasty with ceramic heads, regardless of the extent of trunnion damage noted intraoperatively.

Finite element analysis of hip implant with varying in taper neck lengths under static loading conditions

BACKGROUND AND OBJECTIVE

Total hip arthroplasty is known as one of the best advancements in orthopedics in the 20th century. Due to age or trauma hip joint has to replace by an artificial implant. After the hip arthroplasty, the patients can return to normal day-to-day activities with a normal range of motion. There are several types and designs are currently available. These designs usually depend upon the anatomy of the patients. There is a need for revision surgery due to dislocation and aseptic loosening in these joints over time in actively younger patients. Minor changes in the design stage can certainly improve the life expectancy of the implant and will also further reduce the revision rate.

METHODS

In this current work, finite element analysis is carried out by varying the neck length with a change in femoral head size for a circular-shaped stem. The effects of using a shorter neck are analyzed. A total of nine combinations are considered for analysis. Modeling is carried out in CATIA V-6 and analysis is performed in ANSYS R-19. A femoral head of 36, 40, and 44 mm and taper neck length of 18, 16, and 14 mm is considered. CoPE is considered as the material combination for all the models.

RESULTS

It was observed that the von Mises stresses in the complete implant tend to decrease with an increase in the femoral head size. Maximum 5% variation in stress values when 36 mm femoral head is compared with 44 mm. The stresses in the taper neck region tend to decrease with a decrease in the neck length. Minimum von Mises stress of 161.83 MPa was found for the complete implant and in the head-neck region, a minimum von Mises stress found 91.9 MPa.

CONCLUSIONS

Performance evaluation of hip implant under static loading conditions gives a clear idea about the behavior of implant. It was found that a decrease in the von Mises stresses with a decrease in the taper length. However, these variations won't affect much in the performance of the hip implant. Also, a reduction in taper length can significantly increase the dislocation in the implant. So it is advised to consider the optimal taper length with an increase in the femoral head size.

The mechanics of head-neck taper junctions: What do we know from finite element analysis?

Modular hip implants are widely used in hip arthroplasty because of the advantages they can offer such as flexibility in material combinations and geometrical adjustments. The mechanical environment of the modular junction in the body is quite challenging due to the complex and varying off-axial mechanical loads of physical activities applied to a tapered interface of two contacting materials (head and neck) assembled by an impact force intraoperatively. Experimental analogies to the in-vivo condition of the taper junction are complex, expensive and time-consuming to implement; hence, computational simulations have been a preferred approach taken by researchers for studying the mechanics of these modular junctions that can help us understand their failure mechanisms and improve their design and longevity after implantation. This paper provides a clearer insight into the mechanics of the head-neck taper junction through a careful review on the finite element studies of the junction and their findings. The effects of various factors on the mechanical outputs namely: stresses, micromotions, and contact situations are reviewed and discussed. Also, the simulation methodology of the studies in the literature is compared. Research opportunities for future are scrutinised through tabulating data and information that have been carefully retrieved form the reported findings.

A review on the finite element simulation of fretting wear and corrosion in the taper junction of hip replacement implants

Taperosis/trunnionosis is a scientific term for describing tribocorrosion (fretting corrosion) at the head-neck taper junction of hip implants where two contacting surfaces are undergone oscillatory micromotions while being exposed to the body fluid. Detached ions and emitted debris, as a result of taperosis, migrate to the surrounding tissues and can cause inflammation, infection, and aseptic loosening with an ultimate possibility of implant failure. Improving the tribocorrosion performance of the head-neck junction in the light of minimising the surface damage and debris requires a better understanding of taperosis. Given its complexity associated with both the mechanical and electrochemical aspects, computational methods such as the finite element method have been recently employed for analysing fretting wear and corrosion in the taper junction. To date, there have been more efforts on the fretting wear simulation when compared with corrosion. This is because of the mechanical nature of fretting wear which is probably more straightforward for modelling. However, as a recent research advancement, corrosion has been a focus to be implemented in the finite element modelling of taper junctions. This paper aims to review finite element studies related to taperosis in the head-neck junction to provide a detailed understanding of the design parameters and their role in this failure mechanism. It also reviews and discusses the methodologies developed for simulating this complex process in the taper junction along with the simplifications, assumptions and findings reported in these studies. The current needs and future research opportunities and directions in this field are then identified and presented.

Femoral prosthesis neck fracture following total hip arthroplasty - a systematic review

PURPOSE

Head-neck modularity was introduced into total hip arthroplasty to provide more intraoperative surgical options. However, modularity led to new problems, such as trunnionosis and fractures of the femoral prosthesis neck. The purpose of this study was to identify risk factors for hip neck fractures and to provide recommendations to prevent damage and fractures of the neck.

METHODS

A systematic review of the literature was performed according to the PRISMA guidelines.

RESULTS

Thirty-three case studies were included. Methodologically, most included studies were of moderate or good quality. The 80 neck fractures included in the review took place, on average, 7 years after stem placement. Male gender, high body weight, obesity, previous revision surgery, mixing components from different manufacturers, use of long skirted heads, cobalt-chromium (large size) heads were identified as potential risk factors.

CONCLUSION

Hip neck fractures occur on average 7 years after stem placement. The etiology of hip neck fractures is multifactorial. This review revealed several preventable implant- and surgeon-related risk factors.

Geometric Variations of Modular Head-Stem Taper Junctions of Total Hip Replacements

Taper degradation in Total Hip Replacements (THR) has been identified as a clinical concern, and the degradation occurring at these interfaces has received increased interest in recent years. Wear and corrosion products produced at the taper junction are associated with adverse local tissue responses, leading to early failure and revision surgery. Retrieval and in-vitro studies have found that variations in taper design affect degradation. However, there is a lack of consistent understanding within the literature of what makes a good taper interface. Previous studies assessed different design variations using their global parameters assuming a perfect cone such as: taper length, cone angle and diameters. This study assessed geometrical variations of as-manufactured head and stem tapers and any local deviations from their geometry. The purpose of this study was to provide a greater insight into possible engagement, a key performance influencing parameter predicted by Morse taper connection theory. This was achieved by taking measurements of twelve different commercially available male tapers and six female tapers using a coordinate measurement machine (CMM). The results suggested that engagement is specific to a particular head-stem couple. This is subject to both their micro-scale deviations, superimposed on their macro-scale differences. Differences in cone angles between female and male tapers from the same manufacturer was found to create a predominately proximal contact. However, distally mismatched couples are present in some metal-on-metal head-stem couples. On a local scale, different deviation patterns were observed from the geometry which appeared to be linked to the manufacturing process. Future work will look at using this measurement methodology to fully characterise an optimal modular taper junction for a THR prosthesis.

Modelling changes in modular taper micromechanics due to surgeon assembly technique in total hip arthroplasty

AIMS

The aim of this study was to develop a novel computational model for estimating head/stem taper mechanics during different simulated assembly conditions.

METHODS

Finite element models of generic cobalt-chromium (CoCr) heads on a titanium stem taper were developed and driven using dynamic assembly loads collected from clinicians. To verify contact mechanics at the taper interface, comparisons of deformed microgroove characteristics (height and width of microgrooves) were made between model estimates with those measured from five retrieved implants. Additionally, these models were used to assess the role of assembly technique-one-hit versus three-hits-on the taper interlock mechanical behaviour.

RESULTS

The model compared well to deformed microgrooves from the retrieved implants, predicting changes in microgroove height (mean 1.1 μm (0.2 to 1.3)) and width (mean 7.5 μm (1.0 to 18.5)) within the range of measured changes in height (mean 1.4 μm (0.4 to 2.3); p = 0.109) and width (mean 12.0 μm (1.5 to 25.4); p = 0.470). Consistent with benchtop studies, our model found that increasing assembly load magnitude led to increased taper engagement, contact pressure, and permanent deformation of the stem taper microgrooves. Interestingly, our model found assemblies using three hits at low loads (4 kN) led to decreased taper engagement, contact pressures and microgroove deformations throughout the stem taper compared with tapers assembled with one hit at the same magnitude.

CONCLUSION

These findings suggest additional assembly hits at low loads lead to inferior taper interlock strength compared with one firm hit, which may be influenced by loading rate or material strain hardening. These unique models can estimate microgroove deformations representative of real contact mechanics seen on retrievals, which will enable us to better understand how both surgeon assembly techniques and implant design affect taper interlock strength. Cite this article: Bone Joint J 2020;102-B(7 Supple B):33-40.