Elastomer Nanocomposite; Properties

Curing Behaviors, Mechanical and Dynamic Properties of Composites Containing Chloroprene and Butadiene Rubbers Crosslinked with Nano-Iron(III) Oxide

This paper discusses the curing behaviors, mechanical and dynamical properties of composites containing chloroprene rubber (CR) and butadiene rubber (BR) reinforced with mineral fillers. The iron(III) oxide nanoparticles were used as a crosslinking agent of the CR/BR blends. The research aimed to evaluate the effectiveness of nano-iron(III) oxide (nano-Fe₂O₃) as a new crosslinking agent while producing elastomeric materials with good mechanical properties and reduced flammability. The CR/BR (chloroprene rubber/butadiene rubber) blends were filled with silicas from natural resources (chalcedony, Neuburg silica earth) or silicas used in elastomer technology in many fields (aerosil, ultrasil). The results revealed that all composites were characterized by satisfactory tensile strength, tear resistance, and high resistance to fire. The filler dispersion in the elastomer matrix was carried out by using scanning electron microscopy (SEM), while the possibility of the filler-filler or filler-rubber interaction in the designed compositions was determined using the Payne effect and the Mullins effect.

Micro and nanocomposites of polybutadienebased polyurethane liners with mineral fillers and nanoclay: thermal and mechanical properties

Micro and nanocomposites of hydroxyl terminated polybutadiene (HTPB)-based polyurethanes (NPU) were obtained using five mineral fillers and Cloisite 20A nanoclay, respectively. Samples were prepared by the reaction of HTPB polyol and toluene diisocyanate (TDI), and the chain was further extended with glyceryl monoricinoleate to produce the final elastomeric polyurethanes. Mechanical and thermal properties were studied, showing that mineral fillers (20%w/w) significantly increased tensile strength, in particular nanoclay (at 5% w/w). When nanoclay-polymer dispersion was modified with a silane and hydantoin-bond promoter, elongation at break was significantly increased with respect to NPU with C20A. Thermal properties measured by differential scanning calorimetry (DSC) were not significantly affected in any case. The molecular structure of prepared micro and nanocomposites was confirmed by Fourier transform infrared (FTIR) spectroscopy and Raman spectroscopy. Interaction of fillers with polymer chains is discussed, considering the role of silanes in compatibilization of hydrophilic mineral fillers and hydrophobic polymer. The functionalization of nanoclay with HMDS silane was confirmed using FTIR. Microstructure of NPU with C20A nanoclay was confirmed by Atomic Force Microscopy (AFM).