Studies of the early stages of the dynamic setting process of chemically activated restorative glass-ionomer cements

Evaluation of setting kinetics, mechanical strength, ion release, and cytotoxicity of high-strength glass ionomer cement contained elastomeric micelles

BACKGROUND

Low mechanical properties are the main limitation of glass ionomer cements (GICs). The incorporation of elastomeric micelles is expected to enhance the strength of GICs without detrimentally affecting their physical properties and biocompatibility. This study compared the chemical and mechanical properties, as well as the cytotoxicity, of elastomeric micelles-containing glass ionomer cement (DeltaFil, DT) with commonly used materials, including EQUIA Forte Fil (EF), Fuji IX GP Extra (F9), and Ketac Molar (KT).

METHOD

Powder particles of GICs were examined with SEM-EDX. Setting kinetics were assessed using ATR-FTIR. Biaxial flexural strength/modulus and Vickers surface microhardness were measured after immersion in water for 24 h and 4 weeks. The release of F, Al, Sr, and P in water over 8 weeks was analyzed using a fluoride-specific electrode and ICP-OES. The toxicity of the material extract on mouse fibroblasts was also evaluated.

RESULTS

High fluoride levels in the powder were detected with EF and F9. DT demonstrated an initial delay followed by a faster acid reaction compared to other cements, suggesting an improved snap set. DT also exhibited superior flexural strength than other materials at both 24 h and 4 weeks but lower surface microhardness (p < 0.05). EF and F9 showed higher release of F, Al, and P than DT and KT. There was no statistically significant difference in fibroblast viability among the tested materials (p > 0.05).

CONCLUSIONS

Elastomeric micelles-containing glass ionomer cement (DT) exhibited satisfactory mechanical properties and cytocompatibility compared with other materials. DT could, therefore, potentially be considered an alternative high-strength GIC for load-bearing restorations.

Evaluation of the shear bond strength of a tricalcium silicate-based material to four self-adhering glass ionomer materials: an in vitro study

Background

This study aimed to evaluate and compare the shear bond strength (SBS) of EQUIA Forte HT with that of other restorative materials, including EQUIA Forte, glass ionomer cement (GIC), and resin-modified glass ionomer cement (RMGIC) when bonded to NeoMTA 2.

Materials and methods

A total of 120 holes were created in Teflon molds and filled with NeoMTA 2. The restorative materials were immediately applied using customized silicone molds. The samples were randomly divided into two main groups: one to measure the immediate SBS and the other to measure the delayed SBS. These two main groups were further divided into four subgroups based on the restorative material used: EQUIA Forte HT, EQUIA Forte, GIC, and RMGIC.

Results

The study groups showed statistically significant differences in the mean SBS (p < 0.0001). The immediate SBS of the RMGIC group (mean ± SD: 5.43 ± 1.22) was significantly higher than those of the GIC and EQUIA Forte groups, with no significant difference found compared to the SBS of EQUIA Forte HT. In the delayed SBS, both the RMGIC and EQUIA Forte HT groups (4.98 ± 0.67 and 4.93 ± 0.60, respectively) demonstrated significantly higher bond strengths than the GIC and EQUIA Forte groups (3.81 ± 0.57 and 4.2 ± 0.63, respectively). However, there were no statistically significant differences between the RMGIC and EQUIA Forte HT groups or between the GIC and EQUIA Forte groups.

Conclusion

Based on our findings, EQUIA Forte HT has shown promising outcomes when used as a restorative material following pulpotomies, with results comparable to those of RMGIC.