Biological aspects of modern dental composites

Surface alterations and compound release from aligner attachments in vitro

AIM

The aim of the present study was to assess the alterations in morphology, roughness, and composition of the surfaces of a conventional and a flowable composite attachment engaged with aligners, and to evaluate the release of resin monomers and their derivatives in an aqueous environment.

METHODS

Zirconia tooth-arch frames (n = 20) and corresponding thermoformed PET-G aligners with bonded attachments comprising two composite materials (universal-C and flowable-F) were fabricated. The morphological features (stereomicroscopy), roughness (optical profilometry), and surface composition (ATR-FTIR) of the attachments were examined before and after immersion in water. To simulate intraoral use, the aligners were removed and re-seated to the frames four times per day for a 7-day immersion period. After testing, the eluents were analyzed by LC-MS/MS targeting the compounds Bis-GMA, UDMA, 2-HEMA, TEGDMA and BPA and by LC-HRMS for suspect screening of the leached dental material compounds and their degradation products.

RESULTS

After testing, abrasion-induced defects were found on attachment surfaces such as scratches, marginal cracks, loss of surface texturing, and fractures. The morphological changes and debonding rate were greater in F. Comparisons (before-after testing) revealed a significantly lower Sc roughness parameter in F. The surface composition of the aligners after testing showed minor changes from the control, with insignificant differences in the degree of C = C conversion, except for few cases with strong evidence of hydrolytic degradation. Targeted analysis results revealed a significant difference in the compounds released between Days 1 and 7 in both materials. Insignificant differences were found when C was compared with F in both timeframes. Several degradation products were detected on Day 7, with a strong reduction in the concentration of the targeted compounds.

CONCLUSIONS

The use of aligners affects the surface characteristics and degradation rate of composite attachments in an aqueous environment, releasing monomers, and monomer hydrolysates within 1-week simulated use.

Digital manufacturing techniques and the in vitro biocompatibility of acrylic-based occlusal device materials

OBJECTIVES

Material chemistry and workflow variables associated with the fabrication of dental devices may affect the biocompatibility of the dental devices. The purpose of this study was to compare digital and conventional workflow procedures in the manufacturing of acrylic-based occlusal devices by assessing the cytotoxic potential of leakage products.

METHODS

Specimens were manufactured by 3D printing (stereolithography and digital light processing), milling, and autopolymerization. Print specimens were also subjected to different post-curing methods. To assess biocompatibility, a human tongue epithelial cell line was exposed to material-based extracts. Cell viability was measured by MTT assay while Western blot assessed the expression level of selected cytoprotective proteins.

RESULTS

Extracts from the Splint 2.0 material printed with DLP technology and post-cured with the Asiga Flash showed the clearest loss of cell viability. The milled and autopolymerized materials also showed a significant reduction in cell viability. However, by storing the autopolymerized material in dH2O for 12 h, no significant viability loss was observed. Increased levels of cytoprotective proteins were seen in cells exposed to extracts from the print materials and the autopolymerized material. Similarly to the effect on viability loss, storing the autopolymerized material in dH2O for 12 h reduced this effect.

CONCLUSIONS/CLINICAL RELEVANCE

Based on the biocompatibility assessments, clinical outcomes of acrylic-based occlusal device materials may be affected by the choice of manufacturing technique and workflow procedures.

Considerations about Cytotoxicity of Resin-Based Composite Dental Materials: A Systematic Review

The dental material industry is rapidly developing resin-based composites (RBCs), which find widespread use in a variety of clinical settings. As such, their biocompatibility has gained increasing interest. This literature review presents a summary of research into the cytotoxicity of methacrylate-based composites published from 2017 to 2023. Subject to analysis were 14 in vitro studies on human and murine cell lines. Cytotoxicity in the included studies was measured via MTT assay, LDH assay, and WST-1 assay. The QUIN Risk of Bias Tool was performed to validate the included studies. Included studies (based entirely on the results of in vitro studies) provide evidence of dose- and time-dependent cytotoxicity of dental resin-based composites. Oxidative stress and the depletion of cellular glutathione (GSH) were suggested as reasons for cytotoxicity. Induction of apoptosis by RBCs was indicated. While composites remain the golden standard of dental restorative materials, their potential cytotoxicity cannot be ignored due to direct long-term exposure. Further in vitro investigations and clinical trials are required to understand the molecular mechanism of cytotoxicity and produce novel materials with improved safety profiles.