Study on the observation of Eu2+ and Eu3+ valence states in low silica calcium aluminosilicate glasses

Broad combined orange-red emissions from Eu²⁺- and Eu³⁺-doped low-silica calcium aluminosilicate glass

In this paper, a broad combined orange-red emission from Eu²⁺- and Eu³⁺-doped low-silica calcium aluminosilicate (LSCAS) glass is reported. Spectroscopic results demonstrate that it is possible to tune the emission wavelength by changing the excitation wavelength in the UV-Vis region. The color coordinates for the emission spectra were calculated, and using the Commission Internationale de l'Éclairage 1931 and 1976 chromatic diagrams, it is possible to note that they are dependent on the excitation wavelength. In addition, the (u', v') color coordinates for the investigated LSCAS samples are close to the Planckian spectrum in the cold region between 2000 and 2600K. Our results show that the Eu:LSCAS system can be used in a white light phosphor when mixed in aggregate with phosphors using green-yellow luminescent ions.

Tunable color temperature of Ce3+/Eu2+, 3+ co-doped low silica aluminosilicate glasses for white lighting

In this paper we report results of tunable lighting in Ce(3+)/Eu(2+,3+) doped low silica calcium aluminosilicate glass. Optical spectroscopy experiments indicate that there is a red color compensation from Eu(2+) and Eu(3+) to the green emission from Ce(3+), resulting in a broad and tunable emission spectra depending on the excitation wavelength. This result analysed in the CIE 1976 color diagram shows a close distance from the Plank emission and a correlated color temperature, varying from 5200 to 3500K. This indicates that our system can be easily excited by GaN based blue LEDs, being an interesting phosphor for white lighting devices.