Highly monodisperse Au@Ag nanospheres: synthesis by controlled etching route and size-dependent SERS performance of their surperlattices

A sensitive Ag+-mediated magnetic relaxation and colorimetry dual-mode sensing platform

To address the relatively low sensitivity of current redox reagent-mediated magnetic relaxation sensing methods, we present a novel Ag+-mediated magnetic sensing platform that enhances the sensitivity by three orders of magnitude. The new sensing platform is based on Ag+-catalyzed oxidation of Mn2+ to KMnO4, accompanied by a distinct color change, which facilitates colorimetric detection. In the case of insufficient Ag+ ions, MnO2 is an additional oxidation product and the KMnO4/MnO2 ratio is dependent on the concentration of Ag+. When combined with a specific quantity of reducing agent, both KMnO4 and MnO2 are reduced to Mn2+ with a large relaxivity, and the concentration of Mn2+ in the resultant solution inversely correlates with the amount of KMnO4 since KMnO4 consumes more reductant during reduction. Consequently, the transverse relaxation rate of the solution exhibits a negative correlation with the Ag+ concentration. Thus, by coupling this Ag+-mediated Mn2+ to KMnO4 transformation with reactions that modulate Ag+ concentration, a dual-mode sensing platform for magnetic relaxation and colorimetry can be realized. Herein, we take H2O2 as an example to verify the detection performance of this sensing platform since H2O2 can oxidize Ag0 in Ag@Fe3O4 nanoparticles to Ag+. Experimental findings demonstrate detection limits of 10 nM and 20 nM for the magnetic relaxation and colorimetry modes, respectively, affirming the excellent sensitivity and the potential practical application of this strategy.

Identifying high-order plasmon modes in silver nanoparticle-over-mirror configuration

Metallic nanoparticle-over-mirror (NPOM) represents as a versatile plasmonic configuration for surface enhanced spectroscopy, sensing and light-emitting metasurfaces. However, experimentally identifying the high-order localized surface plasmon modes in NPOM, especially for the best plasmonic material silver, is often hindered by the small scattering cross-section of high-order plasmon modes and the poor reproducibility of the spectra across different NPOMs, resulted from the polyhedral morphology of the colloidal nanoparticles or the rough surface of deposited polycrystalline metals. In this study, we identify the high-order localized surface plasmon modes in silver NPOM by using differential reflection spectroscopy. We achieved reproducible single-particle absorption spectra by constructing uniform NPOM consisting of silver nanospheres, single-crystallized silver microplates, and a self-assembled monolayer of 1,10-decanedithiol. For comparison, silver NPOM created from typical polycrystalline films exhibits significant spectral fluctuations, even when employing template stripping methods to minimize the film roughness. Identifying high-order plasmon modes in the NPOM configuration offers a pathway to construct high-quality plasmonic substrates for applications such as colloidal metasurface, surface-enhanced Raman spectroscopy, fluorescence, or infrared absorption.

Self-assembled core-shell nanoparticles with embedded internal standards for SERS quantitative detection and identification of nicotine released from snus products

Surface enhanced Raman spectroscopy (SERS) is a unique analytical technique with excellent performance in terms of sensitivity, non-destructive detection and resolution. However, due to the randomness and poor repeatability of hot spot distribution, SERS quantitative analysis is still challenging. Meanwhile, snus is a type of tobacco product that can release nicotine and other components in the mouth without burning, and the rapid detection technique based on SERS can reliably evaluate the amount of nicotine released from snus, which is of great significance for understanding its characteristics and regulating its components. Herein, the strategy was proposed to solve the feasibility of SERS quantitative detection based on self-assembled core-shell nanoparticles with embedded internal standards (EIS) due to EIS signal can effectively correct SERS signal fluctuations caused by different aggregation states and measurement conditions, thus allowing reliable quantitative SERS analysis of targets with different surface affinity. By means of process control, after the Au nanoparticles (Au NPs) were modified with 4-Mercaptobenzonitrile (4-MBN) as internal standard molecules, Ag shell with a certain thickness was grown on the surface of the AuNP@4-MBN, and then the Au@4-MBN@Ag NPs were used to regulate and control the assembly of liquid-liquid interface. The high-density nano-arrays assembled at the liquid-liquid interface ensure high reproducibility as SERS substrates, and which could be used for SERS detection of nicotine released from snus products. In addition, time-mapping research shows that this method can also be used to dynamically monitor the release of nicotine. Moreover, such destruction-free evaluation of the release of nicotine from snus products opens up new perspectives for further research about the impact of nicotinoids-related health programs.

Bleach Cleaning of Commercially Available Gold Nanopillar Arrays for Surface-Enhanced Raman Spectroscopy (SERS)

Surface-enhanced Raman spectroscopy (SERS) is a highly sensitive technique that can assist in trace analysis for biomedical, diagnostic, and environmental applications. However, a major limitation of SERS is surface contamination of the substrates used, which can complicate the spectral reproducibility, limits of detection, and detection of unknown analytes. This is especially prevalent with commercially available substrates as shipping under a controlled and clean environment is difficult. Here we report a method using dilute bleach solutions to remove surface contamination from commercially available substrates consisting of gold-coated nanopillar arrays that maintains functionality. The results show that this method can be used to remove background signals associated with typical surface contamination in commercially available substrates as well as remove thiolated self-assembled monolayers (SAMs). Results indicate the bleach oxidizes the surface contaminants, which can then be easily washed away. Although the metallic surface also becomes oxidized in this process, the surface can be reduced without loss of SERS activity. The SERS intensity of SAMs improved following bleach treatment across all concentrations studied.

Au@Ag Nanopencil with Au Tip and Au@Ag Rod: Multimodality Plasmonic Nanoprobe based on Asymmetric Etching for the Detection of SCN- and ClO. SMALL (WEINHEIM AN DER BERGSTRASSE, GERMANY) 2023;19:e2302302. [PMID: 37211700 DOI: 10.1002/smll.202302302]

In this paper, Au@Ag nanopencil is designed as a multimodality plasmonic nanoprobe based on asymmetric etching for the detection of SCN- and ClO- . Au@Ag nanopencil with Au tip and Au@Ag rod is prepared by asymmetric tailoring of uniformly grown silver-covered gold nanopyramids under the combined effect of partial galvanic replacement and redox reaction. By asymmetric etching in different systems, Au@Ag nanopencil exhibits diversified changes in the plasmonic absorption band: O2 •- facilitated by SCN- etches Au@Ag rod from the end to the tip, causing a blue shift of the localized surface plasmon resonance (LSPR) peak as the aspect ratio decreases; while the ClO- can retain Au@Ag shell and etch Ag within rod from the tip to the end, causing a redshift of the LSPR peak as the coupling resonance weakens. Based on peak shifts in different directions, a multimodality detection of SCN- and ClO- has been established. The results demonstrate the detection limits of SCN- and ClO- are 160 and 6.7 nm, and the linear ranges are 1-600 µm and 0.05-13 µm, respectively. The finely designed Au@Ag nanopencil not only broadens the horizon of designing heterogeneous structures, but also enriches the strategy of constructing multimodality sensing platform.

High-performance homogeneous carboxymethylcellulose-stabilized Au@Ag NRs-CMC surface-enhanced Raman scattering chip for thiram detection in fruits

Cellulose material holds considerable promise for effective surface-enhanced Raman scattering (SERS) substrate construction due to its extensive availability, chemically modifying capacity, ease of manufacture, high flexibility and low optical activity. A large-area, high-sensitivity, stable and uniform Au@Ag nanorods (NRs)-CMC substrate was successfully developed via electrostatic repulsion by using negatively-charged core-shell Au@Ag NRs as SERS active plasmonic nanomaterial, combined with negatively-charged carboxymethylcellulose (CMC) hydrogel for nanoparticles stabilization, homodisperse and protection. The obtained Au@Ag NRs-CMC substrate showed excellent sensitivity for the detection of thiram residues in fruits containing low and abundant pigment interferents, such as apples and blueberries, with detection limits of 58 and 78 ppb, respectively. Additionally, it retained more than 80% SERS performance after storage for 9 months under ambient conditions, demonstrating its great potential in facilitating the commercialization of cellulose-based SERS technology for cost-effective detection of food contaminants with advantages of facile preparation procedure, uniformity, reproducibility and long-term stability.

Flexible Au@AgNRs/CMC/qPCR film with enhanced sensitivity, homogeneity and stability for in-situ extraction and SERS detection of thiabendazole on fruits

In this study, a high-performance, stable and homogeneous Au@AgNRs/CMC/qPCR flexible film surface-enhanced Raman scattering (SERS) substrate was constructed by synergistically stabilizing and protecting bimetallic core-shell Au@Ag nanorods (Au@AgNRs) with carboxymethylcellulose (CMC) and fluorescent-quantitative-polymerase-chain-reaction (qPCR) film. The network structure of CMC immobilized and aligned Au@AgNRs through coordination of carboxyl groups with surface Ag atoms to provide intensive and stable 'hot spots', and the qPCR bilayer film performed as carrier and barrier to protect Au@AgNRs from oxidation, humidity and optical damage and improved the robustness and stability. The Au@AgNRs/CMC/qPCR film was used for in-situ extraction and SERS detection of thiabendazole on nectarine (0.24 ppm) and lemon (0.27 ppm) with low detection of limits. Furthermore, it retained 98.6% SERS performance after storage for 90 days under ambient conditions, revealing the great potential in promoting the commercialization of the SERS technique for sensitive contaminants sensing with simple fabrication procedures, homogeneity, reproducibility and long-term stability.

Detection of Soluble Mercury in Cinnabar Using a CV-Ag NPs SERS Probe

In the current work a uniform morphological Ag nanoparticles (Ag NPs) were prepared with ascorbic acid as a reducing agent and citrate as a stabilizer. The surface of Ag NPs modified by crystal violet (CV) and potassium iodide (KI) was used as an aggregation agent to obtain CV modified Ag NPs (CV-Ag NPs) probes for detecting mercury ions. The mercury ions could be reduced to mercury molecules by citrate, and then deposited on the surface of Ag NPs, leading to the separation of CV molecules from the surface of Ag NPs. Therefore, the SERS signal intensity of CV decreased with the increase of the Hg²⁺ concentration and the concentration of Hg²⁺ was in the range of 1 × 10^-11 to 1 × 10^-5 M. Taking the change of the characteristic peak intensity of CV at 913 cm^-1 as a reference, the SERS spectrum intensity of CV has a linear relationship with the Hg²⁺ concentration. The equation is y = -333.55x + 1343.05, where the linear correlation coefficient is R² = 0.980, and the recovery rate is between 84.20 to 105.60%. Finally, the CV-Ag NPs probe was used to quickly detect soluble mercury in cinnabar. Compared with the conventional large-scale instrument detection method, this simple and fast method, can be applied for rapid detection of soluble mercury, and has a certain significance for concerning the research of mineral medicine processing mechanism.

The rationality of using coreshell nanoparticles with embedded internal standards for SERS quantitative analysis based glycerol-assisted 3D hotspots platform

Surface enhanced Raman spectroscopy (SERS) is a promising sensing technique that can provide unique chemical and structural fingerprint information, but gaining reliable SERS quantitative data with high sensitivity and stability still remains a challenge. Although using a molecule as an internal standard (IS) can improve the SERS quantitative capability, the reliability and SERS measuring conditions for signal fluctuations during calibration based on IS are yet to be explored when the embedded IS molecules and target objects are located in different environments. Herein, a 3D hotspot matrix SERS platform based on Au@4-MPy@AgNPs was constructed in water with the assistance of glycerol and the dynamic signal changes from the IS, i.e. 4-Mpy, and target molecules were monitored during the process of evaporation with high sensitivity and stability. In contrast to the traditional water-dispersed drying film system, the variation trends of IS and target molecules were consistent in the glycerol-assisted liquid film protection system. Therefore, it is reasonable to calibrate the signal fluctuation by utilizing the embedded IS based on the construction strategy of a glycerol-assisted 3D hotspot platform. This work demonstrates a rational, reliable and precise SERS quantitative technique for testing analyte concentrations in practical systems and has great application prospects in the field of analytical chemistry.

Sensitive and reliable identification of fentanyl citrate in urine and serum using chloride ion-treated paper-based SERS substrate

Recently, the phenomenon of fentanyls overdose leading to death is emerging in an endless stream. There is an urgent requirement to quickly identify fentanyl content in body fluids for medical and judicial purposes. With this in mind, we present a paper-based SERS substrate decorated with uniform gold nanospheres treated by chloride ion for the detection of fentanyl citrate in urine and serum. In particular, the paper-based SERS sensor was prepared by liquid/liquid self-assembly technique and chloride ion was introduced to clean and modify the substrate surface, which improved the sensitivity of the solid substrate with an enhancement factor (EF) as high as 1.64 × 10⁵. Moreover, the uniformity of each paper-based substrate and the repeatability on different batches of substrate were excellent, and there was no obvious change in the intensity response of Raman spectra within a month. As a result, the quantitative analysis of fentanyl citrate in artificial urine and rat serum were performed based on the modified paper-based substrate with the limit of detection as low as 0.59 μg/mL and 2.78 μg/mL, respectively. Both the concentrations of the two biological samples with the Raman signal intensity were linearly plotted and the recovery of the spiked samples with different concentrations was collected to verify the accuracy of the quantitative curves. All the results suggest that this work makes SERS method available for the rapid identification and quantitative analysis of illicit drug in the real biological samples.

Wavelength-Dependent Optical Nonlinear Absorption of Au-Ag Nanoparticles

The nonlinear optical absorption properties of Au-Ag nanoparticles (NPs) were studied using an open-aperture Z-scan under a nanosecond pulsed laser with wavelengths of 450 nm, 510 nm, 550 nm, and 600 nm. The experimental results demonstrated that, when the laser intensity was 1.04 × 1013 W/m2, the Au-Ag NPs showed saturated absorption (SA). When the laser intensity was increased to 3.03 × 1013 W/m2, the switch from SA to reverse saturation absorption (RSA) occurred. The nonlinear absorption and its transformation were analyzed by using local surface plasmon resonance (LSPR) effect, bleaching of ground state plasmon, and free carrier absorption theory.

Fabrication of an AAO-based surface-enhanced Raman scattering substrate for the identification of levofloxacin in milk

On-site measurement of levofloxacin in milk via surface-enhanced Raman spectroscopy using a AAO-based SERS substrate.

A dual-functional PDMS-assisted paper-based SERS platform for the reliable detection of thiram residue both on fruit surfaces and in juice

In this work, a dual-functional SERS platform was developed via a paper-based SERS substrate with the aid of hydrophobic polydimethylsiloxane (PDMS) for effective and reliable measurements of thiram on fruit surfaces and in juice. Specifically, the paper-based SERS substrate was fabricated by coating with a core-shell Au@Ag nanorod monolayer, and the SERS performance was optimized compared with multilayer adsorption. Moreover, a versatile SERS platform was constructed by simply pasting the paper-based substrate in reverse onto PDMS using polymethyl methacrylate (PMMA) tape. On the one hand, this detection platform was able to realize sample enrichment due to the excellent hydrophobicity of PDMS, thereby increasing the sensitivity of measurements, and its function was successfully displayed through the identification of thiram in orange juice. On the other hand, PDMS could also play a supporting role and the paper-based substrate reversely stuck on PDMS was able to extract samples on the side without nanoparticles, which greatly avoids damage to nanoparticles on the substrate. Therefore, the accuracy of analysis was significantly improved and the inspection of thiram on the surface of an orange was demonstrated based on this function. As a result, this proposed SERS platform provides a new strategy for preparing multifunctional SERS sensors for the on-site monitoring of chemical contaminants in the food-safety field.

Excellent Water Lubrication Additives for Silicon Nitride To Achieve Superlubricity under Extreme Conditions

Superlubricity has been recognized as the future of tribology. However, it is hard to achieve superlubricity under extreme conditions such as a high load and low sliding speed on the macroscale. In this paper, a remarkable synergetic lubricating effect between nanoparticles and silicon nitride (Si₃N₄) is demonstrated; this effect helps water-lubricated Si₃N₄ achieve superlubricity under extreme conditions successfully. Different kinds of hairy silica nanoparticles were prepared, dispersed into water, and characterized using a variety of methods. The tribological properties of water-lubricated Si₃N₄ with nanoparticle additives were tested using a ball-on-disk tribometer under different loads and sliding speeds. The coefficient of friction and wear scar diameter were measured and analyzed. Both the nanoparticle size and surface functional groups have a significant influence on the tribological properties of water-lubricated Si₃N₄. Amino-modified silica nanoparticles reduce the friction coefficient of water-lubricated Si₃N₄ by 82.9% under 60 N, compared with that achieved using deionized water, and induce superlubricity after the running-in process. Silica nanoparticles effectively form a homogenous film with silica gel on the worn surface under a high load and thus reduce the wear and maintain the superlubricity under extreme conditions.

In-Situ Growth of Au on KTaO3 Sub-Micron Cubes via Wet Chemical Approach for Enhanced Photodegradation of p-Nitrophenol

KTaO₃/Au hetero-nanostructures were synthesized by in-situ reduction of HAuCl₄ on the surface of hydrothermally-grown KTaO₃ sub-micron cubes. The concentration of Au source was found to be a critical factor in controlling the hetero-nucleation of Au nanoparticles on the surface of KTaO₃ sub-micron cubes. Loading of Au particles on KTaO₃ nanocrystals enriched KTaO₃ additional UV-vis absorption in the visible light region. Both KTaO₃ and KTaO₃/Au nanocrystals were shown to be active in the photo-degradation of p-nitrophenol, while the loading of Au on KTaO₃ clearly improved the photo-degradation efficiency of p-nitrophenol compared to that on bare KTaO₃ nanocrystals, probably due to the improved light absorption and charge separation.