Atomic layer deposited nanolaminates of zirconium oxide and manganese oxide from manganese(III)acetylacetonate and ozone

Influence to Hardness of Alternating Sequence of Atomic Layer Deposited Harder Alumina and Softer Tantala Nanolaminates

Atomic layer deposited amorphous 70 nm thick Al2O3-Ta2O5 double- and triple-layered films were investigated with the nanoindentation method. The sequence of the oxides from surface to substrate along with the layer thickness had an influence on the hardness causing rises and declines in hardness along the depth yet did not affect the elastic modulus. Hardness varied from 8 to 11 GPa for the laminates having higher dependence on the structure near the surface than at higher depths. Triple-layered Al2O3/Ta2O5/Al2O3 laminate possessed the most even rise of hardness along the depth and possessed the highest hardness out of the laminates (11 GPa at 40 nm). Elastic modulus had steady values along the depth of the films between 145 and 155 GPa.