Chemical and morphological analysis of dentin irradiated by different high-power lasers: a systematic review

PURPOSE

This systematic review provides an overview of the main chemical and morphological alterations generated on dentin by different high-power lasers' irradiation.

METHODS

The review was registered in PROSPERO (CRD42023394164) and PRISMA guidelines were followed. The search strategy was conducted on MEDLINE (PubMed), Embase (Elsevier), and Web of Science (Clarivate) databases. The eligibility criteria were established according to the PICOS strategy, focusing on in vitro and ex vivo studies that assessed the chemical and morphological changes in dentin using five high-power lasers: Nd:YAG (1064 nm), Er:YAG (2940 nm), Er, Cr:YSGG (2780 nm), diode (980 nm), and CO2 (10,600 nm). Publication range was from 2010 to 2022. Data was summarized in tables and risk of bias was assessed by QUIN tool.

RESULTS

The search resulted in 2255 matches and 57 studies composed the sample. The methods most used to assess the outcomes were scanning electron microscopy (SEM), energy-dispersive spectroscopy (EDS), and Raman. The studies presented "medium" and "low" risk of bias. The laser prevalently identified was the Er:YAG laser, associated with dentin ablation, absence of smear layer, and exposed tubules. The Nd:YAG laser generated vitreous surface and thermal damage, such as carbonization and cracks. The other lasers caused an irregular surface and no adverse thermal effects. Regarding the chemical structure, only the Er,Cr:YSGG laser caused collagen matrix reduction. The effects found were more intense with higher dosimetry.

CONCLUSION

Evidence available indicates that the irradiation of dentin with high-power lasers are related to morphological outcomes favorable to adhesive restorative procedures, with minimal changes in collagen matrix and mineral content. However, those observations should be carried carefully by clinicians and more clinical trials regarding the association of high-power laser irradiation and restorative procedure longevity are needed.

Apical microleakage and SEM analysis of dentin surface after 980 nm diode laser irradiation

This study evaluated the effect of 980-nm diode laser on apical microleakage and intraradicular dentin morphology. Roots of 110 mandibular incisors were used in the study: 92 for microleakage test and 18 for scanning electron microscopy (SEM). Roots were randomly assigned to 3 groups according to the irrigating solution (water, NaOCl and NaOCl/EDTA) and were divided into 3 subgroups according to the laser irradiation protocol (without irradiation, irradiated at 1.5 W and irradiated at 3.0 W). Two specimens of each subgroup were prepared for SEM. The remaining roots were filled with AH Plus and gutta-percha. Apical leakage was assessed by ink penetration and data were analyzed statistically by ANOVA and Tukey-Krammer test (α=0.05). SEM analysis showed intensification of changes with increase of laser power as well as variations according to the irrigating solution. Modified smear layer was observed in specimens treated with water and irradiated with laser. Roots irrigated with NaOCl/EDTA had lower levels of infiltration (0.17 ± 0.18 mm) differing significantly (p<0.05) from those of roots irrigated with water (0.34 ± 0.30 mm), but similar (p>0.05) to those irrigated with NaOCl (0.28 ± 0.29 mm). Non-irradiated roots had lower levels of infiltration (0.10 ± 0.14 mm), differing (p<0.05) from those irradiated at 1.5 W (0.32 ± 0.22 mm) and 3.0 W (0.37 ± 0.32 mm). The 980 nm diode laser modified dentin morphology and increased apical microleakage.